Glass adhesive and preparation method thereof

A technology of glass adhesive and ethyl cyanoacrylate, which is applied in the direction of non-polymer adhesive additives, adhesives, non-polymer organic compound adhesives, etc., can solve the problem of insufficient surface hardness of organic solvents, easy to rub hair, Poor adhesion effect and other problems, to achieve good acid and alkali resistance and neutral salt spray resistance, good adhesion performance effect

Inactive Publication Date: 2019-01-11
江苏耀兴安全玻璃有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Plexiglass is a polymer obtained by polymerization of acrylic acid and its esters. Plexiglass has excellent light transmission properties, high mechanical strength, corrosion resistance, and easy processing, but its texture is brittle and easily soluble in organic solvents. The surface hardness is not enough, easy to rub hair, etc.
Because of its brittle texture, plexiglass needs to use adhesives when combined with other products, but the adhesives currently used have poor bonding effect and poor resistance to acid and alkali

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A glass adhesive, the preparation raw materials include the following components in parts by weight: 10 parts of ethyl cyanoacrylate, 3 parts of polyvinyl acetate, 2 parts of hydroxypropyl methylcellulose, 1 part of stearic acid, 1 part of pentamethyldiethylenetriamine, 2 parts of dimethyl sebacate, 1 part of tricalcium phosphate, 1 part of silicon dioxide, 1 part of glass powder, 1 part of dioctyl phthalate, azo Diformamide 1 part.

[0018] The preparation method of above-mentioned glass adhesive, comprises the steps:

[0019] Step 1, polyvinyl acetate, hydroxypropyl methylcellulose, dimethyl sebacate, tricalcium phosphate and glass powder are stirred and mixed, the stirring speed of stirring and mixing is 120 rpm, and the stirring time is 20 minutes to obtain mixture one;

[0020] Step 2, put the mixture 1 into the reaction kettle, add stearic acid and azodicarbonamide under the vacuum condition of 0.02 MPa, raise the temperature to 60°C, stir for 20 minutes, and ob...

Embodiment 2

[0023] A glass adhesive, the preparation raw materials include the following components in parts by weight: 12 parts of ethyl cyanoacrylate, 4 parts of polyvinyl acetate, 3 parts of hydroxypropyl methylcellulose, 2 parts of stearic acid, 1 part of pentamethyldiethylenetriamine, 3 parts of dimethyl sebacate, 2 parts of tricalcium phosphate, 1 part of silicon dioxide, 1 part of glass powder, 2 parts of dioctyl phthalate, azo Diformamide 1 part.

[0024] The preparation method of above-mentioned glass adhesive, comprises the steps:

[0025] Step 1, polyvinyl acetate, hydroxypropyl methylcellulose, dimethyl sebacate, tricalcium phosphate and glass powder are stirred and mixed, the stirring speed of stirring and mixing is 130 rpm, and the stirring time is 25 minutes to obtain mixture one;

[0026] Step 2, put the mixture 1 into a reaction kettle, add stearic acid and azodicarbonamide under a vacuum condition of 0.03MPa, raise the temperature to 65°C, and stir for 23 minutes to ob...

Embodiment 3

[0029] A glass adhesive, the preparation raw materials include the following components in parts by weight: 16 parts of ethyl cyanoacrylate, 5 parts of polyvinyl acetate, 4 parts of hydroxypropyl methylcellulose, 2 parts of stearic acid, 2 parts of pentamethyldiethylenetriamine, 4 parts of dimethyl sebacate, 3 parts of tricalcium phosphate, 2 parts of silicon dioxide, 2 parts of glass powder, 4 parts of dioctyl phthalate, azo Diformamide 2 parts.

[0030] The preparation method of above-mentioned glass adhesive, comprises the steps:

[0031] Step 1, polyvinyl acetate, hydroxypropyl methylcellulose, dimethyl sebacate, tricalcium phosphate and glass powder are stirred and mixed, the stirring speed of stirring and mixing is 140 rpm, and the stirring time is 27 minutes to obtain mixture one;

[0032] Step 2, put the mixture 1 into the reaction kettle, add stearic acid and azodicarbonamide under a vacuum condition of 0.05MPa, raise the temperature to 68°C, and stir for 25 minutes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass adhesive and a preparation method thereof. The glass adhesive is prepared from ethyl cyanoacrylate, polyvinyl acetate, hydroxypropyl methylcellulose, stearic acid, pentamethyldiethylenetriamine, dimethyl sebacate, tricalcium phosphate, silica, glass frit, dioctyl phthalate and azodicarbonamide. The preparation method comprises the following steps: stirring and mixing the polyvinyl acetate, hydroxypropyl methylcellulose, dimethyl sebacate, tricalcium phosphate and glass frit to obtain a first mixture, adding the first mixture into a reactor, adding stearic acid and azodicarbonamide under a vacuum condition, and performing heating and stirring to obtain a first material; adding the ethyl cyanoacrylate, pentamethyldiethylenetriamine, silica and dioctyl phthalate to the first material, and performing heating and stirring under the protection of an inert gas to obtain the glass adhesive. The glass adhesive provided by the invention has the advantages of goodadhesion and good resistance to acids and alkalis.

Description

technical field [0001] The invention belongs to the technical field of adhesive preparation, and in particular relates to a glass adhesive and a preparation method thereof. Background technique [0002] Glass is usually divided into oxide glass and non-oxide glass according to the main components. There are few varieties and quantities of non-oxide glasses, mainly chalcogenide glasses and halide glasses. The anions of chalcogenide glass are mostly sulfur, selenium, tellurium, etc., which can cut off short-wavelength light and pass through yellow, red light, and near and far infrared light. It has low resistance and has switching and memory characteristics. Halide glass has low refractive index and low dispersion, and is often used as optical glass. [0003] Plexiglass is a polymer obtained by polymerization of acrylic acid and its esters. Plexiglass has excellent light transmission properties, high mechanical strength, corrosion resistance, and easy processing, but its tex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/04C09J4/06C09J11/04C09J11/06
CPCC09J4/06C09J11/04C09J11/06
Inventor 孙祯彬
Owner 江苏耀兴安全玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com