Composition for reinforcing binding power and use thereof

A technology of composition and cohesion, applied in the direction of non-macromolecular adhesive additives, non-macromolecular organic compound adhesives, adhesives, etc., can solve the problem of high-grade energy-saving wooden doors and windows that cannot meet the high toxicity of vinyl acetate , poor environmental protection performance and other problems, to achieve excellent curing time, excellent bonding strength, and improve the effect of environmental protection

Inactive Publication Date: 2015-05-13
NANTONG HONGRUI CHEM
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The vinyl acetate used in this glue is highly toxic and not environmentally friendly
[0006] Chinese invention patent application 201410004735.1 (public date: April 16, 2014) discloses an environmentally friendly white latex, the glue includes: polyvinyl alcohol PVA, vinyl acetate VAC, acrylic acid AA, acrylamide AM, persulfuric acid Ammonium, anionic emulsifier A-102, alkyl polyoxyethylene ether LCN-287 nonionic emulsifier; corn starch, transparent powder, plasticizer, diethylene glycol dibenzoate DEDB, preservative KSG-201, hydrogen Sodium oxide, and methanol; but this glue still uses toxic vinyl acetate, which has poor environmental performance
[0007] At the same time, the related glue disclosed in the prior art has poor overall performance in terms of use effect, and cannot yet meet the relevant requirements for the quality of high-grade energy-saving wooden doors and windows.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for reinforcing binding power and use thereof
  • Composition for reinforcing binding power and use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] This embodiment relates to a composition for enhancing adhesion, and the composition can be used to prepare glue for connecting wooden parts, and the glue includes the following components in parts by weight:

[0019] Polyvinyl acetate 700,

[0020] Vinyl acetate 300,

[0021] polyvinyl alcohol 120,

[0022] Dibutyl phthalate 60,

[0023] Diethylene glycol dibenzoate 20,

[0024] Octanol 10,

[0025] Isopropanol 30,

[0026] Allyl methacrylate 10,

[0027] Ethylene glycol dimethacrylate 5,

[0028] Toluene diisocyanate 3,

[0029] Sodium bicarbonate 35,

[0030] water 1400,

[0031] Emulsifier 40, the emulsifier is sodium oleate (i.e. sodium octadecenoate);

[0032] Initiator 5, the initiator is ammonium persulfate.

[0033] All components involved in this example can be obtained through public commercial channels. In the present embodiment, the preparation method steps of the glue used for connecting wooden parts in the wooden window are as follows:

[003...

Embodiment 2

[0040] This embodiment relates to a composition for enhancing adhesion, and the composition can be used to prepare glue for connecting wooden parts, and the glue includes the following components in parts by weight:

[0041] Polyvinyl acetate 1050,

[0042] Vinyl acetate 350,

[0043] polyvinyl alcohol 145,

[0044] Dibutyl phthalate 100,

[0045] Diethylene glycol dibenzoate 40,

[0046] Octanol 15,

[0047] Isopropanol 45,

[0048] Allyl methacrylate 25,

[0049] Ethylene glycol dimethacrylate 10,

[0050] Toluene diisocyanate 7,

[0051] Sodium bicarbonate 50,

[0052] water 1500,

[0053] Emulsifier 50, the emulsifier is sodium dodecylbenzenesulfonate;

[0054] Initiator 10, the initiator is ammonium persulfate.

Embodiment 3

[0056] This embodiment relates to a composition for enhancing adhesion, and the composition can be used to prepare glue for connecting wooden parts, and the glue includes the following components in parts by weight:

[0057] Polyvinyl acetate 800,

[0058] Vinyl acetate 315,

[0059] Polyvinyl alcohol 125,

[0060] Dibutyl phthalate 80,

[0061] Diethylene glycol dibenzoate 25,

[0062] Octanol 12,

[0063] Isopropanol 35,

[0064] Allyl methacrylate 15,

[0065] Ethylene glycol dimethacrylate 7,

[0066] Toluene diisocyanate 4,

[0067] Sodium bicarbonate 39,

[0068] water 1450,

[0069] Emulsifier 45, the emulsifier is sodium dodecylbenzenesulfonate;

[0070] Initiator 6, the initiator is potassium persulfate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a composition for reinforcing binding power and use thereof. The composition for reinforcing binding power comprises the following components in parts by weight: 10-25 parts of allyl methacrylate, 5-10 parts of glycol dimethacrylate and 3-7 parts of toluene diisocynate. The invention further relates to use of the composition for reinforcing binding power in preparation of glue for connecting wood components. The composition for reinforcing binding power provided by the invention can be used for greatly improving the comprehensive performance of the glue for connecting wood components and ensuring that the glue has excellent performance and excellent comprehensive performance on such indexes as thermal stability, initial drying time, water resistance, bonding strength and curing time.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to a composition for enhancing adhesion and its application. Background technique [0002] At present, the threshold industry of doors and windows is relatively low, and the competition in the industry is relatively chaotic. In order to improve product quality and market competitiveness, continuous improvement is required. High-grade energy-saving wooden doors and windows widely used in building exterior windows include: pure wood doors and windows, aluminum-clad wood doors and windows, and wood-aluminum composite doors and windows. The wood-aluminum composite doors and windows are more suitable for the rainy, high temperature and humid climate conditions in the south because the outer side is made of heat-insulating aluminum alloy profiles and the inner side is made of wood decorative profiles. At present, the structure of wood-aluminum composite doors and windows proces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J4/02C09J4/06C09J11/06
Inventor 杭春林
Owner NANTONG HONGRUI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap