Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A glass and emulsifier technology, applied in the direction of manufacturing tools, metal processing equipment, grinding/polishing equipment, etc., can solve the problems affecting the quality of grinding, uneven joints, easy to burst, etc.
Inactive Publication Date: 2021-11-26
浙江兆民玻璃技术有限公司
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] Aiming at the technical problems existing in the prior art, the present invention provides a glass and its preparation method to solve the problem of cutting, edging, washing, drying and tempering when the existing toughened glass is prepared. It is necessary to use an edging device to grind the edges. Usually, after the edge is finished, the corners must be rounded, which makes the grinding efficiency low. Flat, making it easy to burst during tempering, and, when grinding, the glass cannot be stably limited, thus affecting the quality of grinding
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0041] The principles and features of the present invention are described below in conjunction with the accompanying drawings, and the examples given are only used to explain the present invention, and are not intended to limit the scope of the present invention.
[0042] Tempered glass is a kind of glass, which belongs to safety glass. It is a kind of prestressed glass. In order to improve the strength of glass, chemical or physical methods are usually used to form compressive stress on the glass surface. When the glass is subjected to external force, the surface stress is first offset. The bearing capacity is improved, and the glass's own wind pressure resistance, cold and heat resistance, impact resistance, etc. are enhanced.
[0043] The inventor conducted in-depth investigation and research on the preparation process of tempered glass and found that; during the preparation of tempered glass, it needs to go through steps such as cutting, edging, washing, drying and temperin...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of glass, in particular to glass and a preparation method thereof. The invention discloses glass, which is prepared from the following raw materials in parts by mass: 70 to 80 parts of water, 4 to 5 parts of emulsifier, 2 to 3 parts of n-butyl acrylate, 6 to 7 parts of polymethylhydrosiloxane, 11 to 12 parts of polydimethylsiloxane, 14 to 15 parts of acrylic acid, 10 to 11 parts of polymethacrylate, 1 to 2 parts of tert-butyl hydroperoxide, 25 to 30 parts of polyurethane resin and 4 to 5 parts of lithium sulfate. The invention has the beneficial effects that when a glass body is polished, it can be guaranteed that the glass body cannot move in the polishing process, the polishing quality is guaranteed, meanwhile, an air pump is started, air exhaust operation is conducted on a supporting pipe, therefore, suction force exists on the glass body at the position of a through hole, the limiting effect is better, and in addition, the corners of the glass body can be continuously polished through one polishing head, the whole polishing operation is completed, the polishing efficiency is higher, polishing is more uniform and smoother, and the polishing quality is guaranteed.
Description
technical field [0001] The invention relates to the technical field of glass, in particular to glass and a preparation method thereof. Background technique [0002] Tempered glass is a kind of glass, which belongs to safety glass. It is a kind of prestressed glass. In order to improve the strength of glass, chemical or physical methods are usually used. Physical tempered glass is also called quenched tempered glass. It heats ordinary flat glass in a heating furnace to tempering temperature, that is, when it is close to the softening temperature of the glass, eliminates the internal stress through its own deformation, then moves the glass out of the heating furnace, and then blows high-pressure cold air to the glass with a multi-head nozzle. Tempered glass can be produced by quickly and evenly cooling to room temperature, and compressive stress is formed on the surface of the glass. When the glass is subjected to external force, the surface stress is first offset, thereby imp...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.