Flame-retardant TPU cable sheathing material with electromagnetic shielding function and preparation method of TPU cable sheathing material

A cable sheathing material and electromagnetic shielding technology, which is applied to circuits, electrical components, organic insulators, etc., can solve problems such as instrument and instrument interference, abnormal use, etc., and achieve low production costs, reduced usage, and elongation at break high effect

Inactive Publication Date: 2018-08-17
ADVANCED THERMOPLASTIC POLYMER TECH
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, electromagnetic interference will also cause interference to instruments and meters, resulting in abnormal use, especially in the field of medical equipment, where the precision of instruments is high, and the electromagnetic interference generated by cables is the main reason for affecting the normal operation of instruments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant TPU cable sheathing material with electromagnetic shielding function and preparation method of TPU cable sheathing material
  • Flame-retardant TPU cable sheathing material with electromagnetic shielding function and preparation method of TPU cable sheathing material
  • Flame-retardant TPU cable sheathing material with electromagnetic shielding function and preparation method of TPU cable sheathing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A flame-retardant TPU cable sheath material with electromagnetic shielding function, comprising the following raw materials in parts by weight:

[0048]

[0049] The thermoplastic polyurethane is polyether polyurethane.

[0050] The graphene is graphene whose surface is treated with a coupling agent.

[0051] The graphene is single-layer graphene.

[0052] The flame retardant is a halogen-free flame retardant; the halogen-free flame retardant is ammonium phosphate, ammonium polyphosphate, modified ammonium polyphosphate, aluminum hypophosphite or melamine and compounds thereof.

[0053] The compatibilizer is polyurethane prepolymer modified maleic anhydride grafted polyethylene.

[0054] The antioxidant is tetrakis[methylene-3,5-(di-tert-butyl-4-hydroxy-phenyl)propionate]pentaerythritol ester.

[0055] It also includes 1 part of smoke suppressant and 0.02 part of antihydrolysis agent; the smoke suppressant is molybdenum compound; the antihydrolysis agent is carbod...

Embodiment 2

[0061] A flame-retardant TPU cable sheath material with electromagnetic shielding function, comprising the following raw materials in parts by weight:

[0062]

[0063] The thermoplastic polyurethane is polyester polyurethane.

[0064] The graphene is graphene whose surface is treated with a coupling agent.

[0065] The graphene is multilayer graphene.

[0066] The number of layers of the multilayer graphene is 2 layers.

[0067] The flame retardant is a mixture of a halogen-containing flame retardant and a synergistic flame retardant in a weight ratio of 4:1; the halogen-containing flame retardant is 2,6-dibromophenylene ether, tetrabromobisphenol A , hexabromocyclododecane, octabromoether, decabromodiphenylethane or polypentabromophenol-based acrylate; the synergistic flame retardant is antimony trioxide, bismuth trioxide, molybdenum trioxide or three ferric oxide.

[0068] The compatibilizer is divinyltetramethyldisiloxane, vinyltriethoxysiloxane, vinyltrichlorosilan...

Embodiment 3

[0076] A flame-retardant TPU cable sheath material with electromagnetic shielding function, comprising the following raw materials in parts by weight:

[0077]

[0078] The thermoplastic polyurethane is polycarbonate polyurethane.

[0079] The graphene is graphene whose surface is treated with a coupling agent.

[0080] The graphene is multilayer graphene.

[0081] The number of layers of the multilayer graphene is 10 layers.

[0082] The flame retardant is a halogen-free flame retardant; the halogen-free flame retardant is zinc borate, montmorillonite, clay or metal hydroxide.

[0083] The compatibilizer is γ-glycidyl etheroxypropyl trimethoxysilane, γ-methacryloxypropyl-trimethoxysilane or N-(β-aminoethyl)-γ-aminopropyl -Methyl-trimethoxysilane.

[0084] The antioxidant is tris[2,4-di-tert-butylphenyl]phosphite.

[0085] It also includes 5 parts of smoke suppressant and 0.06 part of anti-hydrolysis agent; said smoke suppressant is metal oxide; said anti-hydrolysis ag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of cable materials, and in particular relates to a flame-retardant thermoplastic polyurethane (TPU) cable sheathing material with an electromagnetic shielding function and a preparation method of the TPU cable sheathing material. The TPU cable sheathing material comprises the following raw materials in parts by weight: 25-85 parts of thermoplastic polyurethane, 5-45 parts of graphene, 5-35 parts of a flame retardant, 0.5-5 parts of a compatibilizer, and 0.02-0.1 part of an antioxidant. The TPU cable sheathing material provided by the invention has the electromagnetic shielding function, the shielding effectiveness (SE) value can reach 17-50 db, and the flame-retardant effect is excellent; and a single vertical burning test can reach a V0 level,the strength is high, the tensile strength can reach 25.2 MPa or more, the flexibility is good, the elongation at break is high and can reach 405% or more, and the mechanical properties are excellent.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a flame-retardant TPU cable sheath material with electromagnetic shielding function and a preparation method thereof. Background technique [0002] At present, cables are widely used in the fields of power systems, information transmission, and instrumentation systems. However, the cable covering materials made of traditional polymer material PVC are prone to fire and combustion during use, causing fires. Due to the The chlorine content is as high as 60%, which produces fumes of toxic gases such as hydrogen halides and carbon monoxide during combustion. [0003] Polyurethane elastomer refers to a type of elastomeric polymer containing more carbamate functional groups (NH-CO-O-) on the main chain of the macromolecule. It is a typical multi-block copolymer with wear resistance Good, wide hardness range, high strength, high elongation, large load support capacity, good shoc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L75/06C08L75/04C08K13/06C08K9/06C08K3/04H01B3/30
CPCC08L75/04C08L75/06C08L75/08C08L2201/02C08L2203/202H01B3/302C08L51/06C08K13/06C08K9/06C08K3/042
Inventor 李同兵黄有为刘悦钟荣栋
Owner ADVANCED THERMOPLASTIC POLYMER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com