Wear-resistant flame-retardant conveying belt

A technology for conveyor belts and mixtures, applied in the field of wear-resistant and flame-retardant conveyor belts, can solve the problems of poor flame-retardant and wear-resistant performance of conveyor belts, and achieve the effects of not easy delamination, low energy consumption, and improved overall performance

Inactive Publication Date: 2018-01-26
青岛环球输送带有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the technical problem of poor flame-retardant and wear-resistant properties of conveyor belts in the prior art, the purpose of the pre...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant flame-retardant conveying belt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Wear-resistant and flame-retardant conveyor belt, the components of the raw materials are composed as follows in parts by weight:

[0023] 22 parts of EPDM rubber, 15 parts of neoprene rubber, 10 parts of nitrile rubber, 8 parts of chlorinated polyethylene, 4 parts of carbon black, 7 parts of sulfur, triisopropylphenyl phosphate, polyisocyanate and dichloro Propyl phosphate is composed of 3 parts of phosphorus-containing flame retardant in a weight ratio of 2:1:1, 0.6 parts of dibenzothiazole disulfide, ammonium polyphosphate, calcium carbonate and pine tar in a weight ratio of 2:2:5 1.2 parts of compound stabilizer, 0.8-1 part of N-isopropyl-N'-phenyl-p-phenylenediamine, 2 parts of anti-aging agent composed of 4010NA and RD according to the weight ratio of 2:3, lead stearate 0.5 parts of dispersant composed of chlorinated paraffin at a weight ratio of 1:3, 6 parts of adhesive composed of reclaimed rubber RR, cyclohexanone and toluene at a weight ratio of 7:2:2, 2 parts...

Embodiment 2

[0025] Wear-resistant and flame-retardant conveyor belt, the components of the raw materials are composed as follows in parts by weight:

[0026] 23 parts of EPDM rubber, 16 parts of neoprene rubber, 12 parts of nitrile rubber, 10 parts of chlorinated polyethylene, 5 parts of carbon black, 8 parts of sulfur, triisopropylphenyl phosphate, polyisocyanate and dichloro Propyl phosphate is composed of 4 parts of phosphorus-containing flame retardant in a weight ratio of 2:1:1, 0.7 parts of dibenzothiazole disulfide, ammonium polyphosphate, calcium carbonate and pine tar in a weight ratio of 2:2:5 1.4 parts of composite stabilizer, 0.8-1 part of N-isopropyl-N'-phenyl-p-phenylenediamine, 2.5 parts of anti-aging agent composed of 2:3 weight ratio of anti-aging agent 4010NA and anti-aging agent RD, lead stearate 0.6 parts of dispersant composed of chlorinated paraffin in a weight ratio of 1:3, 8 parts of adhesive composed of reclaimed rubber RR, cyclohexanone and toluene in a weight ra...

Embodiment 3

[0028] Wear-resistant and flame-retardant conveyor belt, the components of the raw materials are composed as follows in parts by weight:

[0029] 25 parts of EPDM rubber, 18 parts of neoprene rubber, 15 parts of nitrile rubber, 12 parts of chlorinated polyethylene, 6 parts of carbon black, 10 parts of sulfur, triisopropylphenyl phosphate, polyisocyanate and dichloro Propyl phosphate is composed of 5 parts of phosphorus-containing flame retardant in a weight ratio of 2:1:1, 0.8 parts of dibenzothiazole disulfide, ammonium polyphosphate, calcium carbonate and pine tar in a weight ratio of 2:2:5 1.5 parts of composite stabilizer, 1 part of N-isopropyl-N'-phenyl-p-phenylenediamine, 3 parts of anti-aging agent composed of 2:3 weight ratio of anti-aging agent 4010NA and anti-aging agent RD, lead stearate and chlorine 0.7 parts of dispersant composed of paraffin wax in a weight ratio of 1:3, 9 parts of adhesive composed of reclaimed rubber RR, cyclohexanone and toluene in a weight ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a wear-resistant flame-retardant conveying belt, wherein the raw materials comprise, by weight, 22-25 parts of ethylene propylene diene monomer, 15-18 parts of chloroprene rubber, 10-15 parts of nitrile butadiene rubber, 8-12 parts of chlorinated polyethylene, 4-6 parts of carbon black, 7-10 parts of sulfur, 3-5 parts of a phosphorus-containing flame retardant agent, 0.6-0.8 part of dibenzothiazole disulfide, 1.2-1.5 parts of a composite stabilizer, 0.8-1 part of n-isopropyl-n'-phenyl p-phenylenediamine, 2-3 parts of an anti-aging agent, 0.5-0.7 part of a dispersant, 6-9 parts of an adhesive, 2-4 parts of a plasticizer, 6-8 parts of asbestos fiber, 8-10 parts of dioctyl phthalate, 16-18 parts of a reinforcing filler, 3-5 parts of a sulfamide accelerator, and0.5-0.8 part of stearic acid. According to the present invention, the wear-resistant flame retardant conveying belt has advantages of high conveying efficiency and good surface elasticity; the tensile strength of the prepared stretching-resistant and wear-resistant flame-retardant conveying belt covering glue is increased by 13.6% and the wear resistance is improved by 39% compared to the existing products; and the wear-resistant flame retardant conveying belt has advantages of good fire resistance, strength improving, high elongation, and long service life.

Description

technical field [0001] The invention belongs to the technical field of conveyor belts, in particular to wear-resistant and flame-resistant conveyor belts. Background technique [0002] The conveyor belt is suitable for material transportation in coal, mining, port, electric power, metallurgy, building materials and other industries. It has high tensile strength, long service life, small elongation in use, and good flex resistance. Capacity and high speed material conveying. High temperature resistant conveyor belt, also known as heat resistant conveyor belt, is a special heavy conveyor belt, mainly used for conveying high temperature materials in steel, cement, coke and other industries. The high-temperature-resistant conveyor belt with metal material as the skeleton layer has better burning resistance and is suitable for use at higher temperatures, such as 300°C. Therefore, the high-temperature-resistant conveyor belt with metal material as the skeleton layer is also calle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L11/00C08L9/02C08L23/28C08K13/04C08K3/04C08K3/06C08K5/523C08K5/29C08K5/521C08K5/47C08K3/32C08K3/26C08K5/18C08K7/12C08K5/12C08K5/09C08K3/22C08K5/435
Inventor 李坤辉王志强徐刚东
Owner 青岛环球输送带有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap