Degradable polypropylene foamed bead and producing process thereof

A technology of foamed beads and polypropylene, which is applied in the field of degradable polypropylene foamed beads and its production process, and can solve the problems of low mechanical properties, cell structure damage, and collapse of polypropylene foamed beads

Inactive Publication Date: 2017-04-19
苏州市炽光新材料有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] (2) How to improve the technical problems of low mechanical properties of polypropylene foamed beads and damage and collapse of cell structure due to the addition of biodegradable system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] This embodiment is a kind of degradable polypropylene foamed beads, including a polypropylene matrix, and the components in parts by weight of the polypropylene matrix include: polypropylene resin: 105 parts, 3-hydroxypropionitrile: 1 part, o-methyl Hydroquinone: 0.3 parts, nucleating agent: 2.6 parts, antioxidant: 3.1 parts, lubricant: 1.2 parts, filler: 6.5 parts; also includes biodegradation system, the addition amount of biodegradation system is the weight of polypropylene matrix 33%; the components by weight of the biodegradable system consist of: polylactic acid: 67 parts, polycaprolactone: 81 parts, ethoxylated alkylamine: 15 parts, hydroxypolydimethylsiloxane: 7.7 parts, vinyl trimethoxysilane: 8 parts, ammonium polyphosphate: 3.5 parts, nano-montmorillonite: 32 parts, fumed silica: 9.5 parts, γ-aminopropyl triethoxysilane: 2 parts , Alkylphenol polyoxyethylene ether: 2.1 parts, reactive diluent: 0.5 parts, compatibilizer: 0.5 parts, coupling agent: 1.1 parts, l...

Embodiment 2

[0023] This embodiment is a kind of degradable polypropylene foamed beads, including a polypropylene matrix, and the components in parts by weight of the polypropylene matrix include: polypropylene resin: 106 parts, 3-hydroxypropionitrile: 2 parts, o-methyl Hydroquinone: 0.4 parts, nucleating agent: 2.7 parts, antioxidant: 3.2 parts, lubricant: 1.3 parts, filler: 6.6 parts; also includes biodegradation system, the addition amount of biodegradation system is the weight of polypropylene matrix 34%; the components by weight of the biodegradable system consist of: polylactic acid: 68 parts, polycaprolactone: 82 parts, ethoxylated alkylamine: 16 parts, hydroxypolydimethylsiloxane: 7.8 parts, vinyl trimethoxysilane: 9 parts, ammonium polyphosphate: 3.6 parts, nano-montmorillonite 33 parts, fumed silica: 9.6 parts, γ-aminopropyl triethoxysilane: 3 parts, Alkylphenol polyoxyethylene ether: 2.2 parts, reactive diluent: 0.6 parts, compatibilizer: 0.6 parts, coupling agent: 1.2 parts, le...

Embodiment 3

[0027] This embodiment is a kind of degradable polypropylene foam beads, including a polypropylene matrix, and the components of the polypropylene matrix in parts by weight include: polypropylene resin: 107 parts, 3-hydroxypropionitrile: 3 parts, o-methyl Hydroquinone: 0.5 parts, nucleating agent: 2.8 parts, antioxidant: 3.3 parts, lubricant: 1.5 parts, filler: 6.7 parts; also includes biodegradation system, the addition amount of biodegradation system is the weight of polypropylene matrix 35% of ; the components by weight of the biodegradable system consist of: polylactic acid: 69 parts, polycaprolactone: 83 parts, ethoxylated alkylamine: 17 parts, hydroxypolydimethylsiloxane: 7.9 parts, vinyl trimethoxysilane: 10 parts, ammonium polyphosphate: 3.7 parts, nano-montmorillonite 35 parts, fumed silica: 9.7 parts, γ-aminopropyl triethoxysilane: 5 parts, Alkylphenol polyoxyethylene ether: 2.3 parts, reactive diluent: 0.7 parts, compatibilizer: 0.7 parts, coupling agent: 1.3 parts,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

A degradable polypropylene foamed bead is disclosed and includes a polypropylene matrix and a biodegradation system. The biodegradation system comprises 67-69 parts of polylactic acid, 81-83 parts of polycaprolactone, 15-17 parts of ethoxylated alkylamine, 7.7-7.9 parts of hydroxy polydimethylsiloxane, 8-10 parts of vinyltrimethoxysilane, 3.5-3.7 parts of ammonium polyphosphate, 32-35 parts of nanometer montmorillonite, 9.5-9.7 parts of fumed silica, 2-5 parts of gamma-aminopropyltriethoxysilane, 2.1-2.3 parts of alkylphenol polyoxyethylene, 0.5-0.7 part of an active diluting agent, 0.5-0.7 part of a compatilizer, 1.1-1.3 parts of a coupling agent, 1.5-1.7 parts of a levelling agent and 0.3-0.5 part of mixed rare earth chlorides. Through adding a high-strength system, degradation performance, strength, high-temperature resistance, flame retardance, physical properties and antistatic properties of the polypropylene foamed bead can be improved.

Description

technical field [0001] The invention relates to a production process of a polypropylene foam material, in particular to a degradable polypropylene foam bead and a production process thereof. Background technique [0002] There are isocyanate residues that are harmful to the human body during the foaming process of polyurethane foam, and the foamed material cannot be recycled. However, chlorofluorocarbons or butane are usually used in the foaming process of polystyrene (PS), which has adverse effects on the environment. The product is difficult to degrade and easy to form "white pollution". The United Nations Environmental Protection Organization has decided to stop using PS foam product. Cross-linked polyethylene foam has low rigidity and a maximum service temperature of 80°C. [0003] Compared with the above foam plastics, polypropylene foam material has many advantages: 1) Polypropylene (PP) is more rigid than polyethylene (PE), PP flexural modulus is about 1.52Gpa, PE i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L67/04C08L83/06C08L71/02C08K13/02C08K5/17C08K5/5425C08K3/32C08K3/34C08K3/36C08K5/544C08K3/16C08J9/18C08J9/12
CPCC08L23/12C08J9/122C08J9/18C08J2203/06C08J2203/08C08J2323/12C08J2467/04C08K2201/003C08K2201/011C08L2201/02C08L2201/04C08L2201/06C08L2201/08C08L2203/14C08L2205/025C08L2205/035C08L67/04C08L83/06C08L71/02C08K13/02C08K5/17C08K5/5425C08K2003/323C08K3/346C08K3/36C08K5/544C08K3/16
Inventor 张海忠顾军
Owner 苏州市炽光新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap