Method for manufacturing delivery steel pipe serving acid environment

A manufacturing method and technology of steel pipes, applied in the direction of manufacturing tools, tubular objects, applications, etc., can solve the problems of poor uniformity of steel pipe structure, poor corrosion resistance of steel pipes, etc., and achieve the effects of improved heat treatment process, high corrosion resistance, and low cost

Inactive Publication Date: 2012-07-18
CHINA NAT OFFSHORE OIL CORP +2
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] What the present invention aims to solve is the poor corrosion resistance of the steel pipe caused by the serious band structure in the center of the plate during the raw material rolling process and the poor uniformity of the steel pipe structure caused by the residual stress and poor heat treatment state in the pipe making process. technical problem, to provide a product that resists H 2 A method for manufacturing steel pipes for service in acidic environments with significantly improved S performance. The steel pipes manufactured by this method have resistance to hydrogen-induced cracking and sulfide stress corrosion resistance, high strength and high pressure resistance, can reduce costs, and can meet steel pipes under acid service conditions. usage of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing delivery steel pipe serving acid environment
  • Method for manufacturing delivery steel pipe serving acid environment
  • Method for manufacturing delivery steel pipe serving acid environment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The present invention will be described in further detail below through specific examples. The following examples can enable those skilled in the art to understand the present invention more comprehensively, but do not limit the present invention in any way.

[0028] The invention discloses a method for manufacturing steel pipes for service in acidic environments. The process of the method includes raw material inspection, uncoiling butt welding, loop storage, steel plate edge milling, steel pipe forming, steel pipe welding, heat treatment of weld seams, air cooling and water cooling, Steel pipe sizing, steel pipe straightening and steel pipe cutting.

[0029] The present invention controls the H resistance of the pipeline steel pipe from the material factors and the pipe making process. 2 S performance, first of all, resistance to H 2 In addition to maintaining the fine grain and high toughness of ordinary pipeline steel, S pipeline steel has higher requirements on th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for manufacturing a delivery steel pipe serving an acid environment. The steel pipe comprises the following chemical components of raw materials in percentage by weight: less than or equal to 0.1 percent of C, less than or equal to 1.6 percent of Mn, less than or equal to 0.02 percent of P, less than or equal to 0.002 percent of S, less than or equal to 0.15 percent of Nb, V and Ti, less than or equal to 0.22 percent of Pcm, more than or equal to 1.5 percent of Ca / S and the balance of Fe. High frequency induction welding is adopted in welding of the steel pipe; the welding quality is improved in the welding process by increasing the welding extrusion quantity, controlling the open angle of seams and increasing welding protective gas; and on-line quenching and on-line tempering are performed in heat treatment of the seams by adopting six intermediate frequency heat treatment machines. By selection of raw material components and metallographic structures, completeness of a welding mechanism and improvement of the heat treatment process, the steel pipe has hydrogen induced cracking resistance and sulfide stress corrosion resistance and has high strength and high pressure resistance, the cost can be reduced, and the use of the steel pipe under the acid serving condition can be met.

Description

technical field [0001] The invention relates to a method for manufacturing a steel pipe in the metallurgical industry, in particular to a method for manufacturing a steel pipe for transportation used in an acidic environment. Background technique [0002] At present, the delivery steel pipes used in acidic environments usually adopt seamless steel pipes. For example, the Chinese invention patent with the publication number CN101146924 "Steel for oil well pipes with excellent resistance to sulfide stress cracking and a method for manufacturing seamless steel pipes for oil wells" proposed A seamless steel pipe for oil wells that can be used in acidic environments. The seamless steel pipe uses higher carbon content and alloying elements to improve corrosion resistance, but has uneven wall thickness, low geometric dimension accuracy, low impact toughness and production costs. advanced defects. [0003] The high-frequency welded (HFW) pipeline steel pipe serving in acidic enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C21D8/10B21C37/08B23K13/01B23K101/06B23K103/04
Inventor 杨连河叶培荣倪明津张晓灵顾艳吴刚孟爱平
Owner CHINA NAT OFFSHORE OIL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products