Anti-corrosion heat-conducting coating for heat exchanger and preparation method of coating

A heat-conducting coating and anti-corrosion technology, applied in the direction of anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of unsuitable use, non-temperature-resistant coatings, etc., and achieve the effect of promoting heat transfer performance and improving thermal conductivity

Active Publication Date: 2013-03-13
江苏四方威凯科技有限公司
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional anti-corrosion and heat-conducting coatings for heat exchangers include epoxy-phenolic anti-corrosion and heat-conducting coatings. This type of coating has excellent acid and alkali resistance, but this type of coating is not heat-resistant, and it is not suitable for use when the working temperature exceeds 200 ° C.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-corrosion heat-conducting coating for heat exchanger and preparation method of coating
  • Anti-corrosion heat-conducting coating for heat exchanger and preparation method of coating
  • Anti-corrosion heat-conducting coating for heat exchanger and preparation method of coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] (1) Add 27g of resin A, 6g of xylene, 8g of butyl ester, 10g of propylene glycol methyl ether acetate and 0.5g of additives into the operation kettle, and disperse for 2min at a speed of 800RPM; resin A is Hubei Sihai Chemical Co., Ltd. Co., Ltd. SH-023-7 type silicone modified epoxy resin product; additive is Bayer's BYK-180 type wetting and dispersing agent;

[0049](2) Add 20g of aluminum nitride, 5g of glass powder, 7g of barium sulfate, 5g of titanium dioxide and 7g of aluminum tripolyphosphate into the operation kettle, add 100g of zirconium beads, and grind for 60min at a speed of 1200RPM; aluminum nitride is Zibo The aluminum nitride powder produced by Jingyi Ceramic Technology Co., Ltd. is PW, a commercially available product with a particle size within the range of 1-15 μm. The glass powder is the glass powder produced by Taizhou Xinhai Special Material Parts Factory, and its softening temperature is 320 ℃-340℃, the sintering temperature is 360℃-380℃; barium s...

Embodiment 2

[0061] (1) Add 30g of resin A, 5g of xylene, 5g of butyl ester, 6g of propylene glycol methyl ether acetate and 1g of additives into the operation kettle, and disperse for 2min at a speed of 800RPM; resin A is from Hubei Sihai Chemical Co., Ltd. Co., Ltd. SH-023-7 type silicone modified epoxy resin product; additive is Bayer's BYK-180 type wetting and dispersing agent;

[0062] (2) Add 22g of aluminum nitride, 6g of glass powder, 7g of barium sulfate, 5g of titanium dioxide and 8g of aluminum tripolyphosphate into the operation kettle, add 110g of zirconium beads, and grind for 80min at a speed of 800RPM; aluminum nitride is Zibo The aluminum nitride powder produced by Jingyi Ceramic Technology Co., Ltd. is PW, a commercially available product with a particle size within the range of 1-15 μm. The glass powder is the glass powder produced by Taizhou Xinhai Special Material Parts Factory, and its softening temperature is 320 ℃-340℃, the sintering temperature is 360℃-380℃; barium...

Embodiment 3

[0074] (1) Add 34.4g of resin A, 6g of xylene, 7g of butyl ester, 6g of propylene glycol methyl ether acetate and 0.5g of additives into the operation kettle, and disperse for 2min at a speed of 800RPM; resin A is Hubei Sihai SH-023-7 type organosilicon modified epoxy resin product of Chemical Industry Co., Ltd.; the auxiliary agent is BYK-180 type wetting and dispersing agent of Bayer Company;

[0075] (2) Add 18g of aluminum nitride, 5g of glass powder, 6g of barium sulfate, 5g of titanium dioxide and 6g of aluminum tripolyphosphate into the operation kettle, add 120g of zirconium beads, and grind for 70min at a speed of 1000RPM; aluminum nitride is Zibo The aluminum nitride powder produced by Jingyi Ceramic Technology Co., Ltd. is PW, a commercially available product with a particle size within the range of 1-15 μm. The glass powder is the glass powder produced by Taizhou Xinhai Special Material Parts Factory, and its softening temperature is 320 ℃-340℃, the sintering tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Softening temperatureaaaaaaaaaa
Sintering temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-corrosion heat-conducting coating for a heat exchanger and a preparation method of the coating. The formula of the anti-corrosion heating conducting coating comprises the following raw materials by weight percent: 30%-40% of matrix resin, 40%-50% of filler, 0.5%-1% of auxiliaries and 15%-25% of diluting agent, wherein the matrix resin is a mixture of resin A and resin B, the resin A is a SH-023-7 type organic silicon modified epoxy resin product, the resin B is a 2130 type phenolic resin product, and the filler is a mixture of 40%-55% of aluminum nitride, 10%-15% of glass powder, 15%-25% of barium sulfate and 10%-15% of titanium dioxide. With the coating provided by the invention, better anti-corrosion performance and heat-conducting performance of the heat exchanger are realized; and in the filler range, the heat conductivity of the coating is maximally up to 3.912W / (m.k).

Description

technical field [0001] The invention relates to an anti-corrosion and heat-conducting coating, in particular to an anti-corrosion and heat-conducting coating for a heat exchanger and a preparation method thereof. Background technique [0002] As an indispensable equipment in the chemical industry, heat exchangers cost about 10%-40% of the total investment, and the corrosion of heat exchangers causes huge economic losses every year. Anti-corrosion and heat-conducting coatings for heat exchangers not only need to ensure sufficient corrosion resistance, but also ensure good thermal conductivity. Traditional anti-corrosion and heat-conducting coatings for heat exchangers include epoxy-phenolic anti-corrosion and heat-conducting coatings. This type of coating has excellent acid and alkali resistance, but this type of coating is not heat-resistant, and it is not suitable for use when the working temperature exceeds 200 ° C. . Contents of the invention [0003] The invention ai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D161/06C09D7/12C09D5/08
Inventor 方芳朱洪江李静冯杰超
Owner 江苏四方威凯科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com