Lead-free piezoelectric ceramic material for breathing machine and preparation method of lead-free piezoelectric ceramic material

A technology of lead-free piezoelectric and ceramic materials, applied in the field of electronic ceramic materials, can solve the problems of nervous system poisoning, PZT piezoelectric ceramic stoichiometry prone to deviation, poor preparation stability, etc., achieve good electrical performance and improve preparation stability , High density effect

Active Publication Date: 2021-11-02
HUNAN MEICHENG CERAMIC TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the PZT piezoelectric ceramic system has excellent piezoelectricity, thermal stability and mature applications, the main raw material PbO for the preparation of PZT ceramics is highly toxic, and it will volatilize during high-temperature sintering, and trace amounts of PbO in the air will Seriously harmful to the nervous system of humans and animals, the lead content in PZT ceramics is as high as 60wt%, which will bring huge environmental pressure from preparation to recycling, and due to the high-temperature volatilization characteristics of PbO, the stoichiometry of PZT piezoelectric ceramics The ratio is prone to deviation and the preparation stability is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lead-free piezoelectric ceramic material for breathing machine and preparation method of lead-free piezoelectric ceramic material
  • Lead-free piezoelectric ceramic material for breathing machine and preparation method of lead-free piezoelectric ceramic material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A lead-free piezoelectric ceramic material for ventilator, represented by the following chemical formula: 0.65 (Bi 0.50 Na 0.50 )TiO 3 -0.25LiNbO 3 -0.10 (Bi 0.75 K 0.25 )HfO 3 -0.15%La 2 O 3 -0.05% LiBiO 2

[0036] Its preparation method is as follows:

[0037] will Bi 2 O 3 , TiO 2, Na 2 CO 3 , The molten salt is weighed and proportioned, the molten salt is composed of NaCl and KCl according to the mass ratio of 1:1, and the amount of molten salt is Bi 2 O 3 , TiO 2 , Na 2 CO 3 3 times the total mass, use anhydrous ethanol as the ball milling medium, dry the ball for 15 hours once, pre-burn at 700°C for 2 hours, then use deionized water as the ball milling medium, dry the ball for 15 hours for the second time, and wash it with water until no Cl - detected, dried, obtained (Bi 0.50 Na 0.50 )TiO 3 , the Li 2 CO 3 , Nb 2 O 5 , The molten salt is weighed and proportioned, the molten salt is composed of NaCl and KCl according to the mass ratio of ...

Embodiment 2

[0039] A lead-free piezoelectric ceramic material for ventilator, represented by the following chemical formula:

[0040] 0.65(Bi 0.50 Na 0.50 )TiO 3 -0.25LiNbO 3 -0.10 (Bi 0.75 K 0.25 )HfO 3 -0.15%La 2 O 3 -0.05% LiBiO 2

[0041] Its preparation method is as follows:

[0042] will Bi 2 O 3 , TiO 2 , Na 2 CO 3 , The molten salt is weighed and proportioned, the molten salt is composed of NaCl and KCl according to the mass ratio of 1:1, and the amount of molten salt is Bi 2 O 3 , TiO 2 , Na 2 CO 3 5 times of the total mass, use absolute ethanol as the ball milling medium, dry after the first ball milling for 10 hours, pre-burn at 700 °C for 2 hours, then use deionized water as the ball milling medium, dry after the second ball milling for 10 hours, and wash with water until no Cl - detected, dried, obtained (Bi 0.50 Na 0.50 )TiO 3 , the Li 2 CO 3 , Nb 2 O 5 , The molten salt is weighed and proportioned, the molten salt is composed of NaCl and KCl accor...

Embodiment 3

[0044] A lead-free piezoelectric ceramic material for ventilator, represented by the following chemical formula:

[0045] 0.65(Bi 0.50 Na 0.50 )TiO 3 -0.25LiNbO 3 -0.10 (Bi 0.75 K 0.25 )HfO 3 -0.15%La 2 O 3 -0.05% LiBiO 2

[0046] Its preparation method is as follows:

[0047] will Bi 2 O 3 , TiO 2 , Na 2 CO 3 , The molten salt is weighed and proportioned, the molten salt is composed of NaCl and KCl according to the mass ratio of 1:1, and the amount of molten salt is Bi 2 O 3 , TiO 2 , Na 2 CO 3 10 times the total mass, use anhydrous ethanol as the ball-milling medium, dry after the first ball-milling for 15h, pre-burn at 700°C for 4h, then use deionized water as the ball-milling medium, dry the ball-milling for 15h after the second time, and wash with water until no Cl - detected, dried, obtained (Bi 0.50 Na 0.50 )TiO 3 , the Li 2 CO 3 , Nb 2 O 5 , The molten salt is weighed and proportioned, the molten salt is composed of NaCl and KCl according to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
piezoelectric charge coefficientaaaaaaaaaa
dielectric lossaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of electronic ceramic materials, and in particular, relates to a lead-free piezoelectric ceramic material for a breathing machine and a preparation method of the lead-free piezoelectric ceramic material, wherein the lead-free piezoelectric ceramic material is represented by the following chemical formula: x(Bi[a]Na[1-a])TiO[3]-yLiNbO[3]-(1-x-y)(Bi[b]K[1-b])HfO[3]-alphaLa[2]O[3]-betaLiBiO[2], x is 0.55-0.70, y is 0.10-0.25, a is 0.45-0.75, b is 0.45-0.75, alpha is 0.15-0.3%, and beta is 0.01-0.1%. The prepared piezoelectric ceramic material is high in density, the piezoelectric property of the piezoelectric ceramic material is superior to that of most of lead-free piezoelectric ceramic materials, and the piezoelectric ceramic material has wide application prospects and can be used for manufacturing piezoelectric valves for breathing machines.

Description

technical field [0001] The invention relates to the field of electronic ceramic materials, in particular to a lead-free piezoelectric ceramic material for ventilators and a preparation method thereof. Background technique [0002] The sign of patients with new coronavirus pneumonia developing into severe or critical illness is respiratory failure and hypoxia. Therefore, early detection of hypoxemia and timely use of ventilator intervention can prevent critically ill patients from becoming critically ill, and save time for the life of patients. Piezoelectric valves made of piezoelectric ceramic materials are the key components of modern ventilators. For the manufacture of ventilators, piezoelectric ceramics are indispensable. [0003] In 1952, Shirane et al. synthesized lead zirconate titanate (PZT), which is considered to be the most valuable piezoelectric material and has received considerable attention and research in the last century. At present, PZT is still the most e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/475C04B35/622C04B35/626
CPCC04B35/475C04B35/622C04B35/62675C04B2235/3298C04B2235/3232C04B2235/3201C04B2235/3203C04B2235/3227C04B2235/3244C04B2235/602C04B2235/656C04B2235/6562C04B2235/6567C04B2235/77
Inventor 方豪杰贺亦文张晓云张斗袁晰
Owner HUNAN MEICHENG CERAMIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com