ASA/PC 3D printing wire rod with low VOC release and preparation method thereof

A technology for printing wire rods and ASA resins, applied in the direction of additive processing, etc., can solve the problems of ASA/PC materials that have not been reported in the application, and do not involve the amount of VOC release, so as to reduce the source of VOC release, smooth printing performance and stable size The effect of good sex and smell

Pending Publication Date: 2021-03-23
LIMING VOCATIONAL UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In addition, there are no reports on the application of ASA / PC materials in 3D printing molding, let alone reports on the amount of VOC released during the molding process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ASA/PC 3D printing wire rod with low VOC release and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A low-VOC release ASA / PC 3D printing wire, the components are calculated by weight percentage: ASA 50%, PC 30%, modified porous calcium silicate 15%, monobutyltin oxide 0.5%, zinc stearate 2 %, antioxidant 1010 {tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester} 0.5% and paraffin wax 2%.

[0034] A preparation method for ASA / PC 3D printing filaments released by low VOC, comprising the following steps:

[0035] (1) Preparation steps of modified porous calcium silicate:

[0036] A. Put 25g of porous calcium silicate into 1L of deionized water for ultrasonic dispersion for 1h, and add 8ml of acetic acid under stirring;

[0037] B. Then add 2g of chitosan, react at room temperature for 2h, then filter, wash until neutral and dry to obtain modified porous calcium silicate.

[0038] (2) ASA, PC, modified porous calcium silicate, monobutyl tin oxide, zinc stearate, and antioxidant 1010 were vacuum-dried respectively, and the dried components an...

Embodiment 2

[0046] A low VOC release ASA / PC 3D printing wire, the components are calculated by weight percentage: ASA 53%, PC 28%, modified porous calcium silicate 14%, tributyltin chloride 0.3%, calcium stearate 2%, antioxidant CA[1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane] 0.7% and silicone oil 2%.

[0047] A preparation method for ASA / PC 3D printing filaments released by low VOC, comprising the following steps:

[0048] (1) Preparation steps of modified porous calcium silicate:

[0049] A. Put 35g of porous calcium silicate into 1L of deionized water for ultrasonic dispersion for 0.5h, and add 10ml of acetic acid under stirring;

[0050] B. Then add 5g of chitosan, react at room temperature for 3h, then filter, wash to neutral and dry to obtain modified porous calcium silicate.

[0051] (2) ASA, PC, modified porous calcium silicate, tributyltin chloride, calcium stearate and antioxidant CA are vacuum-dried respectively, and the components and silicone oil after drying ar...

Embodiment 3

[0055] A low VOC release ASA / PC 3D printing wire, the components are calculated by weight percentage: ASA 63%, PC 21%, modified porous calcium silicate 12%, butyl tin trichloride 0.6%, magnesium stearate 1.3%, antioxidant DNP [N,N'-di(β-naphthyl)-p-phenylenediamine)] 0.6% and stearic acid 1.5%.

[0056] A preparation method for ASA / PC 3D printing filaments released by low VOC, comprising the following steps:

[0057] (1) Preparation steps of modified porous calcium silicate:

[0058] A. Put 20g of porous calcium silicate into 1L of deionized water for ultrasonic dispersion for 2 hours, and add 5ml of acetic acid under stirring;

[0059] B. Then add 1.5g of chitosan, react at room temperature for 2h, then filter, wash until neutral and dry to obtain modified porous calcium silicate.

[0060] (2) ASA, PC, modified porous calcium silicate, butyl tin trichloride, magnesium stearate and antioxidant DNP are vacuum-dried respectively, and each component after drying and stearic aci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ASA / PC 3D printing wire rod with low VOC release, which takes ASA / PC resin as a raw material, is added with modified porous calcium silicate, an accelerant, a heat stabilizer, an antioxidant and a lubricant, and has the advantages of good forming property and mechanical property, wide application field and high application value. Besides, the invention further disclosesa preparation method of the 3D printing wire rod, the prepared ASA / PC 3D printing wire rod is small in VOC release amount in the 3D printing forming process and good in smell in the forming process, and the greenization of the 3D printing forming process is effectively achieved.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an ASA / PC 3D printing wire with low VOC release and a preparation method thereof. Background technique [0002] 3D printing is a new manufacturing technology that integrates the disciplines of machinery, software and materials. It is based on the principle of material accumulation and forming, and is widely used in engineering, education, medical and other fields. As one of the mainstream technologies of 3D printing, fused deposition modeling has attracted people's attention due to its low cost, safe operation and simple post-processing. [0003] ASA resin is a ternary block copolymer composed of acrylonitrile, styrene and acrylate. The material not only has superior processability, mechanical properties and chemical corrosion resistance, but also has good weather resistance. PC resin has good mechanical properties, heat resistance and stability. It is an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L51/04C08L69/00C08K13/06C08K9/04C08K7/26C08K5/098C08K5/57B33Y70/10
CPCC08L51/04B33Y70/10C08L2201/08C08L2205/03C08L69/00C08K13/06C08K9/08C08K7/26C08K5/098C08K5/57
Inventor 林鸿裕焦荃鹏林少芬汤榕彬
Owner LIMING VOCATIONAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com