Technology for preparing baking-free bricks with iron tailings, secondary aluminum ash and acid leaching magnesium residues

A technology of aluminum ash slag and unburned bricks, which is applied in the manufacture of rayon, single-component polyolefin rayon, and fiber chemical characteristics, can solve the problems of unfavorable fiber concrete collective interface, poor concrete dispersion, and difficult mixing. Achieve good mechanical properties and hydrophilic properties, reduce the amount of cement, and good alkali resistance

Inactive Publication Date: 2019-01-04
枞阳县天筑新型建筑材料有限公司
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] As an engineering fiber with excellent performance, polypropylene fiber has its main advantages: good mechanical properties, chemical corrosion resistance, and no insects, but it also has some fatal weaknesses: it does not absorb water, is easy to form a ball, and is difficult to mix with cement. Poor dispersion in concrete is not conducive to forming a good collective interface of fiber concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of technology that utilizes iron tailings-secondary aluminum ash slag-acid leaching manganese slag to prepare burn-free brick is characterized in that, comprises the following steps:

[0024] (1) Melt blending modification of polypropylene fiber:

[0025] Add 0.006 parts of stearic acid to 0.3 parts of heavy calcium carbonate, perform wet activation at 85-95°C for 45 minutes, then dry and grind; blend it with 1 part of polypropylene fiber and 0.1 part of polyethylene glycol , use a 180-200°C twin-screw extruder to blend and granulate, dry the blended pellets at 104-106°C, and use a melt spinning machine to produce filaments to obtain modified polypropylene fibers;

[0026] (2) Pretreatment of raw material secondary aluminum ash:

[0027] Put 155 parts of secondary aluminum ash into an electric blast drying oven at 120-125°C to dry for 3 hours, cool naturally, take it out, and grind it with a ball mill to obtain secondary aluminum ash with a particle size of 200 ...

Embodiment 2

[0035] A kind of technology that utilizes iron tailings-secondary aluminum ash slag-acid leaching manganese slag to prepare burn-free brick is characterized in that, comprises the following steps:

[0036] (1) Melt blending modification of polypropylene fiber:

[0037] Add 0.012 parts of stearic acid to 0.6 parts of heavy calcium carbonate, perform wet activation at 85-95°C for 55 minutes, then dry and grind; blend it with 2 parts of polypropylene fiber and 0.2 parts of polyethylene glycol , use a 180-200°C twin-screw extruder to blend and granulate, dry the blended pellets at 104-106°C, and use a melt spinning machine to produce filaments to obtain modified polypropylene fibers;

[0038] (2) Pretreatment of raw material secondary aluminum ash:

[0039] Put 165 parts of secondary aluminum ash into an electric blast drying oven at 120-125°C to dry for 4 hours, cool naturally, take it out, and grind it with a ball mill to obtain secondary aluminum ash with a particle size of 20...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a technology for preparing baking-free bricks with iron tailing-secondary aluminum ash-acid leaching magnesium residues. The iron tailings, aggregate river sand and gel materials are mixed with the pretreatment secondary aluminum ash and quick lime pretreatment acid leaching magnesium residues, uniform stirring is conducted, mixing water is added for pre-activation, then anadditive is added, stirring is conducted in advance, wheel-grinding mixing is performed, final stirring is conducted, after ageing, the mixture is injected into a forming mold, forming pressure is set, by the adoption of staged pressurizing, the mixture is pressed to be formed under constant pressure, and after steam curing maintaining is conducted in an autoclave, the baking-free bricks are obtained through natural maintaining. Quick lime is adopted for pretreating acid leaching magnesium residues and added into the acid leaching magnesium residues to form an alkaline environment, under alkaline conditions, part of heavy metal ions precipitate, meanwhile, a good adsorption effect on ammonium radical ions is realized, pollution of ammonium radical degradation to air is prevented, and a good excitation effect on acid leaching spiegel residues is realized; the active performance of the magnesium residues is excited, and after gel substances and aggregate are added for uniform mixing andstirring, the baking-free bricks are prepared through the method of pressing forming.

Description

technical field [0001] The invention belongs to the technical field of non-burning bricks, and in particular relates to a process for preparing non-burning bricks by using iron tailings-secondary aluminum ash slag-acid leaching manganese slag. Background technique [0002] my country's iron tailings discharge and accumulation are huge. A large amount of iron tailings piled up not only caused serious damage to the environment, but also took up a lot of cultivated land and brought huge safety hazards to the people around the tailings pond. The use of iron tailings to prepare unburned bricks is not only conducive to the sustainable development of mining enterprises, but also can well implement the purpose of building a healthy, environmentally friendly, and resource-saving society in my country. [0003] Lead ash is the waste residue of lead smelting and secondary lead recovery. In industry, lead ash is mainly used to purify elemental lead, recover salt, and be used as deoxidi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/02D01F6/46D01F1/10
CPCC04B28/02C04B2201/50D01F1/10D01F6/46C04B22/064C04B18/08C04B22/143C04B18/12C04B14/06C04B18/144C04B18/0481C04B22/124C04B22/147C04B24/18C04B2103/302C04B24/122C04B16/0633
Inventor 方明珠
Owner 枞阳县天筑新型建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products