Nd-Fe-B rare earth permanent magnet material

一种稀土永磁、永磁材料的技术，应用在磁性材料、磁性物体、电气元件等方向，能够解决不可接受、矫顽力下降等问题，达到宽烧结温度范围、好磁性能的效果

Active Publication Date: 2006-08-16
SHIN ETSU CHEM CO LTD
View PDF2 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] It is known that the coercive force of currently commercially manufactured Nd-based sintered magnets begins to decrease when the carbon concentration exceeds about 0.05%, and is commercially unacceptable above about 0.1%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Starting materials: neodymium, praseodymium, electrolytic iron, cobalt, iron-boron alloys, aluminum, copper and titanium formulated as 28.9Nd-2.5Pr-balance Fe-4.5Co-1.2B-0.7Al-0.4Cu by weight - a composition of xTi (where x = 0, 0.04, 0.4 or 1.4), followed by the preparation of the corresponding alloys by a single roll quenching process. Then put these alloys at +1.5±0.3kgf / cm 2 Hydrogenation in a hydrogen atmosphere, at a maximum of 10 -2 Dehydrogenation was carried out at 800° C. for 3 hours under Torr vacuum. Each alloy after hydrogenation and dehydrogenation is in the form of a coarse powder with a particle size of several hundreds of micrometers. Each of the coarse powders was mixed with 0.1 wt % stearic acid as a lubricant in a V-blender, and pulverized in a jet mill under nitrogen flow to an average particle size of about 3 μm. The resulting fine powder was filled into a die, oriented in a magnetic field of 25 kOe, and 0.5 metric tons / cm 2 compacted under pre...

Embodiment 2

[0053] Starting materials: relatively high carbon concentrations of neodymium, dysprosium, electrolytic iron, cobalt, iron-boron alloys, aluminum, copper and titanium formulated to be 28.6Nd-2.5Dy-balance by weight Fe-9.0Co-1.0B- The composition of 0.8Al-0.6Cu-xTi (where x=0.01, 0.2, 0.6 or 1.5) was used to compare the effects of different titanium additions, and then an ingot of the corresponding composition was prepared by high-frequency melting and casting into a water-cooled copper mold. The ingots were crushed in a Brown mill. Each coarse powder thus obtained was mixed with 0.05% by weight of lauric acid as a lubricant in a V-blender, and pulverized in a jet mill under nitrogen flow to an average particle size of about 5 μm. The resulting fine powder was filled into a die, oriented in a magnetic field of 15 kOe, and subjected to a pressure of 1.2 metric tons / cm applied perpendicular to the magnetic field. 2 compacted under pressure. The powder compacts thus obtained are...

Embodiment 3

[0059]The starting materials used are neodymium, terbium, electrolytic iron, cobalt, iron-boron alloys, aluminium, copper and titanium with relatively high carbon concentrations. For the dual alloy method, the master alloy is formulated to be composed by weight of 27.3Nd-balance Fe-0.5Co-1.0B-0.4Al-0.2Cu, and the auxiliary alloy is formulated to be composed by weight of 46.2Nd-17.0Tb- The balance is Fe-18.9Co-xTi (where x=0.2, 4.0, 9.8 or 25). The final composition after mixing is 29.2Nd-1.7Tb-balance Fe-2.3Co-0.9B-0.4Al-0.2Cu-xTi (where x=0.01, 0.2, 0.5 or 1.3) in weight ratio. Prepare master alloy by single roll quenching process, then at +0.5~+2.0kgf / cm 2 hydrogenated in a hydrogen atmosphere, and at a maximum of 10 -2 The half-dehydrogenation was carried out at 500° C. for 3 hours under Torr vacuum. The auxiliary alloy is made into an ingot by high-frequency melting and casting into a water-cooled copper mold.

[0060] Next, 90wt% master alloy and 10wt% auxiliary alloy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A rare earth permanent magnet material is based on an R-Fe-Co-B-Al-Cu system wherein R is at least one element selected from Nd, Pr, Dy, Tb, and Ho, 15 to 33% by weight of Nd being contained. At least two compounds selected from M-B, M-B-Cu and M-C compounds (wherein M is Ti, Zr or Hf) and an R oxide have precipitated within the alloy structure as grains having an average grain size of up to 5 mum which are uniformly distributed in the alloy structure at intervals of up to 50 mum.

Description

technical field [0001] The invention relates to a Nd-Fe-B based rare earth permanent magnet material. Background technique [0002] Rare earth permanent magnets are commonly used in electrical and electronic devices due to their excellent magnetic properties and economy. Recently, demands for improving their performance continue to increase. [0003] In order to improve the magnetic properties of R-Fe-B based rare earth permanent magnets, it is necessary to increase the R that exists as the main phase component in the alloy 2 Fe 14 B 1 phase ratio. This means reducing the Nd-rich phase which is a non-magnetic phase. This in turn requires reducing the concentration of oxygen, carbon and nitrogen in the alloy to minimize oxidation, carburization and nitriding of the Nd-rich phase. [0004] However, reducing the oxygen concentration in the alloy creates the possibility of anomalous grain growth during sintering, resulting in high remanence Br, but...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/057C22C38/00
CPCH01F1/0577C22C38/002C22C38/005C22C38/06C22C38/10C22C38/14C22C38/16H01F1/058
Inventor 山本健治广田晃一美浓轮武久
Owner SHIN ETSU CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com