Preparation method of temperature-resistant wear-resistant ceramic resin coating

A wear-resistant ceramic and resin coating technology, applied in the field of coatings, can solve the problems of easy agglomeration, small particle size of nano-ceramic powder, influence, etc., and achieve the effect of good spreading and film-forming, good comprehensive performance and good mechanical properties

Inactive Publication Date: 2018-04-20
枞阳县三金颜料有限责任公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, epoxy resin materials have deficiencies in heat resistance, wear resistance, dimensional stability, brittleness, etc., which affect their application.
In order to improve the quality of coatings, people add nano-ceramic powders to coatings to improve the overall physical and chemical properties of coatings. Although certain effects have been achieved, the dispersion effect is not good due to the small particles of nano-ceramic powders and easy agglomeration. Corresponding There is still a lot of room for improvement in the improvement of the mechanical and other qualities of coatings. For this, people will carry out surface modification treatment when filling and using it. The most common method is to use silane coupling agent for surface coupling modification treatment. Although The filling quality of nano-ceramic powder has been improved, but with the continuous improvement of people's requirements for coating performance, conventional surface modification methods have been unable to meet the needs of design and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing a temperature-resistant and wear-resistant ceramic resin coating, comprising the steps of:

[0029] (1) Preparation of modified resin:

[0030] a. First mix epoxy resin, phenolic resin, terpene resin, and nitrile rubber into the reactor according to the weight ratio of 75:10:5:2, heat to keep the temperature in the reactor at 45°C, and keep stirring After 30min, mixture A was obtained for subsequent use;

[0031] b. Add 0.3% methylpyrrolidone, 2% titanate coupling agent, 1% methyl carbazate, 2% malonate to the total mass of mixture A, and then raise the temperature in the reactor to 60°C, continuously stirred for 1 hour, then took out the modified resin for later use;

[0032] (2) Preparation of modified ceramic powder:

[0033] a. Put the nano-ceramic powder into a nitric acid solution with a mass fraction of 5%, filter it out after soaking for 4 minutes, then put it into a microwave processing instrument for microwave treatment, and take it o...

Embodiment 2

[0048] A method for preparing a temperature-resistant and wear-resistant ceramic resin coating, comprising the steps of:

[0049] (1) Preparation of modified resin:

[0050] a. First mix epoxy resin, phenolic resin, terpene resin, and nitrile rubber into the reactor according to the weight ratio of 78:13:7:4, heat to keep the temperature in the reactor at 47°C, and keep stirring After 32min, mixture A was obtained for subsequent use;

[0051] b. Add 0.5% methylpyrrolidone, 2.5% titanate coupling agent, 2% methyl carbazate, and 3% malonate to the total mass of mixture A in the reactor, and then raise the temperature in the reactor to 63°C, continuously stirred for 1.2 hours, then took out the modified resin for later use;

[0052] (2) Preparation of modified ceramic powder:

[0053] a. Put the nano-ceramic powder into a nitric acid solution with a mass fraction of 6%, filter it after soaking for 5 minutes, then put it into a microwave processing instrument for microwave proces...

Embodiment 3

[0068] A method for preparing a temperature-resistant and wear-resistant ceramic resin coating, comprising the steps of:

[0069] (1) Preparation of modified resin:

[0070] a. First mix epoxy resin, phenolic resin, terpene resin, and nitrile rubber into the reactor according to the weight ratio of 80:15:8:5, heat to keep the temperature in the reactor at 50°C, and keep stirring After 35min, mixture A was obtained for subsequent use;

[0071] b. Add 0.6% methylpyrrolidone, 3% titanate coupling agent, 3% methyl carbazate, and 4% malonate to the total mass of mixture A in the reactor, and then raise the temperature in the reactor to 65°C, continuously stirred for 1.5 hours, then took out the modified resin for later use;

[0072] (2) Preparation of modified ceramic powder:

[0073] a. Put the nano-ceramic powder into a nitric acid solution with a mass fraction of 7%, filter it out after soaking for 7 minutes, then put it into a microwave processing instrument for microwave tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a temperature-resistant wear-resistant ceramic resin coating. The method comprises the following steps: (1) preparation of modified resin, (2) preparation of modified ceramic powder, (3) weighing of raw materials for standby use, and (4) finished product coating preparation. The preparation method of the coating is specially improved, and the finallyobtained ceramic resin coating has good mechanical properties, is resistant to temperature and wear, and has good spreading film forming property, high bonding strength, excellent comprehensive performance, and high promotion application value.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a preparation method of a temperature-resistant and wear-resistant ceramic resin coating. Background technique [0002] Coatings are widely used in modern people's lives, which can not only improve the appearance of parts and products, but also improve their quality of use. Epoxy resin has excellent bonding, corrosion resistance, insulation and other properties, and is widely used in coatings. Due to the characteristics of high strength and low density, epoxy resin composite materials have gradually become one of the indispensable basic materials in the industrial field. However, epoxy resin materials have deficiencies in heat resistance, wear resistance, dimensional stability, brittleness, etc., which affect their application. In order to improve the quality of coatings, people add nano-ceramic powders to coatings to improve the overall physical and chemical properties of c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D161/06C09D5/08C09D5/25C09D7/63C09D7/65C09D7/62
CPCC08K2201/011C08L2201/08C08L2205/035C09D5/00C09D5/08C09D5/18C09D163/00C08L61/06C08L45/00C08L9/02C08K13/06C08K9/02C08K9/04C08K9/08C08K9/00C08K3/00C08K5/10
Inventor 周艺桃
Owner 枞阳县三金颜料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More