A preparation method and application of cross-linked hydrogel for muscle stem cell culture

A cross-linked hydrogel and stem cell culture technology, which is applied in the field of biological food materials, can solve the problems of poor mechanical properties and poor cell adhesion, achieve complete mechanical properties, improve biocompatibility, and facilitate adhesion of stem cells Effect

Active Publication Date: 2021-12-03
SHANTOU DEBAO INVESTMENT CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This form of hydrogel is biocompatible and more environmentally friendly, however, poor mechanical properties and poor cell adhesion are its major drawbacks
Therefore, how to obtain natural hydrogels with high biocompatibility, high cross-linking strength, and strong cell adhesion remains a challenge.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method and application of cross-linked hydrogel for muscle stem cell culture
  • A preparation method and application of cross-linked hydrogel for muscle stem cell culture
  • A preparation method and application of cross-linked hydrogel for muscle stem cell culture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Embodiment 1: the preparation of chitosan / dextran / alginate / calcium ion double network cross-linked hydrogel

[0049] Add 1 g of sodium alginate (AR; 120 kDa; G / M ratio of 35 / 65) and 99 mL of deionized water to the beaker, and stir while adding until the sodium alginate dissolves to obtain a sodium alginate solution with a concentration of 1 wt%. Then add 0.1 g of calcium carbonate to the sodium alginate solution and stir until the calcium carbonate is uniformly dispersed to form a first gel material similar to mud. Then add 1 g of dextran (AR; 80-100 kDa) and 99 mL of deionized water to the beaker, stir until the dextran dissolves to obtain a 1 wt% dextran solution, add 2 g of chitosan (90.24% deacetylation; 230 kDa) into the dextran solution, and stir until the chitosan is evenly dispersed, forming a second gel mass similar to mud. Mix the two gel materials according to the ratio of the first gel material: the second gel material is 1:1, stir and mix evenly. The slur...

Embodiment 2

[0050] Example 2: Heparin-coated chitosan / dextran / alginate / calcium ion double network cross-linked hydrogel

[0051] Sodium heparin (0.5 g) and deionized water (100 mL) were added to the beaker to obtain a heparin solution (5.0 g / L). Prepared CS / Dex / Alg / Ca 2+ The hydrogel was soaked in PBS for 30 minutes, then soaked in heparin solution for 15 minutes, repeated three times, washed with PBS to remove unadsorbed heparin on the surface, and obtained CS / Dex / Alg / Ca coated with heparin by electrostatic adsorption. 2+ Hydrogels.

Embodiment 3

[0052] Example 3: Collagen coated chitosan / dextran / alginate / calcium ion double network cross-linked hydrogel

[0053] Collagen and deionized water were added to a beaker to obtain a collagen solution (20 wt%). The prepared CS / Dex / Alg / Ca coated with heparin 2+ The hydrogel was soaked in PBS for 30 minutes, then soaked in collagen solution for 15 minutes, repeated three times, washed with PBS to remove the collagen on the surface, through the interaction between collagen and heparin, a gel coated with collagen and heparin was obtained. CS / Dex / Alg / Ca 2+ Hydrogels. Subsequently, the hydrogel was freeze-dried in a vacuum freeze dryer (-80 °C).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method and application of a cross-linked hydrogel used for culturing muscle stem cells, and belongs to the technical field of biological food materials. The present invention combines chitosan, alginate, dextran, Ca 2+ Cross-linking forms a double-network hydrogel with high mechanical strength, and then the hydrogel is coated with heparin and collagen by dipping and coating, so that the hydrogel can sequester growth factors and adhere to cells. At the same time, the extracted primary muscle stem cells were placed on the hydrogel and cultured in growth medium (79% DMEM, 10% FBS, 1% double antibody) for 24 hours. Subsequently, cultured in an incubator replaced with differentiation medium (97% DMEM, 2% horse serum, 1% double antibody) for 7 days. The use of this hydrogel can enhance the absorption of nutrients by muscle stem cells and facilitate their growth. Dual network hydrogels have potential as scaffolds for muscle stem cell growth in stem cell cultured meat.

Description

technical field [0001] The invention relates to a preparation method and application of a cross-linked hydrogel used for culturing muscle stem cells, in particular to a preparation method and application of a novel physical double-network cross-linked hydrogel, which belongs to the technical field of biological food materials. Background technique [0002] Stem cell cultured meat has the potential to reduce the environmental impact of meat products compared with traditional meat production (Environmental Science & Technology, 2015, 49, 11941-11949). Stem cell cultured meat has attracted increasing interest, and a variety of methods for the cultivation of meat from stem cells for food purposes have been proposed (Journal of Integrative Agriculture, 2015, 14, 222-233). However, the lack of scalable cell culture substrates (scaffolds) becomes a major challenge limiting stem cell culture. [0003] Artificial simulated extracellular matrix (ECM) hydrogels are used to reproduce t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/075C08L5/08C08L5/02C08L5/04C08L5/10C08L89/00C08K3/26C12N5/077
CPCC08J3/075C12N5/0659C12N2533/74C12N2533/72C12N2533/70C12N2533/54C08J2305/08C08J2405/04C08J2405/02C08J2405/10C08J2489/00C08K2003/265C12N2537/10C12N2533/18C12N5/0658C08J3/24
Inventor 胡静尹健汪翔
Owner SHANTOU DEBAO INVESTMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com