A kind of high specific strength, specific rigidity aluminum-lithium alloy thick-walled annular part and preparation method thereof

An aluminum-lithium alloy, high specific strength technology, used in metal processing equipment, manufacturing tools, casting and molding equipment, etc., can solve problems such as insufficient specific strength, specific stiffness, low density, and inability to meet weight reduction requirements, and achieve good strength. , low density, energy saving effect

Active Publication Date: 2022-04-08
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF18 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem to be solved by the present invention is that the ordinary aluminum alloy ring parts traditionally used in centrifugal casting have low density (density greater than 2.7 g / cm 3 ), and the specific strength and specific stiffness are not enough to meet the growing demand for weight reduction, providing a high specific strength, specific stiffness aluminum-lithium alloy thick-walled ring and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high specific strength, specific rigidity aluminum-lithium alloy thick-walled annular part and preparation method thereof
  • A kind of high specific strength, specific rigidity aluminum-lithium alloy thick-walled annular part and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0055] In a second aspect, the present invention provides a method for preparing the aluminum-lithium alloy thick-walled annular member described in the first aspect, comprising:

[0056] S1. Prepare raw materials according to requirements, and optionally preheat the raw materials;

[0057] S2. Smelting and refining the raw materials obtained in S1;

[0058] S3. Centrifugally casting and cooling the material obtained in S2 to obtain a ring casting;

[0059] S4, performing heat treatment on the annular casting obtained in S3, the heat treatment process includes: first performing solution treatment under an inert atmosphere, then performing quenching treatment, then performing aging treatment under an inert atmosphere, and then performing optional cooling;

[0060] Wherein, boron nitride coatings are respectively provided on the surfaces of all devices that are in contact with molten metal after raw materials are melted.

[0061] All the devices that come into contact with the...

Embodiment 1

[0089] A thick-walled aluminum-lithium alloy ring with high specific strength and specific stiffness, its chemical composition is: Cu1.4wt%, Li 3.0wt%, Mg 1.2wt%, Zn 0.6wt%, Er 0.1wt%, Zr 0.1wt%, Fe≤0.08wt%, Si≤0.05wt%, the balance is Al and unavoidable impurities.

[0090] Its microstructure is fine equiaxed dendrite, the grain size is 70μm, the internal structure of the alloy is dense, and the dendrite segregation is significantly weakened. The size of the aluminum-lithium alloy thick-walled ring is: the height is 400mm, the outer diameter is 380mm, the wall thickness is 80mm, and the mold size is as follows figure 1 shown. The performance of the high specific strength aluminum alloy ring is: the density is 2.47g / cm 3 , the tensile strength is 450MPa, the elongation is 6.3%, the elastic modulus is 81GPa, and the specific strength is 182MPa / (g / cm 3 ), the specific stiffness is 32.8GPa / (g / cm 3 ).

[0091] The integrated preparation method of the aluminum-lithium alloy thi...

Embodiment 2

[0110] A high specific strength, specific stiffness aluminum-lithium alloy thick-walled ring, the chemical composition of the high specific strength aluminum alloy is: Cu 2.5wt%, Li 3.5wt%, Mg 1.3wt%, Zn 0.7wt% , Er 0.2wt%, Zr 0.2wt%, Fe≤0.08wt%, Si≤0.05wt%, and the total amount of alloying elements does not exceed 8.5wt%, and the balance is Al and unavoidable impurities.

[0111] Its microstructure is fine equiaxed dendrite, the grain size is 40μm, the internal structure of the alloy is dense, and the dendrite segregation is significantly weakened. Its dimensions are: the height is 400mm, the outer diameter is 400mm, the wall thickness is 100mm, and the mold size is as follows figure 2 shown. The performance of the aluminum-lithium alloy thick-walled annular part is: the density is 2.53g / cm 3 , the tensile strength is 550MPa, the elongation is 6.1%, the elastic modulus is 85GPa, and the specific strength is 217MPa / (g / cm 3 ), specific stiffness 33.6GPa / (g / cm 3 ).

[0112...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
heightaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides an aluminum-lithium alloy thick-walled ring with high specific strength and specific stiffness and a preparation method thereof, which belongs to the field of new aluminum-lithium alloy materials and manufacturing technology, and comprises the following chemical composition: Cu 0.8-2.8wt%, Li 2.4- 3.8wt%, Mg 0.8‑1.8wt%, Zn 0.5‑1.5wt%, Er 0.1‑0.5wt%, Zr 0.05‑0.2wt%, Fe≤0.08wt%, Si≤0.05wt%, and the total amount of alloying elements is not More than 8.5wt%, the balance is Al and unavoidable impurities. The preparation method includes: alloy batching, boron nitride coating, melting, refining, centrifugal casting and heat treatment. The invention can simplify the forming process of the aluminum alloy ring, has a compact internal structure, and significantly improves the specific strength and specific rigidity of the aluminum alloy ring.

Description

technical field [0001] The invention relates to the field of new aluminum-lithium alloy materials and manufacturing technology, in particular to an aluminum-lithium alloy thick-walled annular part with high specific strength and specific stiffness and a preparation method thereof. Background technique [0002] Metal ring materials can be used as key connection, transmission, slewing and supporting components in the fields of major mechanical equipment, pressure vessels, and aerospace equipment manufacturing. Since aluminum-lithium alloy has a wide service temperature range, good casting performance and mechanical properties, and the density of the current lightweight aluminum-lithium alloy is only 1 / 3 of that of traditional steel materials, it is in the face of the global energy crisis and environmental degradation. In the background, exploring the use of aluminum-lithium alloy annular structural parts to replace traditional steel materials has broad industrial application p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C21/18C22C1/03C22C1/06C22F1/04C22F1/057C22F1/02B22D13/04B22C3/00B22D13/10
CPCC22C21/00C22C21/18C22C21/16C22C21/14C22C1/026C22C1/03C22C1/06C22F1/04C22F1/057C22F1/002C22F1/02B22D13/04B22C3/00B22D13/10
Inventor 王俊升杨兴海田光元薛程鹏王硕张宇轩
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com