A kind of niobium microalloyed high-speed wheel steel with medium carbon and medium silicon and preparation method of wheel

A technology of micro-alloying and wheel steel, which is applied in manufacturing tools, heat treatment equipment, furnaces, etc., can solve the problems of poor adaptability, low strength and hardness of high-speed wheel steel, and improve the matching of strength and toughness, enhance hardness and wear performance. improved effect

Active Publication Date: 2021-12-14
MAANSHAN IRON & STEEL CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the problems of poor adaptability, low strength and low hardness of medium and high-speed wheel steel in the prior art, the present invention provides a niobium microalloyed high-speed wheel steel with medium carbon and medium silicon and a method for preparing the wheel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of niobium microalloyed high-speed wheel steel with medium carbon and medium silicon and preparation method of wheel
  • A kind of niobium microalloyed high-speed wheel steel with medium carbon and medium silicon and preparation method of wheel
  • A kind of niobium microalloyed high-speed wheel steel with medium carbon and medium silicon and preparation method of wheel

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] A method for preparing a medium carbon medium silicon niobium microalloyed high-speed wheel using the above-mentioned medium carbon medium silicon niobium microalloyed high-speed wheel steel, comprising a heat treatment process, the heat treatment process comprising the following steps:

[0041] S1: The wheel is heated at a temperature of 860-890°C, and kept warm for 2.0-3.5 hours after heating; if the heating temperature exceeds 890°C, the austenite grains will grow significantly, which has a great impact on the toughness index of the wheel;

[0042] S2: Spray water to cool the wheels after heat preservation; specifically, place the heat-preserved wheels in step S1 horizontally on the wheel cooling platform, and at the same time, the wheels move clockwise on the wheel cooling platform at a speed of 20r / min to 30r / min Autobiography, and use the nozzle on the wheel cooling platform to spray water to cool the wheel, so that the metal inside the wheel can be cooled to below...

Embodiment 1

[0046] A niobium microalloyed high-speed wheel steel with medium carbon and silicon, comprising the following components in weight percentage: C: 0.53%, Si: 0.55%, Mn: 0.70%, Nb: 0.02%, P: 0.005%, S0 .007%, the rest is Fe and unavoidable impurity elements; the preparation method of the wheel is as follows: the molten steel containing the above components is passed through the electric furnace steelmaking process, the LF furnace refining process, the RH vacuum treatment process, the round billet continuous casting process, and the cutting process. Ingot rolling process, heat treatment process, processing process and finished product inspection process to form niobium microalloyed high-speed wheels with medium carbon and silicon. Spray water to cool the metal inside the wheel at a cooling rate of 2°C / s-5°C / s to below 550°C, and finally temper at 520°C for 5.0 hours. As a comparative example of the present invention, in this implementation, the composition of ER8 wheel steel incl...

Embodiment 2

[0050] A niobium microalloyed high-speed wheel steel with medium carbon and silicon, comprising the following components in weight percentage: C: 0.54%, Si: 0.60%, Mn: 0.65%, Nb: 0.03%, P: 0.005%, S0 .006%, the rest is Fe and unavoidable impurity elements; the preparation method of the wheel is as follows: the molten steel containing the above components is passed through the electric furnace steelmaking process, the LF furnace refining process, the RH vacuum treatment process, the round billet continuous casting process, and the cutting process. Ingot rolling process, heat treatment process, processing process, and finished product inspection process to form niobium microalloyed high-speed wheels with medium carbon and silicon. Water spray cooling, so that the inner metal of the wheel is cooled to below 550°C at a cooling rate of 2°C / s-5°C / s, and finally tempered at 540°C for 5.5 hours. In this implementation, the composition of the ER8 wheel steel is consistent with that of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a niobium microalloyed high-speed wheel steel with medium carbon and medium silicon and a wheel preparation method, belonging to the field of railway wheel preparation. Aiming at the problems of poor adaptability, low strength and low hardness of high-speed wheel steel in the prior art, the present invention provides a niobium microalloyed high-speed wheel steel with medium carbon and silicon, which includes the following components in weight percentage: C: 0.50‑0.58%, Si: 0.50‑0.80%, Mn: 0.50‑0.90%, Nb: 0.02‑0.04%, P≤0.015%, S≤0.015%, and the rest are Fe and unavoidable impurity elements. The present invention adds niobium element to the composition of the wheel steel, niobium and carbon are combined to form niobium carbide, which plays the role of refining pearlite clusters during steel rolling and heat treatment, and at the same time ensures a certain amount of ferrite precipitation to improve the strength of the wheel steel. The toughness is matched, the strength and hardness levels are increased by more than 5% compared with ER8 wheels, and the contact fatigue resistance and wear performance are also improved. The preparation method of the invention optimizes the heat treatment process, further improves the adaptability of the wheel, and makes it have higher strength and hardness.

Description

technical field [0001] The invention belongs to the technical field of railway wheel preparation, and more specifically relates to a niobium microalloyed high-speed wheel steel with medium carbon and silicon and a method for preparing the wheel. Background technique [0002] my country's high-speed railway development has achieved world-renowned achievements, and the key components of high-speed trains have also achieved independent innovation. At present, my country's high-speed wheels are mainly ER8 wheels in the European standard EN13262, which are made of medium-carbon carbon steel and have high fracture toughness (≥70MPa m 1 / 2 ) to ensure service safety. The structure of ER8 wheel is a small amount of discontinuous reticular ferrite + lamellar pearlite, in which ferrite is a soft phase with good toughness and low yield strength, and pearlite has high strength but poor toughness. The matching relationship determines the final performance of the material. The yield str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/12C21D9/34C21D1/18
CPCC22C38/02C22C38/04C22C38/12C21D9/34C21D1/18C21D2211/009C21D2211/005C21D2211/002
Inventor 赵海丁毅江波刘学华张明如
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com