Method for preparing ZrB2-Cu composite powder

A composite powder, zrb2-cu technology, applied in the field of ceramic/metal composite materials preparation, can solve the problems of difficult uniform distribution of two phases, low performance of composite materials, weak combination of two phase interfaces, etc., to achieve crystallinity without impurity phases, coating Dense, good crystallinity effect

Inactive Publication Date: 2015-05-27
裴洁
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the ZrB 2 The wettability with Cu is poor, the distribution of the two phases is difficult to be uniform, the interface between the two phases is weak, and the performance of the composite material is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment

[0011] Specific embodiment: the preparation process of the present invention comprises ZrB 2 Two steps of pretreatment and electroless copper plating;

[0012] The ZrB 2 The preprocessing step is, the ZrB 2 The powder was soaked in dilute hydrochloric acid solution, cleaned and coarsened for 20 min, washed with deionized water three times, and then ZrB 2 The powder was sensitized by soaking in SnCl2 solution for 20 min, washed three times with deionized water, and finally the ZrB 2 powder soaked in PdCl 2 Activated in the solution for 40min, washed 3 times with deionized water, and the pretreatment process was completed in a magnetic stirrer. During the pretreatment process, the concentration of hydrochloric acid was 100ml / L, and the SnCl 2 +HCl is 30g / L+25ml / L, PdCl 2 +HCl is 0.7g / L+30ml / L;

[0013] Described electroless copper plating step is, plating solution is made of main salt CuS0 4 ·5H 2 0, reducing agent HCHO, complexing agent Na 2 EDTA, stabilizer 2,2'-pyrid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for preparing ZrB2-Cu composite powder, belongs to the field of ceramic / metal composite material preparation and in particular relates to the method for preparing the ZrB2-Cu composite powder having a good internal metal-ceramic binding property. The method comprises two steps of ZrB2 preprocessing and chemical copper plating; the ZrB2 powder is chemically copper-plated by use of a chemical plating method, and then the Cu-coated ZrB2 powder can be prepared. The composite powder prepared by use of the method is good in dispersity; the copper coating is excellent in crystallinity without impurity phase; the surface of the coating is accumulated randomly by fine metal spherical particles; the coating is compact, uniform, flat and smooth, and has wide application prospect.

Description

technical field [0001] The invention belongs to the field of preparation of ceramic / metal composite materials. Background technique [0002] ZrB 2 -Cu composite material is an immiscible ceramic / metal composite material formed by ZrB2 with high melting point and high hardness and Cu with high thermal conductivity and electrical conductivity. This composite material has the dual characteristics of ceramic and metal, which can greatly improve the wear resistance and arc erosion resistance of the material. It is an electrical contact material with high conductivity, high wear resistance, and certain mechanical and mechanical strength. At present, there is little research on the preparation of zirconium diboride ceramics and metal copper composite materials in China. Venkateswaran T et al. used spark plasma sintering (SPS) to prepare ZrB with high hardness and fracture toughness. 2 -6% Cu (mass fraction) composite material, because the addition of Cu significantly improves the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C18/40B22F9/24
Inventor 裴洁
Owner 裴洁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap