A high temperature and corrosion resistant coating

A corrosion-resistant and high-temperature-resistant technology, applied in the field of high-temperature and corrosion-resistant coatings, can solve the problems of not having a good thermal insulation effect, affecting the appearance of the exterior wall and the quality of the exterior wall, poor high temperature resistance and corrosion resistance, etc. Eliminate pinhole defects, improve brushing uniformity, and be less prone to cracking

Active Publication Date: 2017-02-08
重庆嘉达合创节能科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Architectural coatings are indispensable decorative and protective materials in the construction industry. They are used to coat buildings, decorate buildings or protect buildings. Floor coatings and roof coatings, but the exterior wall architectural coatings in the prior art generally have the following problems: 1) The thermal insulation performance is poor, and it cannot play a good thermal insulation effect in cold winter or hot summer , 2) High temperature resistance and poor corrosion resistance. After a long time of use, the exterior wall coating is gradually corroded, which seriously affects the appearance and quality of the exterior wall. Therefore, there is an urgent need for a new coating to solve the above problems. technical problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A high temperature and corrosion resistant coating, said coating comprises the following substances and components, 30 parts of epoxy resin, 22 parts of kaolin, 1 part of antibacterial agent, 1 part of antifungal agent, 15 parts of sericite, 10 parts of water, 10 parts of titanium dioxide 10 parts of alumina powder, 1 part of dispersant, 1 part of antifreeze, 2 parts of expanded perlite, 1 part of film-forming aid, 5 parts of quartz powder, 10 parts of melamine, 10 parts of fly ash, aluminum silicate 20 parts, 8 parts of silicon oxide, 1 part of barium sulfate, 1 part of wollastonite powder, 30 parts of mixed solvent, wherein the mixed solvent is toluene and butanol, and the mass ratio of toluene and butanol is 2.6:0.8. The coating has good chemical stability, excellent heat resistance, acid and alkali resistance, and antibacterial and mildew-proof effects.

Embodiment 2

[0021] A high temperature and corrosion resistant coating, said coating comprises the following substances and components, 40 parts of epoxy resin, 30 parts of kaolin, 3 parts of antibacterial agent, 5 parts of antifungal agent, 25 parts of sericite, 20 parts of water, 14 parts of titanium dioxide 13 parts of alumina powder, 2 parts of dispersant, 2 parts of antifreeze, 4 parts of expanded perlite, 2 parts of film-forming aid, 15 parts of quartz powder, 20 parts of melamine, 18 parts of fly ash, aluminum silicate 30 parts, 15 parts of silicon oxide, 3 parts of barium sulfate, 1.5 parts of wollastonite powder, 35 parts of mixed solvent, wherein the mixed solvent is toluene and butanol, and the mass ratio of toluene and butanol is 3.6:1.

Embodiment 3

[0023] A high temperature and corrosion resistant coating, said coating comprises the following substances and components, 33 parts of epoxy resin, 25 parts of kaolin, 1.5 parts of antibacterial agent, 2 parts of antifungal agent, 18 parts of sericite, 11 parts of water, 12 parts of titanium dioxide Parts, 11 parts of alumina powder, 1.5 parts of dispersant, 1.1 parts of antifreeze, 2.5 parts of expanded perlite, 1.2 parts of film-forming aid, 8 parts of quartz powder, 12 parts of melamine, 12 parts of fly ash, aluminum silicate 22 parts, 9 parts of silicon oxide, 1.5 parts of barium sulfate, 1.1 parts of wollastonite powder, 31 parts of mixed solvent, said mixed solvent is dimethyl phthalate, ethanol, wherein dimethyl phthalate, ethanol mass The ratio is 2.1:0.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel high temperature and corrosion resistant coating. The novel high temperature and corrosion resistant coating comprises the following components in mass ratio: 30 to 40 parts of epoxy resin, 22 to 30 parts of kaolin, 1 to 3 parts of antibacterial agent, 1 to 5 parts of mildew preventive, 15 to 25 parts of sericite, 10 to 20 parts of water, 10 to 14 parts of titanium dioxide, 10 to 13 parts of alumina powder, 1 to 2 parts of dispersing agent, 1 to 2 parts of antifreezing agent, 2 to 4 parts of expanded perlite, 1 to 2 parts of coalescing agent, 5 to 15 parts of quartz powder, 10 to 20 parts of melamine, 10 to 18 parts of coal ash, 20 to 30 parts of aluminium silicate, 8 to 15 parts of monox, 1 to 3 parts of barium sulfate, 1 to 1.5 parts of wollastonite in powder, and 30 to 35 parts of mixed solvent.

Description

technical field [0001] The invention relates to a coating, in particular to a high temperature and corrosion resistant coating. Background technique [0002] With the development of the economy and the continuous advancement of science and technology, people's environmental protection intentions are becoming stronger and stronger, and the country has comprehensively promoted energy conservation and emission reduction as an important task, which makes all walks of life move towards green, environmental protection, technology direction of development. Architectural coatings are indispensable decorative and protective materials in the construction industry. They are used to coat buildings, decorate buildings or protect buildings. Floor coatings and roof coatings, but the exterior wall architectural coatings in the prior art generally have the following problems: 1) The thermal insulation performance is poor, and it cannot play a good thermal insulation effect in cold winter or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D7/12C09D5/08
Inventor 陈建军
Owner 重庆嘉达合创节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products