PTT/carbon fiber composite material and preparation method therefor

A composite material and carbon fiber technology, which is applied in the field of PTT/carbon fiber composite material and its preparation, can solve problems such as low dimensional stability, poor heat resistance, and low strength, and achieve improved surface wettability, low production cost, and high durability. good chemical effect

Inactive Publication Date: 2015-08-26
QINGDAO XINZHAN PLASTIC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polytrimethylene terephthalate (PTT), as a new type of polyester polymer material with excellent comprehensive properties, has been widely used in the fields of fibers, films, engineering plastics, etc., but PTT has poor heat resistance when used alone , low dimensional stability and low strength, which limit its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of PTT / carbon fiber composite material, its component ratio by mass percentage is: PTT 77%, carbon fiber 15%, plasticizer 6%, benzotriazole ultraviolet absorber 1.5%, antioxidant 1010 0.1%, Pentaerythritol stearate 0.4%, described PTT is the polytrimethylene terephthalate of intrinsic viscosity 0.7~1.5dL / g, described carbon fiber is the chopped polyacrylonitrile carbon fiber that the surface has been processed through electrochemical polymerization, described The plasticizer is a compound of thermoplastic polyether ester TPEE and polyisobutylene adipate with a mass ratio of 4:1.

[0020] Preparation method: (1) Place PTT in a forced air circulation oven at 110°C to 120°C and dry for about 6 to 8 hours before use; (2) Carbon fiber surface treatment: use chopped polyacrylonitrile carbon fiber as anode , stainless steel plate as the cathode, the electropolymerization solution is an ammonium salt solution of one of styrene maleic anhydride, methyl vinyl ether maleic ...

Embodiment 2

[0022] A kind of PTT / carbon fiber composite material, its component ratio by mass percentage is: PTT 85%, carbon fiber 10%, plasticizer 4%, benzophenone ultraviolet absorber 0.5%, antioxidant 1010 and antioxidant 0.2% of the compound of agent 168, 0.3% of pentaerythritol stearate, the PTT is poly(trimethylene terephthalate) with an intrinsic viscosity of 0.7-1.5dL / g, and the carbon fiber is the surface treated by electrochemical polymerization. Chopped polyacrylonitrile carbon fiber, the plasticizer is a compound of thermoplastic polyether ester TPEE and polyisobutylene adipate with a mass ratio of 4:1.

[0023] Preparation method: (1) Place PTT in a forced air circulation oven at 110°C to 120°C and dry for about 6 to 8 hours before use; (2) Carbon fiber surface treatment: use chopped polyacrylonitrile carbon fiber as anode , stainless steel plate as the cathode, the electropolymerization solution is an ammonium salt solution of one of styrene maleic anhydride, methyl vinyl et...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a PTT / carbon fiber composite material and a preparation method therefor. The PTT / carbon fiber composite material comprises the following ingredients, by weight, 75%-92% of PTT, 5%-15% of carbon fibers, 2%-6% of plasticizers, 0.5%-2% of ultraviolet ray stabilizing agents, 0.1%-0.5% of anti-oxidants and 0.1%-1% of lubricants. The carbon fibers are short cut polypropionitrile carbon fibers with surfaces processed in an electrochemistry polymerization method. The beneficial effects are that the carbon fibers surfaces are subjected to surface processing in an electrochemistry polymerization method, and the surface infiltration performance and reactivity are raised greatly, and thus the prepared composite material has a high specific strength and excellent crystallization orientation degree; the heat resistance and chemical resistance are good, the size is stable, the preparation technology is simple and controllable, the production cost is low, and popularization is easy.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PTT / carbon fiber composite material and a preparation method thereof. Background technique [0002] Polytrimethylene terephthalate (PTT), as a new type of polyester polymer material with excellent comprehensive properties, has been widely used in the fields of fibers, films, engineering plastics, etc., but PTT has poor heat resistance when used alone , Low dimensional stability and low strength limit its application. Carbon fiber has high strength, high modulus, high temperature resistance, corrosion resistance, fatigue resistance, creep resistance, electrical conductivity, heat transfer and other characteristics. It is a typical high-tech product and is mainly used to prepare advanced composite materials. It has been widely used in aerospace, Sporting goods field, industry field, transportation field and civil construction field. Carbon fiber can be used as a reinf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K13/06C08K9/10C08K7/06
Inventor 不公告发明人
Owner QINGDAO XINZHAN PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products