Economical low-temperature steel pipe with good corrosion resistance and manufacturing method of economical low-temperature steel pipe

A corrosion-resistant and economical technology, applied in the field of low-temperature steel pipes and their manufacturing, can solve the problems of unexplained low-temperature impact performance at -60°C, unfavorable product performance stability, and a wide range of product element components, and achieve excellent low-temperature impact performance. , Improve low temperature impact performance and acid corrosion resistance, low cost effect

Inactive Publication Date: 2020-12-01
ANGANG STEEL CO LTD
View PDF12 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Invention "A Low-Temperature Seamless Steel Tube for Freezing Construction and Its Manufacturing Method" (Application No.: 201210092191.X) added alloying elements such as V to the technical solution disclosed, and did not adopt a heat treatment process. The range of elements is wide, which is not conducive to product performance Stability, and the low-temperature impact performance at -60°C is not described, and the product does not involve corrosion resistance research. The current complex use environment puts forward higher requirements for corrosion resistance
In the product development of the ASTM A333 Gr6 seamless steel pipe for low temperature service, the product is added with various alloys such as V and Mo, which has high cost and a wide range of product element components, which is not conducive to operation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Economical low-temperature steel pipe with good corrosion resistance and manufacturing method of economical low-temperature steel pipe
  • Economical low-temperature steel pipe with good corrosion resistance and manufacturing method of economical low-temperature steel pipe
  • Economical low-temperature steel pipe with good corrosion resistance and manufacturing method of economical low-temperature steel pipe

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] Below by embodiment the present invention will be further described.

[0033] According to the composition ratio of the technical proposal, the embodiments of the present invention carry out converter smelting, refining outside the furnace (LF), continuous casting of square billets, cooling to room temperature and then entering into a heating furnace, continuous rolling to obtain tube billets, reheating, rolling to make tubes, fixed diameter, heat treatment.

[0034] The final rolling temperature of the billet continuous rolling is higher than 950°C, the reheating temperature of the billet is 1250-1270°C, and the continuous rolling pipe is produced with a large rolling elongation coefficient, the rolling elongation coefficient is controlled above 6.5, and the sizing temperature is controlled at 855°C ~875°C;

[0035] Then carry out normalizing heat treatment, the normalizing heating temperature is 910 ℃ ~ 930 ℃, and the normalizing holding time is not less than 45 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides an economical low-temperature steel pipe with good corrosion resistance and a manufacturing method of the economical low-temperature steel pipe. The steel pipe is prepared fromthe following components in percentage by weight: 0.09%-0.12% of C, 0.25%-0.33% of Si,1.10%-1.29% of Mn, 0.015%-0.03% of Ti, 0.01%-0.024% of Al, less than or equal to 0.012% of P, less than or equal to 0.008% of S, wherein the carbon equivalent CE<Pcm> is less than or equal to 0.22, and the formula of CE<Pcm>=(C+Si / 30+Mn / 20+Cu / 20+Ni / 60+Cr / 20+Mo / 15+V / 10+5B) is met. The manufacturing method comprises the steps of converter smelting, external refining (LF), square billet continuous casting, entering a heating furnace after cooling to the room temperature, pipe billet continuous rolling, reheating, continuous rolling for pipe manufacturing, sizing and heat treatment. By applying the economical low-temperature steel pipe with the good corrosion resistance and the manufacturing method of the economical low-temperature steel pipe, low-temperature impact performance and acid corrosion resistance of the steel pipe are improved, and the steel pipe can be used in a low-temperature environment ofminus 45 DEG C and a hydrogen sulfide corrosion environment.

Description

technical field [0001] The invention belongs to the field of metal materials, in particular to an economical low-temperature steel pipe with good corrosion resistance and a manufacturing method thereof. Background technique [0002] In recent years, with the progress of the petrochemical industry, energy development in alpine regions has been increasing. At the same time, the development of new equipment and new technologies has also promoted the updating and improvement of liquefaction, separation, storage and transportation equipment. Therefore, the development of low-temperature pipeline products used in low-temperature fluid delivery pipelines, low-temperature pressure vessels, and petrochemical equipment has begun to receive widespread attention. In the past, low-temperature steel pipe products often added a large amount of alloying elements, such as Ni and Mo, to reduce their ductile-brittle transition temperature, and the cost was relatively high. High, the wide appli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/14C21D1/28C21D6/00C21D8/10C21D9/08B21B37/74
CPCB21B37/74B21B2261/20C21D1/28C21D6/005C21D6/008C21D8/105C21D9/08C22C38/002C22C38/02C22C38/04C22C38/06C22C38/14
Inventor 赵波吴红解德刚袁琴王善宝
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products