Anticorrosive primer for copper

An anti-corrosion primer and component technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of high impact strength and hardness, high adhesion, good corrosion resistance, etc., to achieve good adhesion, good corrosion resistance, The effect of high hardness

Inactive Publication Date: 2014-03-26
JIANGSU PAQINI COPPER IND
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] This application aims at the technical problems of existing hydrophilic coatings such as low flexibility, high impact strength and hardness, good corrosion resistance and high adhesion, and provides an anti-corrosion primer for copper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An anticorrosion primer for copper, the composition of which is expressed in parts by mass: 100 parts of methacrylic acid; 15 parts of sodium hydroxide; 20 parts of 2-ethyl ethyl acrylate; 35 parts of glycolate; 10 parts of isopropanol; 20 parts of isobutyl alcohol; 30 parts of isobutyl methacrylate; 5 parts of butyltriphenylhexanoate; 1 part of styrene; 15 parts of acetone; 5 parts of trimethylol melamine; 10 parts of butyl ester; 40 parts of water.

[0018] The product has good bonding force with copper, and the adhesion reaches Grade 1; the impact resistance is greater than 500MPa, the softness is less than 1mm; the hardness is greater than 2H.

[0019]

Embodiment 2

[0021] An anti-corrosion primer for copper, the composition of which is expressed in parts by mass: 100 parts of methacrylic acid; 20 parts of sodium hydroxide; 30 parts of 2-ethyl ethyl acrylate; 45 parts of glycolate; 20 parts of isopropanol; 25 parts of isobutyl alcohol; 50 parts of isobutyl methacrylate; 10 parts of butyl triphenylhexanoate; 5 parts of styrene; 25 parts of acetone; 10 parts of trimethylolmelamine; 25 parts of butyl ester; 50 parts of water.

[0022] The product has good bonding force with copper, and the adhesion reaches Grade 1; the impact resistance is greater than 520MPa, the softness is less than 0.9mm; the hardness is greater than 2.2H.

[0023]

Embodiment 3

[0025] A kind of anticorrosion primer for copper, it is characterized in that: its composition is expressed in parts by mass: 100 parts of methacrylic acid; 18 parts of sodium hydroxide; 25 parts of 2-ethyl ethyl acrylate; glycolic acid 40 parts of ester; 15 parts of isopropanol; 22.5 parts of isobutyl alcohol; 40 parts of isobutyl methacrylate; 7.5 parts of butyl triphenylhexanoate; 3 parts of styrene; 20 parts of acetone; 7.5 parts; 15 parts of butyl acrylate; 45 parts of water.

[0026] The product has good bonding force with copper, and the adhesion reaches Grade 1; the impact resistance is greater than 550MPa, the softness is less than 0.8mm; the hardness is greater than 2.5H.

[0027] All components in the above examples are commercially available.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
softnessaaaaaaaaaa
Login to view more

Abstract

An anticorrosive primer for copper comprises the components in parts by mass as follows: 100 parts of isopropyl alcohol, 25-30 parts of phenolic novolac resin, 15-30 parts of butyl alcohol, 15-25 parts of polyvinyl acetate, 15-20 parts of zinc chromate, 50-60 parts of toluene, 10-15 parts of a corrosion inhibitor, 10-20 parts of alkyd resin, 3-15 parts of iron oxide red, 3-10 parts of chlorinated paraffin, 15-20 parts of carbon black, 10-15 parts of a dispersant and 5-10 parts of talc powder. The binding force of the primer to the copper is good, the adhesive force reaches grade 1, the shock strength is larger than 500 MPa, the flexibility is smaller than 1 mm, and the hardness is larger than 2 H; and the primer is good in corrosion resistance, convenient to construct, simple in process, free of organic solvents and capable of being widely produced and replacing existing materials.

Description

[0001] technical field [0002] The application belongs to the field of coatings, in particular to an anticorrosive primer for copper. [0003] Background technique [0004] Nano-hydrophilic coatings are specially used for air conditioners. The hydrophilic coatings used in air-conditioners are jointly developed by Xiangzheng Company, University of Science and Technology of China, Hefei University of Technology and other universities, and have obtained nano-hydrophilic film technology and low-cost, high-quality hydrophilicity. Nano-coating preparation process and coating technology. According to this process technology, the nano-hydrophilic coating produced is a nano-coating composed of many nano-components, which has many nano-effects, and the primary particle size of the nano-materials contained in it is between 7 and 80nm. The specific surface area is generally greater than 100㎡ / g. It shows excellent properties in materials, so it is widely used in rubber, plastic, stee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/00C09D7/12C09D5/08
Inventor 王惠张松岩钱忆张陈新燕
Owner JIANGSU PAQINI COPPER IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka