Method for preparing activated carbons by using plastics of recycled waste circuit boards as raw material

A technology for preparing activated carbon and waste circuit boards, which is used in electronic waste recycling, recycling technology, and solid waste removal. Energy-saving, automation-friendly effects

Inactive Publication Date: 2011-01-19
KUNMING UNIV OF SCI & TECH
View PDF2 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These treatment methods either have low recycling rates and high treatment costs, or produce waste gas containing dioxins, furans and carbon dioxide during the treatment process, causing serious air pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing activated carbons by using plastics of recycled waste circuit boards as raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Using the above-mentioned technological process, using zinc chloride as the activator, under the conditions of microwave power 633W, irradiation time 8min, and zinc chloride volume percentage 40%, the iodine adsorption value of the activated carbon product is 426.8mg / g, methylene blue The adsorption value is 52.4mg / g, and the yield is 37.3%.

Embodiment 2

[0044] Using the above-mentioned technological process, using phosphoric acid as an activator, under the conditions of microwave power 792W, irradiation time 10min, and phosphoric acid volume percentage 30%, the activated carbon product has an iodine adsorption value of 404.8mg / g and a methylene blue adsorption value of 47.2mg. / g, yield 38.1%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
iodine adsorption valueaaaaaaaaaa
iodine adsorption valueaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for recycling the plastics of waste circuit boards, which comprises the following steps: preparing activated carbons by using the plastics of screened waste circuit boards as a raw material through the methods of chemical activation and microwave heating; then soaking the obtained activated carbons in drug with certain concentration for twenty-four hours, wherein the volume ratio of the plastic powder of the waste circuit boards to the drug is 1:3; activating by putting the activated carbons in a micro-wave oven for radioactivation; carrying out acid-washing on the activated carbons subjected to radioactivation by hydrochloric acid solution with 1:9 in volume ratio so as to remove ashes; rinsing the activated carbons subjected to acid-washing by water so as to regulate the pH value of the activated carbon to be 7; finally, putting the activated carbons in a drying oven, and then crushing the dried activated carbons so as to obtain the finished activated carbon product. The iodine sorption value of the prepared activated carbon product is 404.8 mg / g, the methylene blue sorption value thereof is 47.2 mg / g, and the yield is 38.1 percent. By using the method of the invention, the plastics of waste circuit boards are prepared into activated carbons by using the methods of chemical activation and microwave heating, and the adsorption property of the prepared activated carbon is similar to that of general industrial activated carbons, therefore, the method of the invention is also a new better way for recycling the plastics of waste circuit boards.

Description

technical field [0001] The invention relates to recycling of waste materials, in particular to a method for preparing activated carbon from the recycling of waste circuit board plastics in electronic products. Background technique [0002] Every year, tens of thousands of circuit boards are scrapped in electronic products. These circuit boards contain a large amount of metal. Landfilling is not only a waste of resources, but also will leach highly toxic metal elements and pollute groundwater. Therefore, effective treatment and disposal of waste circuit boards can reduce the volume of pollutants, stabilize dangerous components, and recycle useful components. Waste circuit boards usually contain 30% plastic, and there are five main processing methods: one is to process waste polymer materials directly after classification, cleaning, crushing, and granulation; the other is to process polymer materials through thermal decomposition technology. Carry out pyrolysis, that is, deco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/12B09B3/00
CPCY02W30/82
Inventor 张德华邓杰宁平
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com