Easy-to-clean ceramic product and preparation method thereof

A ceramic product and easy-to-clean technology, applied in the field of ceramic products, can solve the problems that the surface is not smooth enough, not easy to clean, easy to scratch, etc., and achieves the effect of high yield, not easy to scratch, and delicate glaze

Active Publication Date: 2020-08-11
德化县德鸿陶瓷有限公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned ceramic products also have the following disadvantages: the surface is not smooth enough, easy to stain, and difficult to clean; low hardness, not wear-resistant, and easy to scratch during use, which further leads to easy staining and difficult cleaning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-to-clean ceramic product and preparation method thereof
  • Easy-to-clean ceramic product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] A preparation method for easy-to-clean ceramic products, comprising the following steps:

[0020] S1. Glaze production: put the above-mentioned nepheline syenite, dolomite, flint and spodumene into a pulverizer and then pass through a 100-mesh sieve to obtain a powder, and mix the powder with the above-mentioned magnesite, talc, barium carbonate Add Hongdie strontium carbonate into a ball mill for dry grinding for 8 hours to obtain the basic glaze, add 1.3 times the water of the basic glaze and Hebei Lingshou tourmaline whose weight is 8% of the basic glaze, carry out wet grinding for 10 hours, and then pass through a 200-mesh sieve , get glaze;

[0021] S2. Biscuit production: put the above clay, bentonite and quartz into a pulverizer and pulverize them, and then filter them with a 200-mesh sieve to obtain the basic powder. Put the basic powder into a ball mill for dry grinding for 8 hours, and then add 1.1 times of raw material water for wet grinding. After grinding ...

Embodiment 1

[0025] An easy-to-clean ceramic product, comprising a green body and a glaze layer applied on the surface of the green body, the green body includes the following raw materials in parts by weight: 30 parts of pottery clay, 8 parts of bentonite, and 10 parts of quartz; the glaze layer includes the following weight parts Parts of raw materials: 40 parts of nepheline syenite, 1 part of magnesite, 10 parts of flint, 4 parts of talc, 4 parts of barium carbonate, 10 parts of dolomite, 1 part of spodumene, and 1 part of strontium carbonate.

[0026] A preparation method for easy-to-clean ceramic products, comprising the following steps:

[0027] S1. Glaze production: Put the above-mentioned nepheline syenite, dolomite, flint and spodumene into a pulverizer and pulverize them, then pass through a 100-mesh sieve to obtain a powder, and put the powder into a high-temperature furnace for a heating rate of 8°C / min, 700°C heat preservation for 2.5h, anaerobic calcination at a cooling rate...

Embodiment 2

[0032] An easy-to-clean ceramic product, comprising a green body and a glaze layer applied on the surface of the green body, the green body includes the following raw materials in parts by weight: 40 parts of pottery clay, 13 parts of bentonite, and 17 parts of quartz; the glaze layer includes the following weight parts Parts of raw materials: 50 parts of nepheline syenite, 5 parts of magnesite, 18 parts of flint, 8 parts of talc, 10 parts of barium carbonate, 18 parts of dolomite, 5 parts of spodumene, and 5 parts of strontium carbonate.

[0033] A preparation method for easy-to-clean ceramic products, comprising the following steps:

[0034] S1. Glaze production: Put the above-mentioned nepheline syenite, dolomite, flint and spodumene into a pulverizer and pulverize them, then pass through a 100-mesh sieve to obtain a powder, and put the powder into a high-temperature furnace for a heating rate of 8°C / min, 900°C heat preservation for 1.5h, anaerobic calcination at a cooling...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an easy-to-clean ceramic product which comprises a green body and a glaze layer applied to the surface of the green body. The green body is prepared from the following raw materials in parts by weight: 30-40 parts of argil, 8-13 parts of bentonite and 10-17 parts of quartz. The glaze is prepared from the following raw materials in parts by weight: 40-50 parts of nepheline syenite, 1-5 parts of magnesia, 10-18 parts of flint, 4-8 parts of talc, 4-10 parts of barium carbonate, 10-18 parts of dolomite, 1-5 parts of spodumene and 1-5 parts of red butterfly strontium carbonate. Part of components of the glaze are subjected to anaerobic calcination, then the glaze is prepared through a wet grinding method, and the obtained glaze is fine and smooth and good in stability. The ceramic product is prepared by combining slow temperature control and high-temperature calcination, and the obtained ceramic product has the characteristics of stable performance and high yield.

Description

technical field [0001] The invention belongs to the technical field of ceramic products, in particular to an easy-to-clean ceramic product and a preparation method thereof. Background technique [0002] Ceramic products widely exist in people's daily life, such as ceramic tableware, ceramic tea set, ceramic wine set, etc. The above-mentioned ceramic products also have the following disadvantages: the surface is not smooth enough, easily stained, and difficult to clean; low hardness, not wear-resistant, and easy to scratch during use, which further leads to easy staining and difficult cleaning. [0003] Therefore, it is necessary to improve existing ceramic products, Contents of the invention [0004] The object of the present invention is to overcome the deficiencies of the prior art, and provide an easy-to-clean ceramic product and a preparation method thereof. [0005] The solution of the present application to solve its technical problems is: an easy-to-clean ceramic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/16C04B33/24C04B33/34C03C8/00C04B41/86
CPCC04B33/16C04B33/24C04B33/34C03C8/00C04B41/86C04B41/009C04B41/5022C04B2235/6562C04B2235/96C04B2235/9638C04B41/4539
Inventor 方国栋
Owner 德化县德鸿陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com