Modified fiber concrete tubular pile and preparation method thereof

A technology of concrete pipe piles and modified fibers, which is applied in the direction of manufacturing tools, reinforced molding, ceramic molding machines, etc., can solve the problems of adverse effects on the durability of concrete structures, degradation of use functions, and structural damage, so as to reduce harmful holes and defects content, promoting transformation, and the effect of bonding surface compaction

Inactive Publication Date: 2016-12-07
ANHUI XINRUN NEW MATERIALS
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Concrete structure is one of the most widely used structures. About 70% of the housing construction and 50% of bridge structures in China use concrete structures. With the increase of the service time of these engineering structures, the durability damage of concrete materials and structures is becoming more and more serious. The more attention is paid, many engineering structures often cause functional degradation or even structural damage due to durability, which brings unnecessary losses to society. Concrete carbonation is one of the important durability indicators of concrete. Due to carbon dioxide in the atmosphere and concrete The reaction of the alkaline substances in the concrete makes the concrete appear neutral, which is called the carbonization of the concrete. Carbonization makes the steel bars in the concrete structure lose the protection of the passivation film, which easily makes the steel bars rust, and then destroys the structure. With the continuous advancement of the industrialization process, the emission of carbon dioxide has increased greatly, which has a negative impact on the durability of concrete structures while producing the greenhouse effect;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A modified fiber concrete pipe pile, which is composed of the following raw materials in parts by weight:

[0022] Dimethylol propionic acid 0.2, n-methylpyrrolidone 7-10, bone char 20, ordinary Portland cement 640, yellow sand 400, gravel 300, polycarboxylate superplasticizer 15, polyethylene wax 20, peroxide Benzoyl 0.2, maleic anhydride 6, polyethylene glycol monomethyl ether 3, ethyl cellulose 4, sp-80 0.7, waste rubber powder 70, triethylamine 0.2, IPDI trimer 3.

[0023] A method for preparing a modified fiber concrete pipe pile, comprising the following steps:

[0024] (1) Add the above-mentioned polyethylene wax to No. 3 white oil that is 3 times its weight, add dibenzoyl peroxide and maleic anhydride, heat and stir at 140°C for 2 hours, cool the discharge to room temperature, and add to In acetone with 2-3 times the weight of the cooling material, fully stir, filter, dry, mix with polyethylene glycol monomethyl ether, add No. 3 white oil 1.8 times the weight o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified fiber concrete tubular pile. The modified fiber concrete tubular pile comprises, by weight, 0.1-0.2 parts of dimethylolpropionic acid, 7-10 parts of n-methylpyrrolidone, 10-20 parts of bone black, 500-640 parts of ordinary portland cement, 300-400 parts of yellow sand, 200-300 parts of broken stone, 7-15 parts of a polycarboxylic acid water reducer, 16-20 parts of polyethylene wax, 0.1-0.2 parts of dibenzoyl peroxide, 5-6 parts of maleic anhydride, 2-3 parts of methoxy polyethylene glycol, 4-7 parts of ethyl cellulose, 0.7-2 parts of sp-80, 50-70 parts of waste and old rubber powder, 0.1-0.2 parts of triethylamine and 2-3 parts of an IPDI trimer. The modified fiber concrete tubular pile further improves carbon dioxide intrusion inhibition, reduces harmful aperture and defect contents of a concrete structure, reduces hydration product alkalescence and promotes conversion of a low strength hydration product into a high strength hydration product.

Description

technical field [0001] The invention relates to a modified fiber concrete pipe pile, in particular to a modified fiber concrete pipe pile and a preparation method thereof. Background technique [0002] Concrete structure is one of the most widely used structures. About 70% of the house construction and 50% of bridge structures in China use concrete structures. With the increase of the service time of these engineering structures, the durability damage of concrete materials and structures is becoming more and more serious. The more attention is paid, many engineering structures often cause functional degradation or even structural damage due to durability, which brings unnecessary losses to society. Concrete carbonation is one of the important durability indicators of concrete. Due to carbon dioxide in the atmosphere and concrete The reaction of alkaline substances in the concrete makes the concrete appear neutral, which is called the carbonization of concrete. Carbonization ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04B28B21/66B28B21/68B28B11/24
CPCB28B11/245B28B21/66B28B21/68C04B28/04C04B24/04C04B24/128C04B14/022C04B14/06C04B2103/302C04B24/2611C04B24/12C04B24/32C04B24/383C04B18/22C04B24/121
Inventor 朱安会马洪章
Owner ANHUI XINRUN NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products