Paint for forming hydrophilic coating on surface of catheter, and preparation and application methods thereof

A hydrophilic coating and primer technology, applied in the field of medical devices, can solve the problems of toxicity of isocyanate compounds, lack of adhesion of catheters, insufficient wear resistance of coatings, etc., and achieve excellent wear resistance, complement performance and function. Insufficient, low curing temperature effect

Active Publication Date: 2016-10-05
BEIJING DEMAX MEDICAL TECH
View PDF35 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this system, the substrate is not connected with other components by chemical reaction, so the coating firmness is still insufficient
In addition, isocyanate compounds are toxic and pose a safety hazard to health
[0016] It can be seen that, compared with the non-reactive hydrophilic polymer, the reactive hydrophilic polymer has better coating firmness, but the other components matched with it in the coating are not closely connected to each other. And the lack of sufficient adhesion to the catheter, the coating still has the problem of insufficient wear resistance, so it is necessary to construct a new coating system to achieve the purpose of both hydrophilic lubrication and wear resistance of the interventional catheter, and it is still necessary to provide new technologies to Get Higher Performance Catheter Coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paint for forming hydrophilic coating on surface of catheter, and preparation and application methods thereof
  • Paint for forming hydrophilic coating on surface of catheter, and preparation and application methods thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Preparation of side carboxyl group-containing polyurethane (CPU): use solvent method to synthesize side carboxyl group-containing polyurethane, add polyether or polyester diol and diisocyanate into the reactor, heat up to 80°C, stir for 1 hour to obtain prepolymer, Add 2,2-dimethylol propionic acid and 1,4-butanediol, react for 2 hours, add N,N-dimethylformamide, continue the reaction for 1 hour, add dibutyltin dilaurate, and then Reacted for 8 hours, down to room temperature, the solution in the reactor was poured into a container with deionized water, a white precipitate was precipitated, collected the precipitate and washed 3 times with deionized water, placed in a vacuum drying oven, at 90 After vacuum drying at ℃ for 48 hours, a transparent block product was obtained, which was granulated to obtain a side carboxyl group-containing polyurethane masterbatch.

[0042] Wherein, described polyether or polyester diol is selected from polyoxypropylene diol (PPG), polytetr...

Embodiment 2

[0049] Water-based polyurethane, trimethylolpropane-tris[3-(2-methylaziridinyl)]propionate, and deionized water were added to the container, and stirred at room temperature for 30 minutes to obtain a primer, in which three The quality of methylolpropane-tris[3-(2-methylaziridinyl)]propionate is 1% of the waterborne polyurethane quality, and the quality of deionized water is 80% of the total quality of the primer. Add side carboxyl group-containing polyurethane CPU-1, polymethyl vinyl ether-maleic anhydride, polyethylene glycol monomethyl ether, and N,N-dimethylformamide into the container, and stir at room temperature for 30 minutes to obtain Top coat, wherein the mass ratio of CPU-1 to polymethyl vinyl ether-maleic anhydride is 1:0.1, and the quality of polyethylene glycol monomethyl ether is 1% of the mass of polymethyl vinyl ether-maleic anhydride , The quality of N,N-dimethylformamide is 80% of the total mass of the top coat. Polymethyl vinyl ether-maleic anhydride is a p...

Embodiment 3

[0054] Water-based polyurethane, trimethylolpropane-tris(3-aziridinyl)propionate, and deionized water were added to the container, and stirred at room temperature for 30 minutes to obtain a primer, wherein trimethylolpropane-tris(3-aziridinyl)propionate The quality of (3-aziridinyl) propionate is 2% of the waterborne polyurethane quality, and the quality of deionized water is 83% of the total quality of the primer. Add side carboxyl group-containing polyurethane CPU-2, polymethyl vinyl ether-maleic anhydride, polyethylene glycol monomethyl ether, and N,N-dimethylacetamide into the container, and stir at room temperature for 30 minutes to obtain Top coat, wherein the mass ratio of CPU-2 to polymethyl vinyl ether-maleic anhydride is 1:0.5, and the quality of polyethylene glycol monomethyl ether is 3% of the mass of polymethyl vinyl ether-maleic anhydride , the quality of N,N-dimethylacetamide is 83% of the total mass of the top coat. Polymethyl vinyl ether-maleic anhydride is a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a paint for forming a hydrophilic coating on the surface of a catheter, and preparation and application methods thereof. The paint comprises a prime paint and a top paint; the prime paint comprises aqueous polyurethane, a multi-functionality aziridine derivative and deionized water; and the top paint comprises side carboxyl polyurethane, polymethyl vinyl ether-maleic anhydride and an organic solvent. During curing, all the components form a crosslinking structure; the bottom and the top of the coating are tightly bonded through a covalent bond, and the coating is firmly adhered on the surface of the catheter; and the coating has excellent hydrophilic lubricity and wear resistance, and is applicable to hydrophilic lubrication treatment of apparatuses like an intervention catheter for TCM treatment in the technical field of endovascular intervention diagnosis and treatment technology.

Description

technical field [0001] The invention relates to the field of medical devices, in particular to a coating for forming a hydrophilic coating on the surface of a catheter and a preparation and application method thereof. Background technique [0002] Intravascular interventional diagnosis and treatment technology is widely used in clinical angiography, angioplasty, removal of intravascular thrombus or foreign body, etc. Compared with traditional medical technology, it is not only convenient to operate, but also reduces the pain of patients due to the low trauma of interventional treatment , the risk of treatment is small, and the cost of treatment is relatively low, so this technology has been widely promoted and used in the medical field. Intravascular interventional diagnosis and treatment technology is to use interventional catheters to reach distant diseased parts in the body through the vascular lumen, such as coronary arteries and other vascular parts, and then inject dia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D175/08C09D175/06C08G18/10C08G18/32C08G18/34B05D5/04B05D7/24A61L29/08
Inventor 王兴元戴华英
Owner BEIJING DEMAX MEDICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com