Fluorine-containing polymer-based dielectric composite film and preparation method thereof

A composite film and polymer technology, applied in the field of dielectric composite materials, can solve the problems of difficult processing of composite materials, large dielectric loss of composite materials, etc.

Active Publication Date: 2015-04-29
RUYUAN YAO AUTONOMOUS COUNTY DONGYANGGUANG FORMED FOIL CO LTD
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are mainly two ways to obtain this type of composite dielectric material: one, such as the Chinese patent CN102558718B, fills the polymer with ceramic particles with a high dielectric constant to prepare a ceramic / polymer two-phase composite, but in order to obtain a high The dielectric constant and the filling amount of ceramics are very high, which makes it difficult for composite materials to be processed into thin films; another kind such as CN1322052A, CN101423645B and CN102627781B is based on the percolation effect, and simultaneously fills conductive particles and ceramics in the polymer to prepare conductive Particle / ceramic / polymer three-phase composite, but the dielectric loss of the obtained composite is relatively large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorine-containing polymer-based dielectric composite film and preparation method thereof
  • Fluorine-containing polymer-based dielectric composite film and preparation method thereof
  • Fluorine-containing polymer-based dielectric composite film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] In some embodiments of the present invention, the metal conductive powder is selected from aluminum powder or zinc powder;

[0008] In some embodiments of the present invention, the fluoropolymer is polyvinylidene fluoride, polyvinylidene fluoride-trifluoroethylene, polyvinylidene fluoride-trifluoroethylene-chlorotrifluoroethylene, polyvinylidene fluoride- Any of hexafluoropropylene;

[0009] In some embodiments of the present invention, the core of the rubber particles is acrylic rubber, and the shell is polymethyl methacrylate core-shell rubber.

[0010] In some embodiments of the present invention, the mass ratio of metal conductive powder, barium zirconate titanate, rubber particles, and fluoropolymer is 1-2.5:17.5:2:10.

[0011] In some embodiments of the present invention, the mass ratio of metal conductive powder, barium zirconate titanate, rubber particles, and fluoropolymer is 2:17.5:2:10.

[0012] In some embodiments of the present invention, the mass ratio ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fluorine-containing polymer-based dielectric composite film. The dielectric composite film is prepared from conductive metal powder, calcium copper titanate, rubber particles and fluorine-containing polymer as raw materials in the presence of a compound liquid of N, N-dimethyl acetamide and polyacrylic acid as a solvent, wherein the mass ratio of components is (0-2.5): (10-30): (0-3): 10. The invention also discloses a preparation method of the composite film. The fluorine-containing polymer-based dielectric composite film is a dielectric composite film which has the advantages of high dielectric constant, high compressive strength, low dielectric loss and excellent elongation and controllable thickness.

Description

technical field [0001] The invention relates to the field of dielectric composite materials, in particular to a fluorine-containing polymer-based dielectric composite film and a preparation method thereof. Background technique [0002] With the rapid development of the microelectronics industry, the demand for miniaturized capacitors is becoming more and more urgent. In order to obtain capacitors with light weight and high energy storage density while being small in size, it is key to develop dielectric films with low density, high dielectric constant and high withstand voltage as dielectric materials. Traditional organic thin film dielectric materials are mostly polymer single-phase materials, and the general dielectric constant is between 1 and 3, which makes the capacitors produced by them have low capacitance density and cannot meet the needs of industry development. Although the ceramic material has a relatively high dielectric constant, its processing performance is p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/16C08K3/08C08K3/24C08J5/18
CPCC08J5/18C08L27/16C08L2205/025C08L2205/035C08L2207/53C08L33/02C08L33/12C08K2003/0812C08K3/24C08K2003/0893
Inventor 栗彦娜邹智杰汤诚
Owner RUYUAN YAO AUTONOMOUS COUNTY DONGYANGGUANG FORMED FOIL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products