Production method of aluminum and copper composite metal band

A composite metal plate and production method technology, applied in the direction of metal rolling, tension/pressure control, roll speed control, etc., can solve the problems of inability to obtain aluminum and copper composite metal strips, difficult aluminum oxidation, and unstable product quality and other problems, to achieve remarkable economic effects, solve oxidation problems, and stabilize product quality

Active Publication Date: 2010-06-30
LUOYANG TONGYI METAL MATERIAL DEV +2
View PDF0 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current production method has disadvantages such as complex production process, high production cost, low efficiency, low composite strength, and unstable product quality. Especially when aluminum is composited with copper, the problem of aluminum oxidation is difficult to solve, and the current production method can only A single plate is produced, and continuous aluminum and copper composite metal strips cannot be obtained

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A method for manufacturing aluminum and copper composite metal strips, comprising the following steps: heating and smelting metal aluminum, refining and degassing at 790°C, and after refining and degassing, when the temperature of the aluminum liquid is 690°C, the aluminum liquid is Stand still for 5 minutes, and then pour into the preheated nozzle of the aluminum casting and rolling machine. The cast aluminum liquid is cooled and crystallized into a semi-solid state; choose a copper strip with a thickness of 0.3mm, and the copper strip is firstly treated with alkali washing and degreasing, and then Put the copper strip close to the surface of the grinding roller for single-sided online grinding until there is no oxide layer on the surface. After grinding, the copper strip is heated to 230°C online; the semi-solid aluminum is in contact with the polished surface of the copper strip. Anaerobic continuous casting and rolling, the rolling speed during anaerobic continuous c...

Embodiment 2

[0013] A method for producing aluminum and copper composite metal strips, comprising the following steps: heating and melting aluminum alloy liquid according to the chemical composition of the aluminum alloy grade 1050, refining and degassing at 810°C, and after the refining and degassing is completed, the aluminum liquid is When the temperature is 760°C, let the molten aluminum stand for 15 minutes, and then pour it into the preheated nozzle of the aluminum casting and rolling machine. The cast aluminum liquid is cooled and crystallized into a semi-solid state; two copper plates with a thickness of 0.5mm are selected. The two copper strips are respectively treated with alkali washing and degreasing, and then the two copper strips are respectively attached to the roller surfaces of the upper and lower grinding rollers for single-sided online grinding until there is no oxide layer. After grinding, the copper strips are heated online to 250°C; contact semi-solid aluminum with the...

Embodiment 3

[0015] A method for producing aluminum and copper composite metal strips, comprising the following steps: heating and melting aluminum alloy liquid according to the chemical composition of aluminum alloy grade 1070, refining and degassing at 800°C, and after refining and degassing, when the aluminum liquid is When the temperature is 820°C, let the molten aluminum stand for 15 minutes, and then pour it into the preheated nozzle of the aluminum casting and rolling machine. The cast aluminum liquid is cooled and crystallized into a semi-solid state; two copper strips with a thickness of 2mm are selected. , the two copper strips are respectively treated with alkali washing and degreasing, and then the two copper strips are respectively attached to the roller surfaces of the upper and lower grinding rollers for single-sided online grinding until there is no oxide layer on the surface, and the copper strips are placed online after grinding. Heating to 240°C; contact semi-solid alumin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of an aluminum and copper composite metal band. In the method, the aluminum and copper composite metal band is manufactured by anaerobic continuous casting and rolling of semisolid aluminum or aluminum alloy and a solid copper band. In the production method of the invention, the anaerobic metallurgical combination of the solid copper band and molten aluminum is realized, the aluminum oxidization problem is solved, the combined strength is high, and the aluminum and copper bonding strength is more than or equal to 100MPa; the continuous casting and rolling of the copper band and the molten aluminum are adopted to produce the aluminum and copper composite metal band, so the production efficiency is greatly improved by scores of times and the product quality is stable; the produced aluminum and copper composite metal band retains the original surface quality of the copper band, has a uniformly-thick copper layer and can be deeply processed by cold rolling; and the copper band and the molten aluminum, which comprise different components, can be used, and products are diversified and widely applicable. The method has the advantages that: the production process of the copper and aluminum composite band is advanced and comprises a few working procedures; and the energy-saving, material-saving and economic effects are obvious.

Description

technical field [0001] The invention relates to the technical field of metal strip production, in particular to a production method of aluminum and copper composite metal strip. Background technique [0002] Copper and aluminum are important non-ferrous metals, which are widely used in industrial and civilian fields. Copper has good electrical and thermal conductivity, corrosion resistance, and antibacterial properties, and aluminum has good electrical and thermal conductivity. Compared with aluminum, copper resources are scarce, and aluminum resources are abundant, and the proportion of aluminum is small, and the price is low. Aluminum and copper composite metal strip is a kind of bimetal with aluminum as the matrix and copper-coated outer layer. It combines the high-quality electrical conductivity and low-cost resources of aluminum with the high chemical stability of copper and low contact It is a new type of conductor material and decoration material that integrates resi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/38B21B37/46B21B37/48
Inventor 尚郑平符会文叶晋予尚爱平谢敬佩王爱琴王文焱李继文李洛利
Owner LUOYANG TONGYI METAL MATERIAL DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com