Process for producing anti-radiation worsted wool fabric containing stainless steel fibers

A production process and stainless steel technology, applied in the field of clothing fabrics, can solve the problems of uneven fabric surface, poor fabric resilience, easy to pilling, etc., and achieve the effect of strong water absorption and heat preservation, corrosion resistance, and reduction of disadvantages.

Inactive Publication Date: 2017-03-15
JIANGSU SUNSHINE
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the use of mordant dyeing process, although the color is uniform, the color fastness is good, and the cost is low, but the dyeing temperature is high, the time is long, the damage to the wool is great, and the fabric resilience is poor.
For another example, the use of inappropriate finishing process will make the surface of the fabric uneven, the phenomenon of curling is serious, the shrinkage rate is large, and it is easy to fluff and pilling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The invention relates to a production process of a radiation-proof worsted wool fabric containing stainless steel fibers. The fabric is made through the process of variety design, combing, spinning and finishing in sequence. The specific steps are as follows:

[0015] 1) Yarn variety design:

[0016] Choose wool fiber, cashmere fiber, bamboo charcoal polyester fiber and stainless steel fiber, anti-pilling treatment, enzyme treatment and softening treatment for wool fiber, cashmere fiber, bamboo charcoal polyester fiber and stainless steel fiber, anti-pilling treatment is anti-pilling treatment using phosphate ester antimony trioxide The mixture is used as an anti-pilling agent. The dosage of antimony trioxide phosphate mixture is 1.5-4% of the weight of wool fiber. The enzyme treatment is treated with protease. The dosage of protease is 0.1-0.2% of the weight of wool fiber. It is a water-soluble silicone softener, and the dosage of the water-soluble silicone softener is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a process for producing an anti-radiation worsted wool fabric containing stainless steel fibers. The process for producing the anti-radiation worsted wool fabric containing stainless steel fibers includes: selecting a phosphate ester-antimony trioxide mixture as an anti-pilling agent to perform anti-pilling treatment so as to improve the anti-pilling effect of fibers and the fabric, wherein the anti-pilling effect can reach 4-5 grade; and selecting a water-soluble organic silicon softener to perform softening treatment so as to allow a wool cashmere fiber fabric to possess a smooth and plump hand feeling. The stainless steel fibers have excellent characteristics including anti-radiation, high temperature resistance, corrosion resistance, and high strength, and then advantage complementation and weakness subduction of all the fibers can be achieved, and the fabric made of the fibers is high in strength, is high in water absorbing and thermal insulation performance, is stiff and smooth, and is beneficial to human health and environment protection.

Description

technical field [0001] The invention relates to a production process of a fabric, in particular to a production process of a radiation-proof worsted wool fabric containing stainless steel fibers, and belongs to the technical field of garment fabrics. Background technique [0002] The most important wool fiber for textile is sheep wool, which is usually called wool, or wool fiber, or wool for short. Its advantages are obvious. First, it has high water absorption and is very comfortable to wear. Second, it has warmth retention property, natural curl, and can form many stagnant air zones as a barrier. The third is durable, with very good stretchability and elastic recovery. The wool worsted fabrics currently on the market are often due to the use of inappropriate manufacturing methods, which greatly reduces the quality of the fabrics. For example, the use of mordant dyeing process, although the color is uniform, the color fastness is good, and the cost is low, but the dyeing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D03D15/02D06C9/02D06B21/00D06B15/00D06C7/02D02G3/04D02G3/12D06M13/292D06M11/47D06M16/00D06M13/50D06M101/12D06M101/32D03D15/233D03D15/25D03D15/283D03D15/47D03D15/50D03D15/513
Inventor 陶雅芸
Owner JIANGSU SUNSHINE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products