White composition capable of solidifying by ultraviolet light

A composition and ultraviolet light technology, applied in the field of ultraviolet light curing white compositions, can solve the problems of poor covering of white paint to substrates, poor curing of paints, difficult adhesion of substrates, etc. The effect of adhesion and simple construction process

Inactive Publication Date: 2008-04-02
湖南阳光新材料有限公司
View PDF0 Cites 66 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, the white paint obtained by this invention has poor covering property to the substrate, and the raw material is expensive
Usually, the white pigment titanium dioxide has a strong absorption of ultraviolet light, so the coating cannot be cured well, and the substrate is difficult to adhere to.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Carboxyl-containing epoxy acrylic resin (EP-I) 10%

[0033] Carboxyl-containing urethane acrylate (YG-I) 20%

[0034] Hyperbranched polyester acrylate (6361-100) 30%

[0035] 1,6-Hexanediol Acrylate 20%

[0036] Titanium dioxide 12%

[0037] 2-Hydroxy-2-methyl-1-phenylacetone (1173) 3%

[0038] Bis(2,4,6-trimethylbenzoyl)phenylphosphine oxide (819) 0.8%

[0039] Fumed silica 1%

[0040] BYK-130 (dispersant) 0.2%

[0041] 6153-1 1.5%

[0042] PM-2 1.5%

[0043] Mix any of the above three resins with acrylic acid monomer, titanium dioxide, fumed silica, and dispersant in proportion, and grind them on a three-roller machine until the fineness is ≤30μ, then add other components in proportion, at 40°C After fully stirring or dispersing at -20°C, filter with a 200-mesh filter cloth to obtain the UV-curable white composition of the present invention. Apply this composition to solid wood board or density board, and control the wet film thickness at 20-30μ , After being...

Embodiment 2

[0045] Carboxyl-containing epoxy acrylic resin (EP-I) 40%

[0046] Carboxyl-containing urethane acrylate (YG-II) 5%

[0047]Hyperbranched polyester acrylate (CN2301) 10%

[0048] Tripropylene glycol diacrylate (TPGDA) 20%

[0049] Hydroxyethyl Methacrylate 6%

[0050] Titanium dioxide 8%

[0051] 2-Hydroxy-2-methyl-1-phenylacetone (1173) 4%

[0052] Bis(2,4,6-trimethylbenzoyl)phenylphosphine oxide (819) 1%

[0053] BYK-161 0.4%

[0054] PM-2 2.8%

[0055] 6153-1 2%

[0056] The sample preparation method and curing conditions are the same as in Example 1, and the test results are shown in Table-1.

Embodiment 3

[0058] Carboxyl-containing epoxy acrylic resin (EP-1) 15%

[0059] Carboxyl-containing polyurethane acrylate (YG-II) 15%

[0060] Hyperbranched polyester acrylate (CN2301) 10%

[0061] Pentaerythritol Triacrylate (PETA) 15%

[0062] Hydroxyethyl Methacrylate 14%

[0063] Titanium dioxide 20%

[0064] 2-Hydroxy-2-methyl-1-phenylacetone (1173) 4%

[0065] Bis(2,4,6-trimethylbenzoyl)phenylphosphine oxide (819) 1%

[0066] BYK-130 (dispersant) 0.2%

[0067] 6153-1 5.8%

[0068] The sample preparation method and curing conditions are the same as in Example 1, and the test results are shown in Table-1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a white composition for ultraviolet solidification. The composition comprises the components of the weight percentages: (1) 10 percent to 40 percent of epoxy acrylate containing carboxyl; (2) 5 percent to 20 percent of polyurethane acrylic ester containing carboxyl; (3) 10 percent to 30 percent of super branching polyester acrylate; (4) 15 percent to 40 percent of acrylic monomer of single- or multi-functional degree; (5) 8 percent to 20 percent of titanium dioxide; (6) 1 percent to 8 percent of light initiator; (7) 0.5 percent to 3 percent of auxiliary aid; and (8) 0.5 percent to 10 percent of adhesive assistant agent. The construction process of the coating of the present invention is simple; the coating can be widely used (not limited) for various density boards, and solid plate materials. After the coating is solidified by ultraviolet irradiation, the coating film has good adhesive capability, high hardness, good covering capability and leveling performances.

Description

technical field [0001] The invention relates to an ultraviolet light-curable white composition, which can be widely used in various density boards and solid wood boards, and has good hardness and good hiding power. Background technique [0002] UV curing materials have been widely used in wood, plastic, metal, paper and other industries due to their high efficiency, energy saving and environmental protection. Due to the absorption of ultraviolet light by inorganic pigments, especially titanium dioxide (titanium dioxide), it has always been difficult to design and prepare UV-curable thick coating materials that can be completely covered. At present, the UV curing materials used commercially are mainly transparent. CN1225642A discloses a photosensitive composition and white paint. This invention adopts a special photosensitive composition, which is colorless and transparent at room temperature, but can It is cured and whitened by ultraviolet light to produce a white substance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/00C09D163/10C09D175/14C09D167/06
Inventor 胡辉梁亮余四清梁建华胡立新
Owner 湖南阳光新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com