High-elasticity, corrosion-resistant, wear-resistant and oil-resistant rubber material

An oil-resistant rubber and corrosion-resistant technology, which is applied in the field of high-elasticity, corrosion-resistant, wear-resistant and oil-resistant rubber materials, can solve the problems of non-wear resistance, weak elasticity, and high cost, and achieve the effect of reducing the volume change rate and avoiding direct contact

Inactive Publication Date: 2018-12-11
合肥旭亚新材料科技有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current corrosion-resistant rubber material has high cost, weak elasticity, and is not wear-resistant.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high-elastic, corrosion-resistant, wear-resistant and oil-resistant rubber material is composed of the following components in parts by weight:

[0019] Nitrile rubber 137~145, MgO10~15, accelerator M2.5~3.5, thermoplastic polyurethane 35~47, polyvinyl chloride 7~23, stearic acid 2.5~3.5, paraffin wax 1.0~1.5, carbon black N550 125~145 , carbon black N330 55~63, paraffin oil 70~100, accelerator CZ1.0~1.5, accelerator TRA 1.3~2.4, accelerator BZ 0.9~1.2, accelerator TMTD 1.0~1.5, antioxidant 4010NA3.3~4.2 , Anti-aging agent BLE1.5~2.3, silicone masterbatch 6.0~8.0, sulfur 1.2~1.8.

[0020] A method for preparing a highly elastic, corrosion-resistant, wear-resistant and oil-resistant rubber material, comprising the following steps:

[0021] The first step: pre-plastic material: Put the weighed nitrile rubber, carbon black N550 and carbon black N330, each third of the weight of MgO and stearic acid into the internal mixer, at 130±5℃ Mixing at the banburying temperature...

Embodiment 2

[0024] A high-elastic, corrosion-resistant, wear-resistant and oil-resistant rubber material is composed of the following components in parts by weight:

[0025] Nitrile rubber 137~145, MgO10~15, accelerator M2.5~3.5, thermoplastic polyurethane 35~47, polyvinyl chloride 7~23, stearic acid 2.5~3.5, paraffin wax 1.0~1.5, carbon black N550 125~145 , carbon black N330 55~63, paraffin oil 70~100, accelerator CZ1.0~1.5, accelerator TRA 1.3~2.4, accelerator BZ 0.9~1.2, accelerator TMTD 1.0~1.5, antioxidant 4010NA3.3~4.2 , Anti-aging agent BLE1.5~2.3, silicone masterbatch 6.0~8.0, sulfur 1.2~1.8.

[0026] A method for preparing a highly elastic, corrosion-resistant, wear-resistant and oil-resistant rubber material, comprising the following steps:

[0027] The first step: pre-plastic material: Put the weighed nitrile rubber, carbon black N550 and carbon black N330, each third of the weight of MgO and stearic acid into the internal mixer, at 130±5℃ Mixing at the banburying temperature...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-elasticity, corrosion-resistant, wear-resistant and oil-resistant rubber material, and belongs to the technical field of rubber materials. The rubber material comprisesnitrile rubber, MgO, thermoplastic polyurethane, polyvinyl chloride, stearic acid, paraffin, carbon black N550, carbon black N330, paraffin oil, a promotor CZ, a promotor TRA, a promotor BZ, a promotor TMTD, an anti-aging agent 4010NA, anti-aging agent BLE, silicone master batch and sulfur. Through a modification process, the heat resistance, corrosion resistance, environment stress crack resistance and wear resistance of the rubber material are improved, and the rubber material has the advantages of superior aging resistance, particular outdoor aging resistance, ultraviolet light irradiationresistance, insusceptibility to decomposition and yellowing, and capability of keeping original luster and color. Meanwhile, the rubber material has high corrosion resistance, can resist chemical products such as acids, alkalis, salts and grease, and has excellent oil resistance, cold resistance and high temperature resistance, and the cost is lowered.

Description

technical field [0001] The invention belongs to the technical field of rubber materials, and in particular relates to a high-elastic, corrosion-resistant, wear-resistant and oil-resistant rubber material. Background technique [0002] Rubber materials refer to the connection sealing joints used in underground engineering pipelines, the permanent deformation joints provided in the concrete pouring of infrastructure projects, and the highly elastic sealing rubbers suitable for subways, tunnels, culverts, water conservancy and other projects. The rubber material used for the waterstop. The medium that can cause irreversible changes in the chemical structure of the rubber is called a chemically turbid medium. When rubber products are in contact with chemical media, the rubber and compounding ingredients are decomposed due to chemical action, resulting in chemical corrosion, and sometimes unbalanced swelling of rubber. The chemical substances entering the rubber break and disso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L75/04C08L27/06C08L91/06C08K13/02C08K3/22C08K3/04C08K3/06C08K5/09
CPCC08L9/02C08K2003/222C08L2205/035C08L75/04C08L27/06C08L91/06C08K13/02C08K3/22C08K3/04C08K3/06C08K5/09
Inventor 王永国
Owner 合肥旭亚新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com