High-strength creep-resistant polyester industrial yarn and preparation method thereof

A technology of polyester industrial yarn and creep resistance, applied in the field of spinning, can solve problems such as traffic accidents, elongation and deformation of tire frame, etc., and achieve the effects of reducing creep degree, increasing elastic modulus, and good mechanical properties

Active Publication Date: 2021-05-04
JIANGSU HENGLI CHEM FIBER
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As one of the cord materials, polyester industrial yarn has a close relationship between its creep phenomenon and its performance. If the creep degree is large, it will cause the elongation and deformation of the tire frame, which will lead to traffic accidents.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength creep-resistant polyester industrial yarn and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A preparation method of high-strength creep-resistant polyester industrial yarn, the specific steps are as follows:

[0055] (1) preparation of modified polyester;

[0056] (1.1) Esterification reaction;

[0057] Make a slurry of terephthalic acid, ethylene glycol and 2-(4-pyridine) terephthalic acid with a molar ratio of 1:1.2:0.03, add catalyst (antimony trioxide) and stabilizer (triphenyl phosphate ) are mixed evenly, the addition of catalyst and stabilizer is respectively 0.01wt% and 0.03wt% of the addition of terephthalic acid, and pressurizes in nitrogen atmosphere to carry out esterification reaction, pressurized pressure is 0.2MPa, esterification reaction The temperature is 259°C, when the amount of water distilled out in the esterification reaction reaches 96% of the theoretical value, it is the end point of the esterification reaction;

[0058] (1.2) polycondensation reaction;

[0059] After the esterification reaction is over, start the polycondensation re...

Embodiment 2

[0076] A preparation method of high-strength creep-resistant polyester industrial yarn, the specific steps are as follows:

[0077] (1) preparation of modified polyester;

[0078] (1.1) Esterification reaction;

[0079] Make a slurry of terephthalic acid, ethylene glycol and 2-(4-pyridine) terephthalic acid with a molar ratio of 1:1.5:0.03, add catalyst (antimony trioxide) and stabilizer (triphenyl phosphate ) are mixed evenly, the addition of catalyst and stabilizer is respectively 0.01wt% and 0.04wt% of the addition of terephthalic acid, and then pressurized in nitrogen atmosphere to carry out esterification reaction, pressurized pressure is 0.2MPa, esterification reaction The temperature is 260°C, when the amount of water distilled in the esterification reaction reaches 96% of the theoretical value, it is the end of the esterification reaction;

[0080] (1.2) polycondensation reaction;

[0081] After the esterification reaction is over, start the polycondensation reactio...

Embodiment 3

[0098] A preparation method of high-strength creep-resistant polyester industrial yarn, the specific steps are as follows:

[0099] (1) preparation of modified polyester;

[0100] (1.1) Esterification reaction;

[0101] Make a slurry of terephthalic acid, ethylene glycol and 2-(4-pyridine) terephthalic acid with a molar ratio of 1:2.0:0.03, add catalyst (antimony trioxide) and stabilizer (trimethyl phosphate ) mixed uniformly, the addition of catalyst and stabilizer is respectively 0.02wt% and 0.05wt% of the addition of terephthalic acid, and then pressurized in a nitrogen atmosphere to carry out esterification reaction, pressurized pressure is 0.3MPa, esterification reaction The temperature is 254°C, when the amount of water distilled in the esterification reaction reaches 95% of the theoretical value, it is the end point of the esterification reaction;

[0102] (1.2) polycondensation reaction;

[0103] After the esterification reaction is over, start the polycondensation re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-strength creep-resistant polyester industrial yarn and a preparation method thereof. The preparation method comprises the following steps of carrying out solid phase polycondensation and tackifying on modified polyester, and then carrying out spinning winding and coordination treatment to obtain the high-strength creep-resistant polyester industrial yarn, wherein the coordination treatment is performed at 80-100 DEG C for 60-72 hours; a coordination agent is AgNO3, FeCl2, CuCl2 or NiCl2; a polyester chain segment of the prepared high-strength creep-resistant polyester industrial yarn comprises a terephthalic acid chain segment, an oxalic acid chain segment and a 2-(4-pyridine) terephthalic acid chain segment, and the 2-(4-pyridine) terephthalic acid chain segments of different polyester chain segments are coordinated through metal ions (Ag<+>, Fe<2+>, Cu<2+> or Ni<2+>); the molar ratio of the terephthalic acid chain segment to the 2-(4-pyridine) terephthalic acid chain segment is 1: (0.03-0.05); and an N atom on pyridine of the 2-(4-pyridine) terephthalic acid chain segment participates in coordination. According to the invention, the metal ions and 2-(4-pyridine) terephthalic acid are coordinated, so that the creep degree of polyester fiber is greatly reduced.

Description

technical field [0001] The invention belongs to the technical field of spinning, and relates to a high-strength creep-resistant polyester industrial yarn and a preparation method thereof. Background technique [0002] Polyester industrial yarn has excellent physical and mechanical properties such as high strength, high modulus, low elongation, impact resistance, fatigue resistance, good heat resistance, and the elongation value in wet state is basically the same as that in dry state. As one of the four major contemporary rubber skeleton materials (viscose, nylon, polyester, and steel wire), it has broad application prospects in vehicle tires, conveyor belts, conveyor belts, safety belts, and water hoses. [0003] Under the action of constant temperature and constant stress, the deformation of polymer gradually increases with time, which is called creep. Creep is one of the main problems existing in organic fibers, and creep damage is also an urgent problem that needs to be ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/84C08G63/685C08G63/78
CPCD01F6/84C08G63/6856C08G63/78Y02P70/62C08G63/183C08G63/85D06M11/13D06M11/28D06M11/83D01D5/16D02G3/02D10B2331/04D10B2401/062D10B2401/063
Inventor 汤方明王山水王丽丽张烨魏存宏张玉梅赵艳丽
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com