High-toughness scratch-resistant ABS/PBT alloy and preparation method thereof

A scratch-resistant, high-toughness technology, applied in the field of scratch-resistant ABS/PBT alloy and its preparation, high toughness, can solve the problems of ABS and PBT difficult to dissolve, low impact strength, etc., to improve impact toughness, excellent durability Scratchability, high toughness effect

Inactive Publication Date: 2019-01-04
ORINKO NEW MATERIAL CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the existing technology, in order to solve the problems of difficult miscibility and low impact strength in the blending process of ABS and PBT

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness scratch-resistant ABS/PBT alloy and preparation method thereof
  • High-toughness scratch-resistant ABS/PBT alloy and preparation method thereof
  • High-toughness scratch-resistant ABS/PBT alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The high-toughness, scratch-resistant ABS / PBT alloy material in the present embodiment is made up of following raw material according to weight part:

[0028]

[0029]

[0030] Concrete preparation method comprises the following steps:

[0031] (1) Dry the ABS resin in an oven at 80°C for 4 hours, the PBT resin in an oven at 120°C for 4-6 hours, and the TPU elastomer in an oven at 80°C for 2 hours, and control the water content of the three to Below 0.1%, for use.

[0032] (2) 75 parts of ABS resin, 20 parts of PBT resin, 2 parts of styrene-acrylonitrile-GMA, 3 parts of polyester polyurethane elastomer, 0.5 part of silicon dioxide, 0.5 part of erucamide, antioxidant 1010 0.1 1 part, antioxidant 168 0.1 part ethylene bis stearamide 1 part mixed in a high-speed mixer for 10 minutes, put into the main feed of the co-rotating twin-screw extruder, melt extruded and granulated to obtain ABS / PBT Alloy materials; the extrusion temperature of the extruder is 220-240°C, t...

Embodiment 2

[0034] The high-toughness, scratch-resistant ABS / PBT alloy material in the present embodiment is made up of following raw material according to weight part:

[0035]

[0036] Concrete preparation method comprises the following steps:

[0037] (1) Dry the ABS resin in an oven at 85°C for 5 hours, the PBT resin in an oven at 130°C for 5 hours, and the TPU elastomer in an oven at 90°C for 3 hours, and control the water content of the three to 0.1% Below, to be used.

[0038] (2) 62 parts of ABS resin, 30 parts of PBT resin, 3 parts of styrene-acrylonitrile-GMA, 5 parts of polyether polyurethane elastomer, 2 parts of ultrafine barium sulfate, 0.3 parts of erucamide, silicone masterbatch 1 part, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 168, and 0.5 part of ethylene bis stearamide were mixed in a high-speed mixer for 10 minutes, put into the main feed of the co-rotating twin-screw extruder, and melted and extruded , granulation, and obtain the ABS / PBT alloy materia...

Embodiment 3

[0040] The high-toughness, scratch-resistant ABS / PBT alloy material in the present embodiment is made up of following raw material according to weight part:

[0041]

[0042] Concrete preparation method comprises the following steps:

[0043] (1) Dry the ABS resin in an oven at 90°C for 6 hours, the PBT resin in an oven at 140°C for 6 hours, and the TPU elastomer in an oven at 100°C for 4 hours, and control the water content of the three to 0.1% Below, to be used.

[0044] (2) 37 parts of ABS resin, 50 parts of PBT resin, 5 parts of styrene-acrylonitrile-GMA, 8 parts of polyether polyurethane elastomer, 1 part of silicon dioxide, 2 parts of silicone masterbatch, antioxidant DLTP 0.15 parts, 0.15 parts of antioxidant 168, 0.75 parts of pentaerythritol stearate, 0.5 parts of ultraviolet light absorber, 0.5 parts of light stabilizer, 1 part of colorant were mixed in a high-speed mixer for 10 minutes, and put into a co-rotating twin-screw extruder In the main feed, ABS / PBT al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-toughness scratch-resistant ABS / PBT alloy material and a preparation method thereof. The material is prepared from 37-75 parts of ABS resin, 20-50 parts of PBT resin, 2-5 parts of compatilizer, 3-8 parts of thermoplastic polyurethane elastomer, 0.5-2 parts of inorganic nucleating agent, 0.5-2 parts of scratch resistant agent, 0.2-0.4 part of antioxidant, 0.5-1 part of lubricant and 0-2 parts of other auxiliaries. Accordingly, macromolecule containing an epoxy functional group serves as the compatilizer, the thermoplastic polyurethane elastomer serves as flexibilizer, the compatibility of ABS and PBT is improved, the toughness and scratch-resistant property of the alloy material are improved, a melt extrusion method is adopted, the prepared material has the high toughness and the excellent scratch-resistant property, the material is simple in technology, convenience is brought to operate, the yield is high, and the material is suitable for industrial production and has the wide market prospect in the fields of vehicle interior and exterior trimming, household appliances, electrical and electronic products and the like.

Description

technical field [0001] The invention relates to the technical field of polymer composite materials, in particular to a high-toughness, scratch-resistant ABS / PBT alloy and a preparation method thereof. Background technique [0002] Acrylonitrile-butadiene-styrene (ABS) has the characteristics of excellent mechanical properties, high gloss, cold resistance, impact resistance, oil resistance, high dimensional stability, small molding shrinkage, excellent electrical properties, electroplating, and easy molding. It is widely used in automobiles, home appliances, electronic toys and other fields, but there are disadvantages such as poor weather resistance, low heat distortion temperature, especially poor resistance to organic solvents, which limit the expansion of its application range. [0003] Polybutylene terephthalate (PBT) is a crystalline polyester, which has the advantages of good resistance to organic solvents, high rigidity, chemical resistance, self-lubricating propertie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L67/02C08L25/14C08L75/06C08L83/04C08L75/08C08K13/02C08K3/36C08K5/20C08K3/30C08K5/103
CPCC08K2003/3045C08K2201/014C08L55/02C08L67/02C08L2205/035C08L2205/05C08L2205/08C08L2207/04C08L25/14C08L75/06C08K13/02C08K3/36C08K5/20C08L75/08C08L83/04C08K3/30C08K5/103
Inventor 石阳阳陈晓燕周海闫溥李荣群李春忠张玲王庚超
Owner ORINKO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More