Method for cladding copper alloy layer on surface of steel substrate by laser brazing

A copper alloy layer and cladding technology, applied in the direction of metal material coating process, coating, etc., can solve the problems of uneven coating, waste, low bonding strength and so on

Inactive Publication Date: 2010-08-18
TAIYUAN UNIV OF TECH
View PDF2 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Copper alloy has many advantages, but copper reserves are small and expensive, so it is a material that should be used sparingly. Only in special cases, such as special magnetic properties, corrosion resistance, processing properties, mechanical properties and other conditions are required. before considering using
[0004] Tin bronze is widely used in shipbuilding, chemical industry, machinery, instrumentation and other industries. It mainly manufactures wear-resistant parts such as bearings and bushings, as well as anti-corrosion and anti-magnetic parts. Most copper alloy parts are integrally formed, which is costly and wasteful. , so that the application of copper alloys is greatly restricted, therefore, composite materials that choose cheap steel materials as substrates and copper alloys as claddings emerged as the times require
[0005] At present, there are many methods for preparing copper alloy composite coatings on metal surfaces, such as surface sintering, surface spraying, surface electroplating, and surface mechanical treatment. Uniformity, low bonding strength, easy to fall off, some complex processes, high cost, are not ideal, and need further discussion and research

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for cladding copper alloy layer on surface of steel substrate by laser brazing
  • Method for cladding copper alloy layer on surface of steel substrate by laser brazing
  • Method for cladding copper alloy layer on surface of steel substrate by laser brazing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0106] The present invention will be further described below in conjunction with accompanying drawing;

[0107] figure 1 As shown, it is the state diagram of laser brazing cladding copper alloy layer on the surface of the ring steel base. On the laser machine, the ring steel should be clamped firmly, concentric front and rear, and rotate at a constant speed. Rotate clockwise for laser irradiation, and return counterclockwise for cooling .

[0108] The carrier gas argon is used in conjunction with the powder feeder to make the powder feed uniform.

[0109] The laser beam moves parallel to the ring steel synchronously to make the irradiation uniform and prevent surfacing.

[0110] The power of the laser beam should be consistent, the value should be reasonable and moderate, the laser irradiation should be controlled according to the program, rotate at a constant speed according to the helix angle, and irradiate the ring steel with a single starting point and end point.

[011...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for cladding a copper alloy layer on the surface of a steel substrate by laser brazing. A method of feeding powder by argon gas, cladding by laser brazing and vacuum heat treatment is used on a laser machine for cladding a copper alloy layer on the surface of the steel substrate by laser brazing; the laser machine is used for remelting and curing the surface of the steel substrate firstly; and laser beams irradiate in all directions according to the geometric locus of ring steel set by computer programs to enable copper alloy powder and borax powder to be melted and cured on the surface of the steel substrate to form the copper alloy layer. The thickness of the copper alloy layer is 0.5mm; the average microhardness of the copper alloy layer is 375HV0.2 which is 2 times of the average microhardness of the steel substrate; and compared with the steel substrate, the wear resistance of the copper alloy layer is improved by 52.8%, and the corrosion resistance of the copper alloy layer is improved by 45.3%. The method has advanced processes and reasonable parameters; the metallographic structure of the cured and melted layer is compact and firm and can not fall off easily; and the method can be used for cladding alloy layers on the surfaces of steel substrates of various molded surfaces by brazing and can be used for cladding alloy layers on various molded surfaces and special-shaped non-standard molded surfaces, thereby greatly improving the performance of the surfaces of the steel substrates.

Description

technical field [0001] The invention relates to a method for cladding a copper alloy layer by laser brazing on the surface of a steel base, and belongs to the technical field of metal surface enhancement and modification. Background technique [0002] Among non-ferrous metal alloys, copper alloys have good electrical and thermal conductivity, excellent friction reduction and wear resistance, high elastic limit and fatigue limit and good processing performance, and have good corrosion resistance to atmosphere and water. Therefore, copper alloys have been widely used in aerospace, electronics industry, instrument industry, shipbuilding industry and machinery manufacturing industry. [0003] Copper alloy has many advantages, but copper reserves are small and expensive, so it is a material that should be used sparingly. Only in special cases, such as special magnetic properties, corrosion resistance, processing properties, mechanical properties and other conditions are required....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C24/10C22F1/08
Inventor 王文先崔泽琴刘旭张红霞曹国光许并社
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products