Polylactic resin composition film and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of polylactic acid resin and composition, applied in the direction of coating, etc., can solve the problems of high processing equipment requirements, unfavorable sustainable development, reduction of petroleum resources, etc., achieve good processing fluidity, improve processing difficulties, and improve processing flow sexual effect
Active Publication Date: 2014-01-08
CHINA PETROLEUM & CHEM CORP +1
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Patent CN101676324 discloses a polypropylene biaxially oriented film (BOPP) pearlescent synthetic paper masterbatch, which can be used as a packaging material for candy, ice cream, etc., but its matrix is polypropylene. Although it is more environmentally friendly, its source is mostly petroleum In terms of chemical industry, the dwindling and shortage of petroleum resources is not conducive to its sustainable development
And although this method adopts the method of side feeding in order to solve the processing difficulties, the side feeding system has relatively high requirements for processing equipment
[0004] Patent CN101638509 discloses a method of filling polylactic acid with toughened calcium carbonate. Although it can play a toughening role, this method needs to be filled with a large amount of calcium carbonate. Network congestion and other problems
Moreover, the existing toughening method improves the toughness of polylactic acid and also greatly weakens its own rigidity, which is not suitable for some occasions where the film needs to be easily torn.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1-9
[0049] The vacuum-dried polylactic acid resin PLA and antioxidant (1010 and 168 weight ratio 1:1 mixture), lubricant zinc stearate, pearl powder, nano Calcium carbonate and / or light calcium carbonate after surface modification treatment by silane coupling agent KH550 are mixed uniformly in a high-speed mixer according to the amount; the mixed materials are added to the feeder of the WP40 twin-screw extruder, The material enters the twin-screw through the feeder, melts and mixes evenly through the screw, extrudes, granulates, and dries. During the processing, the temperature of the screw is kept between 170-200° C., and the rotational speed of the screw is controlled between 200-350 rpm.
[0050] The extruded and dried material is cast into a film with a thickness of 200-500 μm through a casting machine (Shantou Guanghua Machinery Industry Co., Ltd.). , the temperature of barrel zone 2, zone 3, zone 4, ring network zone and diversion zone is 180°C, 170°C, 170°C, 170°C, 170°C r...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
flexural modulus
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention provides a polylactic resin composition film and a preparation method thereof, and relates to the field of plastic processing. The polylactic resin composition film comprises the following components: 100 weight parts of polylactic resin and 0.5 to 5.5 weight parts of functional filler which are blended, wherein the polylactic resin has the weight-average molecular weight of 80,000-300,000 and the molecular weight dispersibility of 1.5-2.2; and the functional filler is at least one of the following inorganic fillers: calcium carbonate, clay, silica, alumina, barium sulfate, calcium sulfate, talc, magnesium sulfate, titanium dioxide, zeolite, aluminum sulfate, kieselguhr, kaolin, calcium oxide and magnesium oxide. The preparation method comprises the following steps of: melting, blending and granulating the components in the proportion, casting and pressing, and biaxially tensioning to obtain the polylactic resin composition film. The film is completely biodegradable, has balanced rigidity and toughness, maintains the tensile strength, has the elongation at break improved by 3 to 7 times compared with the original elongation at break, and has uniform texture, high decorative property, high printing property and unidirectional tearing property.
Description
technical field [0001] The invention relates to the technical field of resin films, and more specifically, relates to a polylactic acid resin composition film and a preparation method thereof. Background technique [0002] Polylactic acid (PLA), also known as polylactide, is based on starch extracted from corn, wheat, cassava, etc. thermoplastic polyester. Polylactic acid is a completely environmentally friendly biodegradable material with good mechanical properties and biodegradability. It has a wide range of raw materials. It is easily decomposed and replaced by various microorganisms in nature or enzymes in animals and plants, and finally forms water and carbon dioxide. pollutes the environment, and thus is considered to be the most promising biodegradable polymer material. In addition, the non-toxicity of polylactic acid allows it to be used in packaging that comes into direct contact with food. In terms of post-processing, polylactic acid has excellent biodegradabili...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.