Multifunctional biomass composite building material and preparation method

A composite building material and biomass technology, which is applied in the field of multifunctional biomass composite building materials and its preparation, can solve the problem of weak durability stress reduction of reinforced glass fiber mesh cloth, inability to bear the load stress of public buildings, and the cost and price of epoxy resin Problems such as staying high

Inactive Publication Date: 2021-03-02
海南好城新型建材科技有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The Chinese patent with the patent number 200510100940.9 discloses a silicon-magnesium fiber energy-saving high-strength composite material and its method for manufacturing decoration-free building boards. Regarding the technology disclosed in the above-mentioned patent, there are the following problems: 1. The published product technology formula material magnesium chloride Containing an uncertain amount of chlorine ions may have the disadvantages of brine, frost and deformation on building panels; 2. The announced product reinforcement material glass fiber mesh has weak durability stress and decline, and cannot bear the large load stress of public buildings; 3. Germs are indoors Survive in the air for about 2 to 2 hours, survive on copper surface walls for 3 hours, and survive on stainless steel, plastic, cloth, and paper walls for 3-6 days
Science has revealed that the surface of copper is alkaline and acidic, which can cause the survival rate of germs to be 4%. 4. In most hospitals, the walls, floors and ceilings of the buildings used are all equipped with one or two floors of shared equipment and pipeline space; 5. The disclosed technology "bamboo winding municipal pipeline" in the patent literature is made of epoxy resin composite bamboo strips, and the ambient temperature is limited to 80 degrees. The technical product is limited to municipal pipelines and does not involve building boards. The cost of epoxy resin high prices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional biomass composite building material and preparation method
  • Multifunctional biomass composite building material and preparation method
  • Multifunctional biomass composite building material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A multifunctional biomass composite building material is made of the following raw materials in parts by weight:

[0035]

[0036] Wherein, the weight of active magnesium oxide in the magnesium oxide accounts for 50% to 75% of the total weight of magnesium oxide, and the modifier is composed of phosphoric acid, stone alkali, organic silicon compound, methyl / butyl acrylate and mica powder, And the weight ratio among them is 0.05˜1:1˜5:1˜5:1˜5:2˜12.

[0037] It should be noted that in the process of preparing the above-mentioned building boards, water is needed, and the amount of water is not required too much. It only needs to make the solid substances fully moisten and swell and stir to form a paddle. .

[0038] In the process of implementing the present invention, the above-mentioned activated magnesium oxide refers to the active ingredient magnesium oxide that can directly participate in the mutual reaction of materials. The overall reaction is an exothermic react...

Embodiment 2

[0056] A preparation method for preparing the above-mentioned multifunctional biomass composite building material, comprising the steps of:

[0057] 1) Prepare materials according to the above parts by weight, and pulverize the solid raw materials into micropowder particles above 100 mesh;

[0058] 2) Place the magnesium sulfate heptahydrate and the modifier in the slurry bin of the mixer, add water and stir to dissolve, then add magnesium oxide and filler material to the slurry bin and then fully stir to form a slurry;

[0059] 3) pouring the slurry in step 2 into the wallboard formwork, and leveling the slurry in the wallboard formwork, and then placing a plurality of raw biomass bamboos above the slurry;

[0060] 4) Obtain foam through an air compressor, inject the foam into the slurry bin and stir to obtain the adsorption raw material;

[0061] 5) pouring the adsorption raw material obtained in step 4 into the wallboard formwork, and covering the non-woven grid cloth or m...

Embodiment 3

[0070] A biomass wallboard, which is prepared from the above-mentioned multifunctional biomass composite building material according to the above-mentioned preparation method, and a core material is arranged inside the wallboard, the main component in the core material is an air-entraining agent, and the surface of the wallboard is also It has a decorative layer, which is composed of different colors of different organic materials, such as white, gray, yellow, red, blue, green, etc. in mica powder, and rice husk, wheat straw powder, mahogany powder, etc. in fiber biomass materials. Oak powder and bamboo bran have different colors, and organic matter extraction pigments such as iron dioxide red, iron green, iron yellow, etc. can also be added to color. The mixture of these different color materials can form a beautiful wall panel with bright spots on the surface. It is the decorative layer.

[0071] Preferably, there are at least two core materials, and the core material can be...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a multifunctional biomass composite building material and a preparation method, wherein the building material is prepared from the following raw materials by weight: 100 partsof magnesium oxide; 30-40 parts of magnesium sulfate heptahydrate; 40-60 parts of a modifier; and 30-50 parts of a filling material; specifically, the weight of active magnesium oxide in the magnesiumoxide accounts for 50%-75% of the total weight of the magnesium oxide, the modifier is formed by mixing phosphoric acid, soda brick, an organic silicon compound, methyl / butyl acrylate and mica powderaccording to a weight ratio of 0.05-1:1-5:1-5:1-5:2-12, and by means of the mode, at least one defect in the background technology is overcome, and energy conservation, environmental protection and good economic benefits are achieved.

Description

technical field [0001] The invention relates to the technical field of building boards, in particular to a multifunctional biomass composite building material and a preparation method thereof. Background technique [0002] The Chinese patent with the patent number 200510100940.9 discloses a silicon-magnesium fiber energy-saving high-strength composite material and its method for manufacturing decoration-free building boards. Regarding the technology disclosed in the above-mentioned patent, there are the following problems: 1. The published product technology formula material magnesium chloride Containing an uncertain amount of chlorine ions may have the disadvantages of brine, frost and deformation on building panels; 2. The announced product reinforcement material glass fiber mesh has weak durability stress and decline, and cannot bear the large load stress of public buildings; 3. Germs are indoors Survive in the air for about two to two hours, survive on copper surfaces fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/30B28B13/02B28B13/06B28B17/02B28B17/00C04B111/20C04B111/27C04B111/28C04B111/52
CPCC04B28/30B28B13/02B28B13/06B28B17/02B28B17/00C04B2111/20C04B2111/27C04B2111/28C04B2111/52C04B22/066C04B22/142C04B22/165C04B24/42C04B22/10C04B24/045C04B14/042C04B18/24C04B18/26C04B18/08C04B14/02C04B18/12C04B18/141C04B14/06
Inventor 张维善
Owner 海南好城新型建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com