Preparation method of extinction powder special for elastic paint

A technology of matting powder and elastic paint, applied in chemical instruments and methods, silica, inorganic chemistry, etc., can solve problems such as difficult to improve, poor transparency, small pore volume, etc., to improve pore structure and increase collision frequency , The effect of increasing the pore volume

Inactive Publication Date: 2018-09-21
山西天一纳米科技股份有限公司
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Silica powder prepared by precipitation method has high oil absorption value, but has disadvantages such as poor structure, small pore volume, poor transparency, etc., especially the specific surface area usually only reaches 170-200m 2 / g, hard to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of extinction powder special for elastic paint
  • Preparation method of extinction powder special for elastic paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In a 5000L stirred reactor, add 1000L water and 480L sodium silicate solution and stir evenly, raise the temperature to 45°C, and add 30% sulfuric acid dropwise to the solution at a speed of 4L / min under stirring until the pH value is 6.0-7.0, stir for 30 minutes, add 20% ammonia water to adjust the pH value to 8-9, age for 50 minutes, continue to heat up to 90°C, at this temperature, add sodium silicate with a flow rate of 0.55L / min into the reaction kettle at the same time 820L and sulfuric acid, and keep the pH value of the solution at 8-9, continue to age for 50 minutes, continue to add acid until the pH value is 4-5 after the reaction, filter and wash the reaction slurry to obtain a silica filter cake, and re-beaten To form a suspension solution, add polydimethylsiloxane and acrylic acid block polymer to it, then dry, pulverize and classify.

Embodiment 2

[0023] In a 5000L stirred reactor, add 1000L water and 500L sodium silicate solution and stir evenly, raise the temperature to 40°C, and add 30% sulfuric acid dropwise to the solution at a speed of 5L / min under stirring until the pH value is 6.0-7.0, stir for 30 minutes, add 20% ammonia water to adjust the pH value to 8-9, age for 50 minutes, continue to heat up to 85°C, at this temperature, add sodium silicate with a flow rate of 0.55L / min into the reaction kettle at the same time 750L and sulfuric acid, and keep the pH value of the solution at 8-9, continue to age for 50min, continue to add acid until the pH value is 4-5 after the reaction, filter and wash the reaction slurry to obtain a silica filter cake, and re-beaten To form a suspension solution, add polydimethylsiloxane and acrylic acid block polymer to it, then dry, pulverize and classify.

Embodiment 3

[0025] In a 5000L stirred reactor, add 1000L water and 400L sodium silicate solution and stir evenly, raise the temperature to 45°C, add 25% sulfuric acid dropwise to the solution at a speed of 4L / min under stirring until the pH value is 6.0-7.0, stir for 30 minutes, add 20% ammonia water to adjust the pH value to 8-9, age for 50 minutes, continue to heat up to 100°C, at this temperature, add sodium silicate with a flow rate of 0.55L / min into the reaction kettle at the same time 1000L and sulfuric acid, and keep the pH value of the solution at 8-9, continue to age for 50 minutes, continue to add acid until the pH value is 4-5 after the reaction, filter and wash the reaction slurry to obtain a silica filter cake, and re-beaten To form a suspension solution, add polydimethylsiloxane and acrylic acid block polymer to it, then dry, pulverize and classify.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of extinction powder special for elastic paint. In a reaction kettle, sodium silicate and water are added, the temperature is increased to 45 DEG C, in the stirring state, sulfuric acid with the concentration being 30% is added, the PH value is regulated to 6-6.5, ammonium hydroxide is added to regulate the PH value to 8.5-9.0, aging is performed for 50 min, then, the temperature is increased to 90 DEG C, meanwhile, sodium silicate and sulfuric acid of the certain concentration are added, aging is performed for 50 min, acid is added till the PH value is 4-5, and filtering, washing, drying and smashing and classification are performed to obtain finished extinction powder. The extinction powder has the advantages of being high in oil absorption value, good in dispersibility, fine in touch, high in transparency and the like, and is reasonable in technology and high in production efficiency.

Description

technical field [0001] The invention belongs to the preparation technology of powder materials, in particular to a preparation method of silica matting powder for elastic paint matting. Background technique [0002] Silica micropowder is actually an aggregate of very small silica grains, which is an amorphous white powder. Silica matting powder has the advantages of easy dispersion, good matting performance, little interference with the transparency of the coating film, little effect on the mechanical and chemical properties of the coating film, good suspension in liquid coatings, and high chemical inertness. widely used in. [0003] The preparation of silica matting powder mainly includes three categories: precipitation method, gel method and gas phase method. Both the gas phase method and the gel method have higher production costs. And the specific surface area produced by different production processes is different. The gel method silica has the characteristics of hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B33/12C09C1/30C09C3/10C09C3/12
CPCC01B33/128C01P2004/61C01P2006/12C01P2006/14C09C1/3072C09C1/3081C09C1/309
Inventor 张原僖张伟梁建强刘娟梅赵燕平赵建卿
Owner 山西天一纳米科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com