A kind of oxide reinforced low activation steel and its manufacturing method

A low-activation steel and manufacturing method technology, applied in the field of iron and steel metallurgy, can solve the problems of high cost, low efficiency, and difficulty in producing oxide-strengthened steel, etc., achieve strong effects, improve high-temperature mechanical properties, and improve He brittleness resistance Effect

Active Publication Date: 2021-12-07
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF22 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, limited by the mechanical alloying method, the cost is high and the efficiency is low
A nuclear fusion demonstration reactor needs to use about 3,500 tons of low-activation materials. Due to the lack of large-scale production equipment, it is difficult to produce such a large-scale oxide-strengthened steel by mechanical alloying.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of oxide reinforced low activation steel and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The manufacturing method of the oxide-reinforced low-activation steel of this embodiment comprises the following steps:

[0044] (1) Ultra-pure smelting of rare earth-rich steel: use a vacuum induction furnace to smelt according to the chemical composition of 9Cr2WVTa steel, and wait until the composition of the low-activation steel reaches the standard (and the mass fraction of oxygen in the steel is less than 10×10 -6 ) to add Ti pure metal, after the Ti metal is melted, add rare earth Y, after adding rare earth Y, carry out 300kW power stirring and refining for 15min, and then carry out tapping and casting into steel ingots; wherein, the amount of Ti added is 0.25% of the mass of the low-activation steel ; The amount of Y added is 0.5% of the low-activation steel mass;

[0045] (2) Pretreatment of low-activation steel: place the steel ingot at 1200 ° C for 3 hours, and then roll it into a wire rod with a diameter of 5 mm for use; during the rolling process, the start...

Embodiment 2

[0050] The manufacturing method of the oxide-reinforced low-activation steel of this embodiment comprises the following steps:

[0051] (1) Ultra-pure smelting of rare earth-rich steel: use a vacuum induction furnace to smelt according to the chemical composition of 9Cr2WVTa, and wait until the composition of the low-activation steel reaches the standard (and at this time the mass fraction of oxygen in the steel is less than 10×10 -6 ) to add Ti pure metal, after the Ti metal is melted, add rare earth Y, after adding rare earth Y, carry out 500kW power stirring and refining for 10min, and then carry out tapping and casting into steel ingots; wherein, the amount of Ti added is 0.5% of the mass of the low-activation steel ; The amount of Y added is 1% of the low-activation steel mass;

[0052] (2) Pretreatment of low-activation steel: place the steel ingot at 1250°C for 2 hours, and then roll it into a wire rod with a diameter of 10mm for use; during the rolling process, the sta...

Embodiment 3

[0057] The manufacturing method of the oxide-reinforced low-activation steel of this embodiment comprises the following steps:

[0058] (1) Ultra-pure smelting of rare earth-rich steel: use a vacuum induction furnace to smelt according to the chemical composition of 9Cr2WVTa steel, and wait until the composition of the low-activation steel reaches the standard (and the mass fraction of oxygen in the steel is less than 10×10 -6 ) to add Ti pure metal, after the Ti metal is melted, add rare earth Y, after adding rare earth Y, carry out stirring and refining with 400kW power for 13min, and then carry out tapping and casting into steel ingots; wherein, the amount of Ti added is 0.35% of the mass of the low-activation steel ; The amount of Y added is 0.65% of the low-activation steel mass;

[0059] (2) Pretreatment of low-activation steel: place the steel ingot at 1230°C for 2.5 hours, and then roll it into a wire rod with a diameter of 7mm for use; during the rolling process, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an oxide-reinforced low-activation steel and a manufacturing method thereof. The manufacturing method comprises: adding Ti, Zr or Hf to the low-activation steel when the composition of the low-activation steel reaches the standard during the smelting process of the low-activation steel , after being melted, add Y and stir evenly, tap out and cast into steel ingots; carry out uniform annealing and rolling on the steel ingots to obtain wire rods; draw the wire rods into wires; arc fuse the wires Forming to obtain the oxide-strengthened low-activation steel; the ion gas and protective gas used in the arc fuse forming process are both CO 2 Mixed gas with Ar gas, the cooling method is natural cooling and solidification under Ar protection atmosphere. The oxide-strengthened low-activation steel of the present invention has a more complex structure of the oxide-strengthened reinforcement phase, and has better high-temperature mechanical properties than the existing oxide-strengthened low-activation steel, and the processing method of the present invention can quickly realize oxide strengthening. The processing of low-activation steel helps to increase the yield of oxide-strengthened low-activation steel.

Description

technical field [0001] The invention belongs to the technical field of iron and steel metallurgy, and in particular relates to an oxide-strengthened low-activation steel and a manufacturing method thereof. Background technique [0002] As an important engineering structural material, low-activation steel is considered to be the preferred structural material for the cladding of the first wall of a nuclear fusion reactor due to its advantages such as low activation, low radiation swelling rate, and excellent thermophysical properties. The design working temperature range of low-activation steel is 325-550°C, which can no longer meet the requirements of CFETR Phase II and future nuclear fusion reactors. The current main solution is to add oxide disperse phases to prepare oxide-strengthened alloys, which adopt mechanical alloying process The prepared steel has the best performance. Dispersed distribution of Y in steel 2 o 3 It can pin dislocations to improve the high-temperat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04C22C38/22C22C38/24C22C38/26C22C38/28B21C1/02B22F10/18C21D1/26C21D6/00C21D8/06C21D9/52B33Y10/00B33Y70/10
CPCB21C1/02B33Y10/00B33Y70/10B22F10/18C21D1/26C21D6/002C21D8/065C21D9/525C22C32/0026C22C33/04C22C38/005C22C38/22C22C38/24C22C38/26C22C38/28Y02P10/25
Inventor 邱国兴李小明韦旭立白冲贺芸李林波
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com