Microwave sintering of superfine grain base titanium carbonitride

A technology of titanium carbonitride and ultra-fine grains, which is applied in the field of microwave sintering of ultra-fine grain titanium carbonitride-based cermets, which can solve the problems of coarse material grains, high energy consumption, long sintering and holding time, etc. , to achieve the effect of simple process, excellent performance, uniform and reliable heating

Inactive Publication Date: 2009-03-11
HUNAN UNIV OF SCI & TECH
View PDF11 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The information disclosed in the above-mentioned public documents shows that those that really involve the material sintering process use conventional vacuum sintering or atmosphere protection sintering technical solutions, which have long sintering and holding time, high energy consumption, and easy to make material grains coarse, etc. defect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microwave sintering of superfine grain base titanium carbonitride
  • Microwave sintering of superfine grain base titanium carbonitride
  • Microwave sintering of superfine grain base titanium carbonitride

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Take a certain proportion of TiC 0.7 N 0.3 , WC, TaC, Co, Ni, Mo 2 C, ZrC, VC powder, according to the following mass ratio formulated into a mixture:

[0033] TiC 0.7 N 0.35 0.5wt% WC 15wt% TaC 10wt% Mo 2 C 8wt% Co 10w Mt% Ni 5wt% ZrC 1.0wt% VC 0.5wt%

[0034] The particle size of the powder of each of the above components is ≤1 μm.

[0035] Then the blank is made by powder metallurgy method, the process is:

[0036] (1) Wet grinding: Put the above mixed powder into the stainless steel ball mill tank of QM-1SP4 ball mill, add n-hexane at 200-400ml / l, select Φ5 hard alloy balls, the ball-to-material ratio is 5:1, and the speed is 200rpm , ball milling for 48 to 96 hours;

[0037] (2) Add molding agent: weigh paraffin wax by 3-5wt%, dissolve it in n-hexane, add ball mill tank and wet mill together with the mixture;

[0038] (3) Sieving: pass the ball milled slurry through a 60-mesh sieve, and settle for 1 to 2 hours;

[0039] (4) Drying: Put the precipitated mate...

Embodiment 2

[0050] Take a certain proportion of TiC 0.5 N 0.5 , WC, TaC, Co, Ni, Mo 2 C, ZrC, VC powder, according to the following mass ratio formulated into a mixture:

[0051] TiC 0.5 N 0.5 50.5wt% WC 15wt% TaC 10wt% Mo 2 C8 wt% Co 10wt% Ni5wt% ZrC 1.0wt% VC 0.5wt%.

[0052] The particle size of the powder of each of the above components is ≤1 μm.

[0053] Then the blank is made by powder metallurgy technology, the process is:

[0054] (1) Wet grinding: put the above mixed powder into the stainless steel ball milling tank of QM-1SP4 ball mill, add n-hexane at 350ml / l, select Φ5 hard alloy balls, the ball-to-material ratio is 5:1, and the speed is 200rpm. 96 hours.

[0055] (2) Adding forming agent: weigh paraffin wax according to 5wt%, dissolve it in n-hexane, add ball mill jar and wet mill together with the mixture.

[0056] (3) Screening: pass the milled slurry through a 60-mesh sieve, and settle for 2 hours.

[0057] (4) Drying: Put the precipitated material into a ZK-82...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The utility model provides microwave sintering of an ultra-fine grain titanium carbonitride group cermet. A 300MHz to 8GHz microwave frequency medium is used as a heat source to enable a billet of the ultra-fine grain titanium carbonitride group cermet to absorb microwave energy to complete the sintering process. During the sintering process, vacuum and atmosphere protection microwave heating and sintering techniques are adopted respectively according to the ratio of carbon to nitrogen of the billet of the ultra-fine grain carbon titanium nitride cermet. The 300MHz to 8GHz microwave frequency is used to heat and sinter the billets of the titanium carbonitride group cermet with different ratio of carbon to nitrogen and vacuum microwave sintering and atmosphere protection microwave sintering technological proposals are used respectively for the billets of the titanium carbonitride group cermet with the different ratio of carbon to nitrogen, which overcomes the defects of the prior vacuum or atmosphere protection sintering techniques, such as low heating efficiency, long sintering time, large energy consumption, serious environment pollution and oversized grains, and the like. The microwave sintering can be widely applied to sintering other ceramics, ceramic matrix composites and intermetallic compound materials with stronger microwave absorbing capacity.

Description

technical field [0001] The invention relates to microwave sintering, in particular to microwave sintering of ultrafine grain titanium carbonitride-based cermets. Background technique [0002] TiCN-based cermet is a new type of tool material developed in the early 1970s. Its excellent performance fills the gap between WC-based cemented carbide and ceramics, and is especially suitable for steel at high speeds of 200-400m / min. Semi-finishing and finishing of cast iron. At present, the traditional sintering methods for producing TiCN-based cermets at home and abroad are mainly conventional vacuum sintering / atmosphere protection sintering, using heating elements such as graphite to generate heat, and heating the material from the surface to the inside through radiation, convection, and conduction. The heating method requires a long time to heat up and keep warm, so that the sintered TiCN-based cermet material can reach a certain strength and hardness. At present, the domestical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/58C04B35/64
Inventor 张厚安唐思文颜建辉许剑光李鹏南李颂文古思勇严迪科
Owner HUNAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com