High-strength and good-abrasion-resistance zirconium carbide ceramic material and preparing method thereof

A technology of ceramic materials and zirconium carbide, which is applied in the field of ceramic materials, can solve the problems of low mechanical strength and achieve the effects of improving wear resistance, high mechanical strength and chemical stability, and good high temperature resistance

Active Publication Date: 2015-11-04
NANTONG JUJIU NEW MATERIAL SCI & TECH CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mechanical strength of boron-based cermet materials is low, and there is still room for improvement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and good-abrasion-resistance zirconium carbide ceramic material and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A zirconium carbide ceramic material with high strength and good wear resistance, made of the following weight (kg) raw materials: kaolin 16, zirconium carbide 80, tungsten powder 2, black diamond powder 7, stainless steel powder 3, fly ash 6, ceramics Waste 8, polysilicate ferric sulfate 1, water glass 2, white oil 6, ferrosilicon nitride powder 3, red mud 1, molybdenum disilicide 1, polyvinyl alcohol 2, potassium nitrite 0.5, additive 5, water amount The auxiliary agent is made of the following weight (kg) raw materials: aluminum oxide 20, magnesium aluminum spinel powder 6, yttrium carbonate 1, silicon nitride 2, earthy graphite powder 2, diamond powder 0.5, bone powder 2, poly Sodium acrylate 0.5, polyethylene glycol 1, glycerin 2, water in proper amount; the preparation method is: mix aluminum oxide, magnesium aluminum spinel powder, yttrium carbonate, silicon nitride, earthy graphite powder, diamond powder, and bone powder into the mixture In the feeder, add sodiu...

Embodiment 2

[0023] A zirconium carbide ceramic material with high strength and good wear resistance, made of the following weight (kg) raw materials: kaolin 17, zirconium carbide 90, tungsten powder 2, black diamond powder 8, stainless steel powder 4, fly ash 7, ceramics Waste 10, polysilicate iron sulfate 2, water glass 3, white oil 7, ferrosilicon nitride powder 4, red mud 2, molybdenum disilicide 1, polyvinyl alcohol 3, potassium nitrite 0.6, additive 6, water amount ; The auxiliary agent is made of the following weight (kg) raw materials: aluminum oxide 25, magnesium aluminum spinel powder 7, yttrium carbonate 1, silicon nitride 2, earthy graphite powder 3, diamond powder 0.8, bone meal 3, poly Sodium acrylate 0.7, polyethylene glycol 2, glycerin 3, water in proper amount; the preparation method is: mix aluminum oxide, magnesium aluminum spinel powder, yttrium carbonate, silicon nitride, earthy graphite powder, diamond powder, and bone powder into the mixture In the feeder, add sodium...

Embodiment 3

[0030] A zirconium carbide ceramic material with high strength and good wear resistance, made of the following weight (kg) raw materials: kaolin 18, zirconium carbide 95, tungsten powder 3, black diamond powder 9, stainless steel powder 4, fly ash 8, ceramics Waste 12, polysilicate iron sulfate 3, water glass 3, white oil 8, ferrosilicon nitride powder 5, red mud 3, molybdenum disilicide 2, polyvinyl alcohol 4, potassium nitrite 0.8, additive 7, water amount ;

[0031] The auxiliary agent is made of the following weight (kg) raw materials: alumina 30, magnesium aluminum spinel powder 8, yttrium carbonate 2, silicon nitride 3, earthy graphite powder 4, diamond powder 1, bone powder 3, polyacrylic acid Sodium 0.8, polyethylene glycol 3, glycerin 4, water in proper amount; the preparation method is: mix alumina, magnesium aluminum spinel powder, yttrium carbonate, silicon nitride, earthy graphite powder, diamond powder, and bone powder to the mixture In the machine, add sodium p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength and good-abrasion-resistance zirconium carbide ceramic material and a preparing method thereof. The high-strength and good-abrasion-resistance zirconium carbide ceramic material comprises, by weight, 16-18 parts of kaolin, 80-95 parts of zirconium carbide, 2-3 parts of tungsten powder, 7-9 parts of black corundum powder, 3-4 parts of stainless steel powder, 6-8 parts of coal ash, 8-12 parts of ceramic waste, 1-3 parts of polysilicic acid ferric sulfate, 2-3 parts of water glass, 6-8 parts of white oil, 3-5 parts of ferro-silicon nitride powder, 1-3 parts of red mud, 1-2 parts of molybdenum disilicide, 2-4 parts of polyvinyl alcohol, 0.5-0.8 part of potassium nitrite, 5-7 parts of auxiliaries and an appropriate amount of water. The zirconium carbide serves as the main raw material of the ceramic material, and the prepared ceramic material has good high-temperature resisting performance, electric conduction performance and heat conducting performance, high mechanical strength and chemical stability; in addition, the fire resistance of the ceramic material is enhanced through the black corundum powder, the ferro-silicon nitride powder and the like; the abrasion resistance of the ceramic material is further improved through the tungsten powder, the stainless steel powder, the molybdenum disilicide, the auxiliaries and the like; and the quality of the product is guaranteed.

Description

technical field [0001] The invention relates to the technical field of ceramic materials, in particular to a zirconium carbide ceramic material with high strength and good wear resistance and a preparation method thereof. Background technique [0002] Ceramic materials are a class of inorganic non-metallic materials made of natural or synthetic compounds through shaping and high-temperature sintering. It has the advantages of high melting point, high hardness, high wear resistance and oxidation resistance. It can be used as structural material, tool material, and because ceramics also have some special properties, they can also be used as functional materials. [0003] Cermet has the advantages of both metal and ceramics. It has low density, high hardness, wear resistance, good thermal conductivity, and will not be brittle due to sudden cooling or heat. In addition, coating a layer of ceramic coating with good air tightness, high melting point and poor heat transfer perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/56C04B35/626
Inventor 张焕明
Owner NANTONG JUJIU NEW MATERIAL SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More