Phosphate-based high-temperature-resistant anti-corrosion paint and preparation method thereof
An anti-corrosion coating and phosphate technology, applied in anti-corrosion coatings, coatings, etc., can solve problems such as economic loss, oxidation, and surface corrosion of incinerators, and achieve the effect of prolonging the service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] Add 240.0g of phosphoric acid into the reactor, add 40.0g of magnesia several times in batches, and react to obtain phosphate. The reaction temperature is between 20°C and 50°C. Add 20.0g of chromium trioxide, 1.0 G potassium molybdate, 250g water were stirred to obtain a clear and transparent phosphate base material; in addition, 250g ultrafine chrome green, 4.0g boric acid, 5.0g sodium hexametaphosphate, 3.0g chromium nitrate, 300g water were mixed and ground for 3 hours Finally, the fineness of the color paste is measured to be less than 4 microns; after mixing the phosphate base material and the color paste, stir and disperse, and the stirring speed is 800 to 1000 revolutions per minute. After dispersing for 4 hours, use a 300-mesh nylon mesh to filter to obtain a phosphate-based high-temperature resistant and anti-corrosion coating.
[0034] The coating is resistant to 900°C and 1000 hours without cracking or peeling off. Neutral salt spray test for 2000 hours The...
Embodiment 2
[0036] Add 250.0g of phosphoric acid into the reactor, add 50.0g of aluminum oxide in batches and several times, the reaction temperature is between 50°C and 102°C, and react to obtain phosphate, add 18.0g of chromium trioxide to the above-mentioned phosphate, 3.0 G molybdic acid, 250g water were stirred to obtain a clear and transparent phosphate base material; in addition, 255g ultrafine chrome green, 5.0g boric acid, 2.0g sodium hexametaphosphate, 3.0g chromium nitrate, 320g water were mixed and ground, and after grinding for 2 hours The fineness of the color paste is measured to be less than 4 microns; after mixing the phosphate base material and the color paste, stir and disperse at a stirring speed of 800 to 1000 revolutions per minute. After dispersing for 4 hours, use a 300-mesh nylon mesh to filter to obtain a phosphate-based high-temperature resistant and anti-corrosion coating.
[0037] The coating is resistant to 900°C and 1200 hours without cracking or peeling off...
Embodiment 3
[0039] Add 230.0g of phosphoric acid into the reactor, add 60.0g of aluminum hydroxide and 8.0g of aluminum oxide in batches in small amounts, the reaction temperature is between 50°C and 102°C, and the reaction will give phosphate. Add 18.0g of aluminum hydroxide to the above phosphate g chromium trioxide, 2.0g potassium dichromate, and 220g water were stirred to obtain a clear and transparent phosphate base material; in addition, 240g ultrafine chrome green, 5.0g boric acid, 4.0g sodium hexametaphosphate, 1.0g chromium nitrate, 2.0g Chromium phosphate, 1.0g of chromium sulfate, and 350g of water are mixed and ground. After grinding for 2 hours, the fineness of the color paste is less than 4 microns; after mixing the phosphate base and color paste, stir and disperse at a stirring speed of 800 to 1000 rpm. After dispersing for 4 hours, use a 300-mesh nylon mesh to filter to obtain a phosphate-based high-temperature resistant and anti-corrosion coating.
[0040] The coating is ...
PUM
Property | Measurement | Unit |
---|---|---|
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com