Phosphogypsum-based metal-like decoration material and preparation method thereof

A decorative material, phosphogypsum technology, applied in the field of phosphogypsum-based imitation metal decorative materials and its preparation, can solve the problems such as the technical scheme of imitation metal decorative materials that have not been seen, and achieve sustainable development, high compressive strength, good The effect of the decorative effect

Inactive Publication Date: 2015-09-16
GUIZHOU KAILIN GRP CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At the same time, there is also the technology of using phosphogypsum to prepare building insulation materials, but there is no technical solution for the imitation of metal decoration materials in the process of using phosphogypsum to prepare building materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphogypsum-based metal-like decoration material and preparation method thereof
  • Phosphogypsum-based metal-like decoration material and preparation method thereof
  • Phosphogypsum-based metal-like decoration material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Formula: phosphogypsum 300kg, electrolytic yellow phosphorus slag 150kg, quicklime 10kg, copper gold powder 10kg, nitro varnish 21kg, banana water 29kg.

[0040] Preparation:

[0041] Take phosphogypsum and unslaked lime according to the mass ratio of 10:1 and neutralize them for 1min, put them in a mixer and stir for 30s, then turn on the mixer, add electrolytic yellow phosphorus slag and continue to stir for 60s to obtain a mixed material, and then dry the mixed material to After the free water is ≤1%, put it into a ball mill for grinding for 40 minutes, until the specific surface area is 275m 2 / kg; the mixed material after ball milling was calcined at 140°C for 3 hours, and then aged for 24 hours; the aged material was put into a vibration molding machine, and formed by vibration according to the required shape; After natural curing of the vibration-molded material for 7 days, autoclave curing is carried out. The heating rate is 20°C / h, the control temperature is ...

Embodiment 2

[0043] Formula: phosphogypsum 800kg, electrolytic yellow phosphorus slag 600kg, quicklime 100kg, copper gold powder 10kg, nitro varnish 21kg, banana water 29kg.

[0044] Preparation:

[0045] Take phosphogypsum and unslaked lime according to the mass ratio of 10:1 and neutralize them for 1min, put them in a mixer and stir for 30s, then turn on the mixer, add electrolytic yellow phosphorus slag and continue to stir for 60s to obtain a mixed material, and then dry the mixed material to After the free water is ≤1%, put it into a ball mill and grind for 42 minutes until the specific surface area is 275m2 / kg; the mixed material after ball milling was calcined at a temperature of 142°C for 3 hours, and then aged for 26 hours; the aged material was put into a vibration molding machine, and formed by vibration according to the required shape; After natural curing of vibration-molded materials for 7 days, autoclave curing is carried out. The heating rate is 20°C / h, the control temper...

Embodiment 3

[0047] Formula: phosphogypsum 400kg, electrolytic yellow phosphorus slag 250kg, quicklime 30kg, copper gold powder 10kg, nitro varnish 21kg, banana water 29kg.

[0048] Preparation:

[0049] Take phosphogypsum and unslaked lime according to the mass ratio of 10:1 and neutralize them for 1min, put them in a mixer and stir for 30s, then turn on the mixer, add electrolytic yellow phosphorus slag and continue to stir for 60s to obtain a mixed material, and then dry the mixed material to After the free water is ≤1%, put it into a ball mill and grind for 44 minutes until the specific surface area is 276m 2 / kg; the mixed material after ball milling was calcined at a temperature of 144°C for 3 hours, and then aged for 28 hours; the aged material was put into a vibration molding machine, and formed by vibration according to the required shape; After natural curing of the vibration-molded material for 7 days, autoclave curing is carried out. The heating rate is 20°C / h, the control te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a phosphogypsum-based metal-like decoration material and a preparation method thereof. The phosphogypsum-based metal-like decoration material comprises the following raw materials by weight part: 60-130 parts of phosphogypsum, 70-90 parts of electrolytic yellow phosphorus slag and 3-9 parts of quicklime. The preparation method comprises the following steps: burdening, aging, moulding, performing autoclaved curing on a phosphogypsum base material, drying, and spraying to obtain the finished product. The phosphogypsum-based metal-like decoration material has the characteristics of simple construction process, good waterproof flame resistance, high compressive strength, high flexural intensity and strong weatherability, has good decorative effect as an interior decoration building material, consumes a lot of phosphogypsum, reduces natural stone exploitation, and has important meaning for environment protection and continuous development.

Description

technical field [0001] The invention relates to the field of chemical building materials, in particular to a phosphogypsum-based imitation metal decoration material and a preparation method thereof. Background technique [0002] Phosphogypsum is the main industrial by-product when phosphate and compound fertilizer enterprises use phosphate rock and sulfuric acid as raw materials to produce phosphoric acid. The wet-process phosphoric acid production process is to produce extraction slurry by decomposing phosphate rock powder with sulfuric acid, and then filtering to obtain phosphoric acid, which is filtered and washed. Phosphogypsum waste is generated in the process. [0003] With the development of ammonium phosphate industry and high-concentration phosphate compound fertilizer, the discharge of phosphogypsum is increasing year by year. At present, the annual increase of phosphogypsum discharge in the world is 280 million tons, and China is about 50 million tons, accounting ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/14C04B18/14C04B41/61B28B11/24
CPCY02W30/91
Inventor 杨步雷杨永彬向前勇王伟刘小成胡新菊李泽钢李显权
Owner GUIZHOU KAILIN GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com