Optical glass with high refractive index and preparation method thereof

A technology of optical glass and high refractive index, applied in the field of optical glass, can solve the problems of increasing equipment erosion, undisclosed anti-reflection coating, refractive index and other performances that need to be further improved, so as to promote glass network crosslinking and enhance refractive index and light transmittance, enhanced strength and density effects

Active Publication Date: 2021-10-19
GUOGUANG OPTICAL GLASS CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the strong corrosion of tungsten oxide and zinc oxide used in this patent, it will increase the erosion of equipment during the preparation process; at the same time, the specific anti-reflection coating is not disclosed, and the refractive index and other properties need to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Step 1: (1) ultrasonically disperse bismuth nitrate in ethylene glycol, drop zinc nitrate solution; ultrasonically homogenize; place the obtained solution in a microwave reactor, set the power to 520W for 5 minutes, wash, filter and dry; Transfer to a high-temperature furnace and set the temperature at 550°C for 1.5 hours to obtain Zn-Bi 2 o 3 . (2) Mix tetrabutyl titanate, absolute ethanol, and hydrofluoric acid evenly, add copper nitrate and cerium nitrate, and stir continuously for 3.5 hours to obtain a mixed solution, which is placed in an autoclave with a temperature of 160°C , hydrothermal reaction for 24 hours, washed, filtered and dried; transferred to a high-temperature furnace, set the temperature at 450 ° C for 2.5 hours in a nitrogen atmosphere, and calcined for 2.5 hours to obtain Ce-Cu-TiO 2 . (3) Dissolve ammonium metatungstate in deionized water, add indium nitrate, stir to form a sol, add polyvinyl alcohol solution, add nitric acid dropwise, homogeni...

Embodiment 2

[0033] Step 1: (1) ultrasonically disperse bismuth nitrate in ethylene glycol, drop zinc nitrate solution; ultrasonically homogenize; place the obtained solution in a microwave reactor, set the power to 520W for 2 minutes, wash, filter and dry; Transfer to a high-temperature furnace and set the temperature at 500°C for 1 hour to obtain Zn-Bi 2 o 3 . (2) Mix tetrabutyl titanate, absolute ethanol, and hydrofluoric acid evenly, add copper nitrate and cerium nitrate, and stir continuously for 3 hours to obtain a mixed solution, which is placed in a high-pressure reactor and set at a temperature of 160°C , hydrothermal reaction for 24 hours, washed, filtered and dried; transferred to a high-temperature furnace, set the temperature at 400 ° C for 2 to 3 hours in a nitrogen atmosphere, and obtained Ce-Cu-TiO 2 . (3) Dissolve ammonium metatungstate in deionized water, add indium nitrate, stir to form a sol, add polyvinyl alcohol solution, add nitric acid dropwise, homogenize; lyoph...

Embodiment 3

[0038] Step 1: (1) ultrasonically disperse bismuth nitrate in ethylene glycol, drop zinc nitrate solution; ultrasonically homogenize; place the obtained solution in a microwave reactor, set the power to 520W for 6 minutes, wash, filter and dry; Transfer to a high-temperature furnace and set the temperature at 600°C for 2 hours to obtain Zn-Bi 2 o 3 . (2) Mix tetrabutyl titanate, absolute ethanol, and hydrofluoric acid evenly, add copper nitrate and cerium nitrate, and stir continuously for 4 hours to obtain a mixed solution, which is placed in a high-pressure reactor and set at a temperature of 160°C , hydrothermal reaction for 24 hours, washed, filtered and dried; transferred to a high-temperature furnace, set the temperature at 500 ° C for 3 hours in a nitrogen atmosphere, and calcined for 3 hours to obtain Ce-Cu-TiO 2 . (3) Dissolve ammonium metatungstate in deionized water, add indium nitrate, stir to form a sol, add polyvinyl alcohol solution, add nitric acid dropwise,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses optical glass with high refractive index and a preparation method thereof. The optical glass with the high refractive index comprises base glass and an anti-reflection coating; the raw material of the base glass comprises In-W composite nanoparticles; and the In-W composite nanoparticles are obtained by pre-doping WO3 and In2O3 according to a mass ratio of (0.5-0.7): 1. The optical glass has the beneficial effects that WO3 and In2O3 are used for pre-doping to inhibit the corrosivity of a monometal oxide, and dipole interaction between two metals is used for reforming a light absorption band gap, so that the refractive index and the light transmittance of the optical glass are further enhanced, the dosage of the two metals WO3 and In2O3 is reduced, and meanwhile, the corrosion resistance of the glass is further enhanced; and the metal effect in Ce-Cu-TiO2 is utilized to induce generation of high-transmittance bismuth silicate crystals with high refraction and low dispersion, so that the performance and quality of the glass are further enhanced.

Description

technical field [0001] The invention relates to the technical field of optical glass, in particular to a high refractive index optical glass and a preparation method thereof. Background technique [0002] Optical glass is a kind of glass material that transmits light through refraction, reflection and transmission, with the key technologies of refractive index, Abbe number and transmittance. It is used to manufacture lenses, prisms, mirrors, windows, etc., and is widely used in optical instruments such as cameras and microscopes. Among them, high refractive index and dispersion determine the basic performance of optical glass. At present, because the higher the refractive index, the thinner and lighter the optical glass, the better the light transmittance, so the pursuit of optical glass with a higher refractive index. However, under normal circumstances, the refractive index is inversely proportional to the dispersion, and the increase of the refractive index will lead to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/068
CPCC03C3/068
Inventor 沈杰沈强国
Owner GUOGUANG OPTICAL GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap