A kind of carbon dot/polyurethane composite material and its preparation method and application

A composite material and polyurethane technology, applied in chemical instruments and methods, organic compound/hydride/coordination complex catalysts, chemical/physical processes, etc., can solve separation difficulties, small carbon dot size, and unreported inventions, etc. problem, to achieve the effect of simple preparation process, easy separation and environmental friendliness

Active Publication Date: 2021-12-14
NORTH CHINA ELECTRIC POWER UNIV (BAODING)
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the size of carbon dots is small, and it is difficult to separate them when used alone. It needs to be combined with solid-phase materials. The composite material of synthesized carbon dots is convenient for application.
So far, no related inventions using carbon dots for photocatalytic enrichment of uranium have been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of carbon dot/polyurethane composite material and its preparation method and application
  • A kind of carbon dot/polyurethane composite material and its preparation method and application
  • A kind of carbon dot/polyurethane composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) Synthesize yellow light carbon dots by hydrothermal method: weigh 2.3g of neutral red with a balance and dissolve in 60mL of ethylene glycol, and stir for 30 minutes. Then it was transferred to a polytetrafluoroethylene-lined stainless steel hydrothermal reactor and reacted at 200°C for 4 hours. After the reaction was finished, it was naturally cooled to room temperature, and the reacted solution and solid were taken out, and centrifuged and washed with a mixed solution of n-hexane and acetone (volume ratio: 95:5). After centrifugation, take the supernatant in a beaker, which is the carbon dot solution used later, and its concentration is 0.1g / L.

[0035](2) Synthesis of carbon dots / polyurethane composite material: Polyurethane is a commercially available polyurethane foam, which is cut into cubes of 2cm*2cm*2cm (the porosity of the polyurethane foam is 93%). Get 20mL of the carbon dot solution in step (1), immerse the polyurethane foam block (0.2g) in the carbon d...

Embodiment 2

[0044] (1) Synthesize yellow light carbon dots by hydrothermal method: weigh 2.3g of neutral red with a balance and dissolve in 60mL of ethylene glycol, and stir for 30 minutes. Then it was transferred to a polytetrafluoroethylene-lined stainless steel hydrothermal reactor and reacted at 200°C for 4 hours. After the reaction was finished, it was naturally cooled to room temperature, and the reacted solution and solid were taken out, and centrifuged and washed with a mixed solution of n-hexane and acetone (volume ratio: 95:5). After centrifugation, take the supernatant in a beaker, and this supernatant is the carbon dot solution used later.

[0045] (2) Synthesis of carbon dots / polyurethane composites:

[0046] Take 10g of polyethylene glycol and 5g of 4,4'-dicyclohexylmethane diisocyanate, stir and mix evenly, and react at a constant temperature of 80°C to obtain product A; add 10PEG-2000, 0.7g of simethicone and 0.7g of liquid paraffin, drop 3 Drop dibutyltin dilaurate, con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
porosityaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of preparation of carbon dots and carbon dot composite materials, in particular to a carbon dot / polyurethane composite material and its preparation method and application. After dissolving neutral red in ethylene glycol, stirring and mixing, reacting at 200 ° C for 4 hours, centrifuging and washing with a mixed solution of n-hexane and acetone, and taking the supernatant to prepare a carbon dot solution, and then immersing the polyurethane foam in After standing in the carbon dot solution, take it out, wash and dry to obtain the carbon dot / polyurethane composite material. The carbon dot / polyurethane composite material of the present invention has a simple preparation process, is environmentally friendly, and is cheap and easy to obtain. When used for photocatalytic enrichment of uranium, it can accelerate the transfer of electrons and substances, thereby improving its photocatalytic performance, and is easy to separate after the reaction , for subsequent reuse.

Description

technical field [0001] The invention relates to the technical field of preparation of carbon dots and carbon dot composite materials, in particular to a carbon dot / polyurethane composite material and its preparation method and application. Background technique [0002] Energy is the cornerstone of the development of modern society. With the continuous progress of the economy, the demand for energy, especially clean energy, is becoming more and more urgent. Nuclear power is a clean energy that plays an important role in future energy supply. The reserves of uranium, the main fuel, directly threaten the sustainable development of nuclear power. my country is a country with depleted uranium, and the reserves of uranium resources are small and the grade is poor. In addition, uranium has both radiotoxicity and heavy metal toxicity, which poses a threat to the environment and human health. Therefore, finding unconventional uranium sources, such as seawater uranium extraction, nu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/06B82Y20/00B82Y40/00C02F1/30C22B60/02C22B7/00C02F101/20
CPCB01J31/069B01J31/06B01J35/004B01J35/023B82Y20/00B82Y40/00C02F1/30C22B60/0278C22B7/006C02F2101/006C02F2101/20C02F2305/10Y02P10/20
Inventor 王哲张康杰李斌商海林王祥科
Owner NORTH CHINA ELECTRIC POWER UNIV (BAODING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com