Preparation method of titanium alloy seamless pipe

A seamless pipe and titanium alloy technology, applied in the field of titanium alloy seamless pipe preparation, can solve the problems of uneven deformation, inconsistent deformation of pipe inner and outer diameters, large consumption of metal and tools, etc., to achieve high uniformity of structure, The effect of shortening the production cycle and reducing the cost of electricity consumption

Inactive Publication Date: 2021-03-05
湖南湘投金天科技集团有限责任公司 +1
View PDF12 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Cross rolling piercing + hot continuous rolling process can realize piercing and forming at one time, low cost, relatively small consumption of titanium metal and tools, but high deformation temperature, severe deformation, difficult to control surface quality and material structure properties; at the same time, thermal tension The use of mandrelless empty rolling for diameter reduction will cause the inner surface of the seamless pipe to be polygonal, the outer surface is damaged and the inner surface is not round, so that the hot-rolled seamless pipe needs a large amount of surface grinding before delivery to meet the use requirements and dimensional accuracy
The extrusion process is used to prepare seamless pipes. Due to the drilling of the round bar billet and the extrusion process, the consumption of metal and tools will increase, which will increase the production cost of titanium alloy seamless pipes. Due to the extrusion lubrication problem, the inside and outside of the pipe The surface is prone to uneven deformation such as scratches, bulging, and pits; at the same time, the deformation of the inner and outer diameters of the pipe is inconsistent, and there is a deviation in the grain size. The size is limited by the extrusion die, and the inner and outer diameters cannot be adjusted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] The invention provides a method for preparing a titanium alloy seamless pipe, comprising the following steps:

[0049] Step 1: Smelting titanium sponge and intermediate alloys to obtain titanium alloy ingots;

[0050] Step 2: heating the titanium alloy ingot obtained by smelting, and performing drawing and forging to obtain a titanium alloy billet;

[0051] Step 3: Punch through holes on the titanium alloy bar to obtain a titanium alloy hollow bar blank;

[0052]Step 4: coating the surface of the heated titanium alloy billet with a lubricant, and then extruding the titanium alloy to obtain a titanium alloy extruded tube billet;

[0053] Step 5: Carry out one-time precision forging on the titanium alloy extruded tube blank to obtain the finished tube blank;

[0054] Step 6: Carry out heat treatment on the precision forged finished tube blank, and perform straightening and machining after the heat treatment to obtain a large-diameter titanium alloy seamless tube.

Embodiment 1

[0056] Taking the production of TC4 seamless pipes with an outer diameter of φ600mm and an inner diameter of φ540mm as an example, the preparation method is as follows:

[0057] Step 1: Vacuum smelting to obtain an ingot of φ780mm;

[0058] Step 2: After the outer surface is machined and peeled off, a round ingot of φ760 is obtained;

[0059] Step 3: Above the phase transition point of the titanium alloy (T β +20~T β +50℃) and below the transformation point of titanium alloy (T β -50~T β -20°C) staggered multi-fire upsetting to obtain a φ1000mm titanium alloy billet;

[0060] Step 4: Punch through the titanium alloy bar, and obtain a titanium alloy hollow bar blank with an outer diameter of φ950mm and a central hole diameter of φ385mm after boring, and the surface roughness of the central hole of the blank is not higher than 6.3 microns;

[0061] Step 5: Tβ+50℃ electric furnace heating, heating time 240min;

[0062] Step 6: Take it out of the oven, sprinkle glass powder ...

Embodiment 2

[0067] Taking the production of TC11 seamless pipes with an outer diameter of φ480mm and an inner diameter of φ430mm as an example, the preparation method is as follows:

[0068] Step 1: Vacuum smelting to obtain an ingot of φ780mm;

[0069] Step 2: After the outer surface is machined and peeled off, a round ingot of φ760 is obtained;

[0070] Step 3: Above the phase transition point of the titanium alloy (T β +20~T β +50℃) and below the transformation point of titanium alloy (T β -50~T β -20°C) staggered multi-fire upsetting to obtain a φ900mm titanium alloy billet;

[0071] Step 4: Punch through the titanium alloy bar, and obtain a titanium alloy hollow bar blank with an outer diameter of φ870mm and a central hole diameter of φ385mm after boring, and the surface roughness of the central hole of the blank is not higher than 6.3 microns;

[0072] Step Five: T β +50℃ electric furnace heating, heating time 240min;

[0073] Step 6: Take it out of the oven, sprinkle glass p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
surface roughnessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a titanium alloy seamless pipe. The preparation method comprises the following steps: step 1, smelting titanium sponge and intermediate alloy for multiple times to obtain a titanium alloy cast ingot; step 2, heating the titanium alloy cast ingot obtained by smelting, carrying out drawing forging, and carrying out multi-heating-number upsetting and drawing above the transformation temperature of the titanium alloy and below the transformation temperature of the titanium alloy in a staggered manner to obtain a titanium alloy bar blank; step 3, punching a through hole in a titanium alloy bar, and performing boring to obtain a titanium alloy hollow bar blank; step 4, coating the inner surface and the outer surface of the heated titanium alloy hollow rod blank with lubricating agent, and then extruding the titanium alloy hollow rod blank to obtain a titanium alloy extruded pipe blank; step 5, performing one-time forming precision forging on thetitanium alloy extruded pipe blank to obtain a precision forging finished pipe blank; and step 6, conducting straightening and machining after overall heat treatment to obtain the titanium alloy seamless pipe. The titanium alloy seamless pipe manufactured by the preparation method has the advantages of being adjustable in pipe outer diameter and shape, high in size precision, high in structural uniformity and the like.

Description

technical field [0001] The invention relates to the technical field of titanium alloy production, and in particular to a method for preparing a titanium alloy seamless pipe with high structural uniformity by means of extrusion combined with precision forging. Background technique [0002] With the application of titanium and titanium alloys, the demand for titanium and titanium alloy seamless pipes currently used in ships, marine engineering, and marine exploration instruments has increased. The titanium alloy seamless pipes are mainly used in their working conditions. Equipment or components in harsh environments, such as the shell of an oil field logging instrument that needs to be placed thousands of meters underwater, must withstand high pressure, and must also withstand seawater and marine biological corrosion; Shells of deep ocean exploration instruments, pipelines with high pressure and corrosive media, etc. [0003] In the prior art, the manufacture of titanium allo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/06C22C1/03C22C14/00C22F1/18
CPCB21C37/06C22C1/03C22C14/00C22F1/183
Inventor 杨胜孙冬柏周慧俞宏英杨锐雷家峰欧阳涛
Owner 湖南湘投金天科技集团有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products