Method for preparing high-performance irradiation cross-linking ultrahigh polyethylene extrusion plate
A polyethylene, high-performance technology, applied in the field of preparation of high-performance radiation cross-linked melt-extruded sheets, can solve problems such as damage to inherent properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0020] The radiation crosslinked ultra-high molecular weight polyethylene extruded sheet according to the present invention comprises the following steps: using ultra-high molecular weight polyethylene powder with a molecular weight of about 2.5 million as a raw material, and adding 1 wt% of nucleating agent 1,3 -2,4-Dibenzylidene sorbitol, 3wt% polyfunctional sensitizer trimethylolpropane trimethacrylate (TMPTMA), 3wt% polyethylene wax and 1wt% antioxidant 3,4,5-tri Propyl hydroxybenzoate (PG), after being fully mixed, is sent into the extruder, and after conveying, compacting and heating in sequence, it is extruded from the extruder. During the heating process, the temperature and pressure of the raw materials are controlled, and the thickness of the extruded sheet is 10mm. The obtained samples were exposed to air with 60 Co-γ-ray irradiation, the irradiation dose is 40kGy, and the dose rate is 2Gy / s. The irradiated samples were annealed in a vacuum oven at 120°C for 5 hou...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com