Polypropylene composite material with good appearance and preparation method thereof
A technology of composite materials and polypropylene, which is applied in the field of polypropylene composite materials and its preparation, can solve the problems of affecting the appearance of parts and increasing tiger skin patterns, etc., and achieve the effects of low cost, enhanced compatibility and excellent mechanical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] Prepare raw materials according to the following components and weight percent content:
[0029] Copolymerized polypropylene 62%;
[0030] Ethylene-octene copolymer 15%;
[0031] Ternary copolymerized thermoplastic elastomer 12%;
[0032] Wollastonite 10%;
[0033] Antioxidant 0.6%;
[0034] Lubricant 0.4%;
[0035] Put all the raw materials together into a high-speed mixer and mix for 2-5 minutes, and discharge; then put the mixed material into a twin-screw extruder to extrude and granulate to obtain a polypropylene composite material with good appearance. Wherein, the process temperature is 200° C., and the screw speed is 400 rpm.
Embodiment 2
[0037] Prepare raw materials according to the following components and weight percent content:
[0038] Copolymer polypropylene 70%;
[0039] Ethylene-octene copolymer 8%;
[0040] Ternary copolymerized thermoplastic elastomer 6%;
[0042] Antioxidant 0.6%;
[0043] Lubricant 0.4%;
[0044] Put all the raw materials together into a high-speed mixer and mix for 2-5 minutes, and discharge; then put the mixed material into a twin-screw extruder to extrude and granulate to obtain a polypropylene composite material with good appearance. Wherein, the process temperature is 190° C., and the screw speed is 300 rpm.
Embodiment 3
[0046] Prepare raw materials according to the following components and weight percent content:
[0047] Copolymerized polypropylene 65%;
[0048] Ethylene-octene copolymer 9%;
[0049] Ternary copolymerized thermoplastic elastomer 5%;
[0051] Antioxidant 0.6%;
[0052] Lubricant 0.4%;
[0053] Put all the raw materials together into a high-speed mixer and mix for 2-5 minutes, and discharge; then put the mixed material into a twin-screw extruder to extrude and granulate to obtain a polypropylene composite material with good appearance. Wherein, the process temperature is 180° C., and the screw speed is 350 rpm.
PUM
Property | Measurement | Unit |
---|---|---|
melt flow index | aaaaa | aaaaa |
melt flow index | aaaaa | aaaaa |
melt flow index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com