Combined hot melt adhesive net film and preparing technology thereof

A preparation process, a technology of glued omentum, applied in adhesives, melt spinning, spinneret assemblies, etc., can solve problems such as poor adhesion of non-polar materials, achieve high bonding strength, high production efficiency, reduce The effect of production failure

Active Publication Date: 2015-06-17
KUNSHAN TIANYANG HOT MELT ADHESIVE CO LTD +2
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, conventional hot-melt adhesive related products, such as omentum or adhesive film, are basically aimed at bonding polar materials, and the adhesion to non-polar materials is very poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combined hot melt adhesive net film and preparing technology thereof
  • Combined hot melt adhesive net film and preparing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A composite hot-melt adhesive omentum, which is composed of polyamide hot-melt adhesive omentum and polyolefin hot-melt adhesive omentum. The DSC final melting point of the polyamide hot-melt adhesive used is 122°C, and the melt flow rate is 30g / 10min / 160°C; the composition and mass percentage of the polyolefin hot melt adhesive used are:

[0030] Maleic anhydride grafted high-density polyethylene (graft rate 1%) 8%;

[0031] High-density polyethylene (melt flow rate 0.9g / 10min / 190℃) 50%;

[0032] Ethylene-octene copolymer (melt flow rate 1.6g / 10min / 190℃) 10%;

[0033] Benzoyl Peroxide 0.2%;

[0034] Vinyltrimethoxysilane 1%;

[0035] Rosin 145 20%;

[0036] Talc powder 10%;

[0037] Antioxidant 1010 0.8%.

[0038] A preparation process of a composite hot-melt adhesive film, which melts the above-mentioned polyamide and polyolefin hot-melt adhesives and pumps them into the independent first spinneret and second spinneret; the distance between the two spinnerets i...

Embodiment 2

[0041] A composite hot-melt adhesive film, which is composed of polyamide hot-melt adhesive film and polyolefin hot-melt adhesive film. The DSC final melting point of the polyamide hot-melt adhesive used is 116°C, and the melt flow rate is 50g / 10min / 160°C; the composition and mass percentage of the polyolefin hot melt adhesive used are:

[0042] Maleic anhydride grafted low density polyethylene (graft rate 1.2%) 15%;

[0043] Linear low density polyethylene (melt flow rate 2g / 10min / 190℃) 60%;

[0044] Ethylene-octene copolymer (melt flow rate 3g / 10min / 190℃) 5%;

[0045]Di-tert-butyl peroxide 0.4%;

[0046] γ-Aminopropyltrimethoxysilane 1.3%;

[0047] Hydrogenated carbon five resin 10%;

[0048] Nano calcium carbonate 7.7%;

[0049] Antioxidant 1010 0.6%.

[0050] A preparation process of a composite hot-melt adhesive film, which melts the above-mentioned polyamide and polyolefin hot-melt adhesives and pumps them into the independent first spinneret and second spinneret;...

Embodiment 3

[0053] A composite hot-melt adhesive omentum, which is composed of polyamide hot-melt adhesive omentum and polyolefin hot-melt adhesive omentum. The DSC final melting point of the polyamide hot-melt adhesive used is 130°C, and the melt flow rate is 45g / 10min / 160°C; the composition and mass percentage of the polyolefin hot melt adhesive used are:

[0054] Maleic anhydride grafted linear low density polyethylene (graft rate 1%) 10%;

[0055] Low-density polyethylene (melt flow rate 7g / 10min / 190°C) 65%;

[0056] Polystyrene (melt flow rate 10g / 10min / 190°C) 3%;

[0057] Azobisisobutyronitrile 0.8%;

[0058] γ-Aminopropyltrimethoxysilane 0.7%;

[0059] Terpene resin 15%;

[0060] Kaolin 5%;

[0061] Antioxidant BHT 0.5%.

[0062] A preparation process of a composite hot-melt adhesive film, which melts the above-mentioned polyamide and polyolefin hot-melt adhesives and pumps them into the independent first spinneret and second spinneret; the distance between the two spinneret...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
grafting efficiencyaaaaaaaaaa
grafting efficiencyaaaaaaaaaa
Login to view more

Abstract

The invention discloses a combined hot melt adhesive net film and a preparing technology thereof, and particularly relates to a combined hot melt adhesive net film used for bonding metal and nonpolar materials and a preparing technology of the combined hot melt adhesive net film. Due to the fact that the specific formula is adopted, the polar polyamide hot melt adhesive and the nonpolar polyolefin including a bulking agent are effectively fused. According to the combined hot melt adhesive net film prepared through the technology, the bonding strength of the combined hot melt adhesive net film is high, bonding is durable and stable, and the combined hot melt adhesive net film is particularly suitable for bonding and combining of stainless steel, aluminum, copper and other metal materials with polyethylene, polypropylene and other nonpolar polymers. Meanwhile, according to the preparing technology, the process from raw material preprocessing to final finished combined hot melt adhesive net film preparing is finished in one set of production procedures, the production fault can be greatly reduced, the production efficiency is high, and cost is low.

Description

technical field [0001] The invention relates to a composite hot-melt adhesive omentum and its preparation process, in particular to a composite hot-melt adhesive omentum for bonding metals and non-polar materials and its preparation process. Composite hot melt adhesive film, especially suitable for bonding and compounding metal materials such as stainless steel, aluminum, copper and non-polar polymers such as polyethylene and polypropylene. Background technique [0002] Hot-melt adhesive film is a material with corrosion resistance, aging resistance, good thermal stability, good tensile resistance, burst resistance and good water permeability, so it is widely used in clothing, automobiles, electronics and other industries. [0003] CN 101240148 B provides a preparation method of hot-melt adhesive omentum, including the melting of hot-melt adhesive raw materials, adding a crystallization nucleating agent, extrusion, spinning, air drafting, spinning and other processes, the pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H3/009D04H3/007D04H3/16C09J7/10
CPCC09J11/04D04H3/007D04H3/009D04H3/16C09J2423/00C09J2477/00C09J7/10C09J2301/202C09J2301/304C09J7/00C09J11/08C09J123/06C09J2301/312C08K3/26C08K3/34C08K5/13C08K5/134C08K2003/265C09J11/06D01D4/02D01D5/08D01D5/084D01D5/088D10B2321/021D10B2321/022
Inventor 李哲龙朱万育马星全曾作祥张勇健
Owner KUNSHAN TIANYANG HOT MELT ADHESIVE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap