Nanoporous tungsten carbide catalyst and preparation method thereof

Inactive Publication Date: 2007-11-22
POSTECH ACAD IND FOUND
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0007] The present invention relates to a nanoporous tungsten carbide catalyst and a preparation method thereof, and more particularly, to a nanoporous tungsten carbide catalyst having high electrochemical activity and enhanced resistance to poisoning by carbon monoxide (CO), and a preparation method thereof. Accordingly, even after use for an extended period of time, the nanoporous tungsten carbide catalyst of the present invention can maintain a long-term high catalytic activity with a reduced amount of a metallic active component compared to a precious metal catalyst.
[0009] In a fuel cell, hydrogen or fuel is supplied to an anode and oxygen is supplied to a cathode to cause an electrochemical reaction between the anode and the cathode, thereby generating electrical energy. An oxidation reaction of hydrogen or organic materials takes place at the anode and a reduction reaction of oxygen takes place at the cathode, thereby creating a difference in the electric potential between the anode and the cathode.
[0012] Of these fuel cells, the direct methanol fuel cells (DMFCs) are a relatively new type of fuel cell and have several advantages such as high energy density, low working temperature, easy processability of methanol fuel liquid, and so on, and offer the promise of being applied in portable devices such as small-size communication devices, or notebook computers. In addition, the polymer exchange membrane fuel cells (PEMFCs) have remarkably higher power output, lower operation temperature, quicker startup and faster response than other fuel cells. Further, the PEMFCs are suitably developed for use as power supplies in numerous applications, including portable power devices such as automobiles, distributed power devices such as residential areas or public buildings, and small scale power devices such as electronic devices, and so on.
[0013] A cathode and an anode for use in fuel cells are generally fabricated by impregnating a metallic catalyst made of platinum (Pt), a platinum-ruthenium (Ru) alloy, or other active metal alloys, in a carbon mediated support. In particular, since precious metals, e.g., platinum, are expensive and easily poisoned by trace amounts of carbon monoxide, the cathode and anode using a precious metal catalyst are costly and have a short lifespan.
[0018] The present invention provides a nanoporous tungsten carbide catalyst having high electrochemical activity and enhanced resistance to poisoning by carbon monoxide and capable of forming more stabilized single phase crystals, thereby exhibiting high electrochemical activity using a small amount of a supported metal active component.

Problems solved by technology

In particular, since precious metals, e.g., platinum, are expensive and easily poisoned by trace amounts of carbon monoxide, the cathode and anode using a precious metal catalyst are costly and have a short lifespan.
In addition, precious metal catalysts used in electrodes of fuel cells are very expensive and leave no room for price competitiveness even if mass produced.
Accordingly, the challenges are the development of cost-effective active materials as substitutes for precious metal catalysts or maximized utilization of a precious metal used as a catalyst through maximization of an effective surface area of the precious metal.
Unfortunately, tungsten carbide electrocatalysts, in spite of their high tolerance to poisoning from CO, do not exhibit an acceptable level of electrochemical activity without the additional presence of an expensive co-catalyst.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nanoporous tungsten carbide catalyst and preparation method thereof
  • Nanoporous tungsten carbide catalyst and preparation method thereof
  • Nanoporous tungsten carbide catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0073] To prepare an aqueous solution, cetyltrimethylammonium bromide (CTABr) as a surfactant was dissolved in water. In addition, 5 g of ammonium meta tungstate was dissolved in water, and then the solution was transferred to a mixed solution of 1.2 g of resorcinol and 1.8 mL formaldehyde while being stirred to provide homogenous dispersion.

[0074] The resultant solution was loaded in a high-pressure reactor, followed by being subjected to hydrothermal synthesis at 150° C. for 2 days, giving a reaction solid. The reaction solid was filtered and dried at 110° C. for one day. The dried reaction product was heated in an inert gas atmosphere at 900° C. for one hour and then further heated in a hydrogen atmosphere for 2 hours, thereby preparing a tungsten carbide catalyst.

[0075] X-ray diffraction (XRD) analysis of the thus prepared tungsten carbide catalyst was carried out using a transmission electron microscope (TEM) manufactured by Philips (CM-200 model) operated at 200 kV. As shown...

example 2

[0080] 0.29 g of NaOH was dissolved in 25 mL distilled water, 0.64 g of NaBH4 was further dissolved in the solution, and 0.6 g of the porous tungsten carbide catalyst prepared in Example 1 was added to the resultant solution, then the solution was stirred well to provide good dispersion. Thereafter, 1 mL of H2PtCl6 was further added to the resultant dispersion and stirred for about 30 minutes, then the solution was centrifuged and dried, thereby preparing a 7.5% platinum (Pt)-tungsten carbide catalyst.

[0081] The prepared Pt / tungsten carbide catalyst was evaluated by nitrogen adsorption / desorption isotherms, high resolution transmission electron microscopy (HRTEM), and selected area electron diffraction (SAED) analysis.

[0082] The analyzed results showed that the Pt-supported catalyst was substantially the same as the tungsten carbide catalyst prepared in Example 1.

example 3

[0083] A Pt / tungsten carbide catalyst was prepared using the same method as in Example 2, except that 0.47 mL, instead of 1 mL, of H2PtCl6 was added to the solution.

[0084]FIG. 5 is a high resolution transmission electron microscopy (HRTEM) image of the nanoporous Pt / tungsten carbide catalyst prepared in Example 3 according to an embodiment of the present invention. As shown in FIG. 5, Pt particles supported on the nanoporous Pt / tungsten carbide catalyst are well dispersed therein, and the average particle size thereof is about 2 nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Temperatureaaaaaaaaaa
Temperatureaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

Provided are a nanoporous tungsten carbide catalyst that can be used as an electrode of a fuel cell and a preparation method thereof. The nanoporous tungsten carbide catalyst includes tungsten carbide crystalline particles and has nanopores of a mean pore diameter ranging from 2 nm to 5 nm and a nanopore volume of 0.08 to 0.25 cm3 per gram of the catalyst. The nanoporous tungsten carbide catalyst or the nanoporous tungsten carbide catalyst supported with a metallic active component has high electrochemical activity and enhanced resistance to poisoning by carbon monoxide (CO). Therefore, even after use for an extended period of time, the nanoporous tungsten carbide catalyst of the present invention can maintain a long-term high catalytic activity. In addition, since the nanoporous tungsten carbide catalyst of the present invention has small pore sizes and a large pore volume, which are advantageous for dispersing metallic active components, much higher catalytic activity can be demonstrated only with a small amount of the metallic active component. Accordingly, an electrode for use in a fuel cell and a fuel cell employing the electrode can be fabricated in a cost-effective manner, compared to the prior art in which a considerable amount of expensive, precious metal catalysts are used.

Description

BRIEF DESCRIPTION OF THE DRAWINGS[0001]FIG. 1 is a graph showing results of X-ray diffraction on a nanoporous tungsten carbide catalyst prepared in Example 1. [0002]FIG. 2 is a graph depicting the percentage of porosity of the nanoporous tungsten carbide catalyst prepared in Example 1, determined by nitrogen adsorption / desorption isotherms. [0003]FIG. 3 is a high resolution transmission electron microscopy (HRTEM) image of the nanoporous tungsten carbide catalyst prepared in Example 1. [0004]FIG. 4 is a selected area electron diffraction (SAED) image of the nanoporous tungsten carbide catalyst prepared in Example 1. [0005]FIG. 5 is a high resolution transmission electron microscopy (HRTEM) image of a nanoporous tungsten carbide catalyst prepared in Example 3. [0006]FIG. 6 is a graph showing results of a cyclic voltammetry (CV) test on the nanoporous tungsten carbide catalyst prepared in Example 3 and catalysts prepared in Comparative Examples 2 and 3.DETAILED DESCRIPTION OF THE INVE...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J27/22H01M4/88C01B32/949
CPCB01J27/22H01M4/90H01M4/92Y02E60/523H01M8/086H01M8/1009H01M4/925Y02E60/50Y02P70/50C01B32/949B82Y30/00B01J35/60
Inventor LEE, JAE SUNGJUNG, MOOYOUNGRAMAN, GANESANKIM, YOUNGKWON
Owner POSTECH ACAD IND FOUND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products