Hard heat-dissipation paint and preparation method therefor

A heat-dissipating coating and hard technology, applied in chemical instruments and methods, coatings, fibrous fillers, etc., can solve the problems of performance degradation, large specific surface area, high specific surface energy, etc., and achieve good weather resistance and high graft density , good dispersion effect

Inactive Publication Date: 2015-12-02
BENGBU NANZI INSTR
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nano-silica has a large specific surface area and high specific surface energy. It is easy to agglomerate in the coating to form secondary particles, resulting in a decrease in the performance of strengthening and toughening. At the same time, the hydroxyl groups on the surface also strengthen this phenomenon.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] A kind of hard heat dissipation coating, it is made up of the raw material of following weight part:

[0026] Ethylene glycol distearate 2, styrene maleic anhydride copolymer 12, propynyl alcohol 6, tetrahydrofuran 90, graphene 4, nano silicon dioxide 16, silane coupling agent KH5600.2, dimethylformamide 700, sodium nitride 4, aluminum trichloride 0.04, 2% sodium ascorbate solution 1.6, 2% copper sulfate solution 1.8, high-density polyethylene 120, barium metaborate 2, calcium palmitate 0.8, allyl thiourea 0.7, Polyoxypropylene glycol 0.6, aluminum silicate fiber 1, aluminum isopropoxide 0.1.

[0027] A kind of preparation method of described hard heat-dissipating paint, comprises the following steps:

[0028] (1) Mix the above-mentioned calcium palmitate and polyoxypropylene glycol, heat and stir at 60°C for 5 minutes, add styrene maleic anhydride copolymer, stir at 100 rpm for 20 minutes, wash twice with water, dry, and Mix propynyl alcohol and tetrahydrofuran, heat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses hard heat-dissipation paint. The hardheat-dissipation paint consists of the following raw materials in parts by weight:2-3 parts of ethylene glycol distearate, 12-15 parts of styrene-maleic anhydride copolymer, 6-10 parts of propargyl alcohol, 90-100 parts of tetrahydrofuran, 4-7 parts of graphene, 16-20 parts of nano silica, 0.2-0.3 part of a silane coupling agent KH560, 700-800 parts of dimethyl formamide, 4-5 parts of sodium nitride, 0.04-0.05 part of aluminium trichloride, 1.6-2 parts of a 2-3% sodium ascorbate solution, 1.8-2 parts of a 2-3% copper sulfate solution, 120-130 parts of high density polyethylene, 2-3 parts of barium metaborate, 0.8-1 part of calcium palmitate, 0.7-2 parts of allythiourea, 0.6-1 part of poly(oxypropylene) diol, 1-2 parts of aluminosilicate fibers, and 0.1-0.2 part of aluminum isopropoxide. The paint provided by the present invention is high in the surface hardness, good in the impact resistance, good in weather-ability, high in coating membrane stability, and superior in synthesis performance.

Description

technical field [0001] The invention relates to the technical field of heat dissipation coatings, in particular to a hard heat dissipation coating and a preparation method thereof. Background technique [0002] With the rapid development of modern science and technology, the high frequency and high speed of electronic devices and the density and miniaturization of integrated circuits have greatly increased the total power density and calorific value of electronic devices per unit volume, thus making the cooling of electronic devices more difficult. increasingly prominent. However, the cooling capacity achieved by conventional cooling systems is greatly challenged, especially in the fields of energy, automobiles, air conditioning, agriculture, chemicals, heating, aerospace, microelectronics, information, etc. put forward higher requirements. The heat dissipation paint is a special paint that improves the heat dissipation efficiency of the surface of the object and reduces t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/06C09D7/12C09C1/44C09C1/28C09C3/10C09C3/12C09C3/06
Inventor 闫秦峻
Owner BENGBU NANZI INSTR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap