Porous pdfe intermetallic compound modified by pt or au and its preparation method and application

A technology of intermetallic compounds and porous structures, applied in the field of electrochemistry, can solve the problems of poor cycle stability and low catalytic activity, and achieve high cathode oxygen reduction electrocatalytic activity and stability, good electrochemical stability, and equipment simple effect

Active Publication Date: 2021-08-03
HUAZHONG UNIV OF SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention solves the technical problems of low catalytic activity and poor cycle stability in fuel cells in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous pdfe intermetallic compound modified by pt or au and its preparation method and application
  • Porous pdfe intermetallic compound modified by pt or au and its preparation method and application
  • Porous pdfe intermetallic compound modified by pt or au and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A preparation method of a Pt-modified porous PdFe intermetallic compound electrocatalyst, comprising the following steps:

[0038] (1) Preparation of PdFe intermetallic compound: Weigh 70 mg of carbon carrier and add it to 4 mL of acetic acid solution. After fully ultrasonically dispersed, add 42.65 mg of palladium acetate and 33.06 mg of ferrous acetate. dry solvent, after drying, the precursor sample was obtained, wherein the mass fraction of Pd in ​​the precursor (including carbon support) was 20%; the obtained black powder was heated to 700°C in an argon flow for thermal decomposition treatment, and after 120min Cool to room temperature, that is.

[0039] (2) Porous PdFe intermetallic compound: Add a certain amount of the black powder prepared above into a mixed solvent of ethanol and hydrochloric acid aqueous solution (1:1, volume ratio), soak for 2 hours, and make the Fe atoms on the surface of the PdFe intermetallic compound generate Etching, enriching Pd at the...

Embodiment 2

[0042] A method for preparing a Pt-modified porous PdFe intermetallic compound electrocatalyst, comprising the following steps:

[0043] (1) Weigh 70mg carbon carrier, 42.65mg Pd(Ac) 2 and 33.06mg Fe(Ac) 2 Sequentially added to 4mL acetic acid solution, fully ultrasonicated and homogenized, the solvent was evaporated, and the precursor sample was obtained after drying, wherein the mass fraction of Pd in ​​the precursor (including carbon support) was 20%. The obtained black powder was programmed to heat up to 650° C. for thermal decomposition in a nitrogen gas stream, kept for 120 min and then cooled to room temperature to obtain a PdFe intermetallic compound.

[0044] (2) Add a certain amount of black powder prepared in step (1) into a mixed solvent of ethanol and 0.5mol / L hydrochloric acid aqueous solution (1:1, volume ratio), soak for 2 hours, and make the Fe atoms on the surface of the PdFe intermetallic compound Etching occurs, and Pd is enriched at the same time; the Pd...

Embodiment 3

[0047] A method for preparing a Pt-modified porous PdFe intermetallic compound electrocatalyst, comprising the following steps:

[0048] (1) Weigh 85mg Pd(Ac) 2 and 66mg Fe(Ac) 2 Add it into 8mL acetic acid solution, add 140mg of carbon black after ultrasonic homogenization, evaporate the solvent after ultrasonic homogenization, and obtain a precursor sample after drying, wherein the mass fraction of Pd in ​​the precursor (including carbon support) is 20%. The obtained black powder was programmed to heat up to 650° C. for thermal decomposition in a nitrogen gas stream, kept for 120 min and then cooled to room temperature to obtain a PdFe intermetallic compound.

[0049] (2) Porous PdFe intermetallic compound: Add a certain amount of black powder prepared in step (1) into a mixed solvent of 0.5M hydrochloric acid aqueous solution and ethylene glycol, soak for 1 hour, and make the Fe atoms on the surface of the PdFe intermetallic compound be engraved. At the same time, Pd is e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a Pt or Au modified porous PdFe intermetallic compound, a preparation method and an application thereof, and belongs to the technical field of electrochemistry. The intermetallic compound is a nano particle, the inner core of the nano particle is an ordered PdFe intermetallic compound, the surface is a porous structure with evenly distributed Pd, and the surface of the porous structure is decorated with Pt or Au. The preparation method is to use palladium acetate and iron salt as the metal source, and load it on the carbon carrier, and then thermally decompose the acetate in a protective atmosphere to obtain a supported PdFe intermetallic compound. After etching away the Fe on the surface, use Surface modification technology prepared Pt or Au modified PdFe intermetallic compounds with porous surface and ordered inner core. The Pt or Au modified porous PdFe intermetallic compound prepared by the invention shows high activity and stability as a fuel cell cathode oxygen reduction reaction catalyst and an anode hydrogen oxidation reaction catalyst.

Description

technical field [0001] The invention belongs to the technical field of electrochemistry, and relates to a Pt or Au-modified porous PdFe intermetallic compound and a preparation method and application thereof, in particular to an electrocatalyst applied to fuel cell cathode oxygen reduction and anode hydrogen oxidation reactions. Background technique [0002] With the determination of the ban on the sale of fuel vehicles in various countries, the proton exchange membrane fuel cell (proton electrolyte membrane fuel cell, PEMFC) represented by hydrogen-oxygen fuel cell has entered a period of rapid development. In addition to the general advantages of fuel cells, such as high power generation efficiency and less environmental pollution, hydrogen-oxygen fuel cell devices also have the advantages of rapid start-up at room temperature, less electrolyte loss, high specific power and long life. However, the key materials of PEMFC still need further breakthroughs, and the cost needs ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/92H01M8/1007
CPCH01M4/921H01M4/926H01M8/1007Y02E60/50
Inventor 王得丽龚明星申涛邓智平杨弘毅
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com